Stainless Steel 317L Cold Rolled Annealed 2B
Finish state
AISI/SAE 317L · UNS S31703 · EN 1.4438, X2CrNiMo18-15-4 · JIS SUS317L · GB 022Cr19Ni13Mo3
Cold Rolled Annealed 2B = cold Rolled, Annealed, 2B finish
Smooth 2B sheet for fabricated equipment and deep-drawn parts.
Values for the Cold Rolled Annealed 2B condition
Other 317L tempers and conditions
317L is listed in 7 conditions; see the grade overview at 317L.
- Hot Rolled Annealed
- Annealed
- Solution Annealed
- Cold Rolled Annealed 2B
- Cold Drawn
- 1/4 Hard
- 1/2 Hard
Compare all 7 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Hot Rolled, Annealed and Pickled (plate, 1D/No.1 finish) | Heavy plate condition for tanks, scrubbers and pressure vessels. | 255 | 565 | 48 | 160 HB | 2.2 % IACS |
mill annealed sheet/strip/bar | Generic annealed stock condition; mechanically equivalent to solution annealed for this L-grade. | 260 | 575 | 50 | 150 HB | 2.2 % IACS |
Solution AnnealedDefault 1040–1120 °C, rapid quench | Standard supply condition for plate, sheet, pipe and bar — maximum corrosion resistance and ductility. | 265 | 580 | 50 | 155 HB | — |
Cold Rolled Annealed 2BThis page Cold Rolled, Annealed, 2B finish | Smooth 2B sheet for fabricated equipment and deep-drawn parts. | 275 | 590 | 50 | 165 HB | 2.2 % IACS |
Cold Drawn bar (annealed then drawn to size) | Choose for close-tolerance bar and higher yield strength in machined fittings and shafts. | 450 | 690 | 30 | 16 HRC | 2.2 % IACS |
Quarter hard | Light temper rolling when moderate extra strength is needed with usable bend ductility. | 515 | 860 | 15 | 24 HRC | 2.2 % IACS |
Half hard | Higher-strength strip for springs, clamps and structural strapping where forming is minimal. | 760 | 1,035 | 10 | 32 HRC | 2.2 % IACS |
What is 317L Cold Rolled Annealed 2B?
317L Cold Rolled Annealed 2B is 317L supplied in the Cold Rolled Annealed 2B condition — smooth 2B sheet for fabricated equipment and deep-drawn parts. 317L Cold Rolled Annealed 2B has a yield strength of 275 MPa (39.9 ksi) and a tensile strength of 590 MPa (85.6 ksi) — weaker than 77% of stainless steel grades. Elongation at break is 50% and the elastic modulus is 200 GPa (29 Msi). 317L Cold Rolled Annealed 2B has a density of 7.98 g/cm³ (0.288 lb/in³), heavier than 85% of stainless steel grades. It melts at 1,375°C (2,507 °F). Solution Annealed is the default condition FabDigit quotes; Cold Rolled Annealed 2B is available on request or by drawing note.
Advantages
- Readily welded — 90/100, better than 95% of stainless steel grades
- Forms and bends easily — 85/100, better than 95% of stainless steel grades
- Polishes to a fine finish — 84/100, better than 95% of stainless steel grades
- Ductile — tolerates forming and impact — 50%, better than 90% of stainless steel grades
- Good corrosion resistance — 81/100, better than 89% of stainless steel grades
Limitations
- Low strength — 275 MPa (39.9 ksi), worse than 77% of stainless steel grades
317L Cold Rolled Annealed 2B properties
Typical room-temperature values for 317L Cold Rolled Annealed 2B; 23 are specific to this condition. Other listed values are 317L reference data and may not represent this condition. Bars are the position among stainless steel grades.
Physical3
317L Cold Rolled Annealed 2B has a density of 7.98 g/cm³ (0.288 lb/in³), heavier than 85% of stainless steel grades. It melts at 1,375°C (2,507 °F).
Mechanical15
317L Cold Rolled Annealed 2B has a yield strength of 275 MPa (39.9 ksi) and a tensile strength of 590 MPa (85.6 ksi) — weaker than 77% of stainless steel grades. Elongation at break is 50% and the elastic modulus is 200 GPa (29 Msi).
Thermal6
317L Cold Rolled Annealed 2B is rated for continuous service to 870°C (1,598 °F). It conducts heat at 14.2 W/m·K (8.2 BTU/hr·ft·°F), worse than 76% of stainless steel grades. Thermal expansion is 16 µm/m·K (8.89 µin/in·°F).
Electrical3
317L Cold Rolled Annealed 2B conducts electricity at 2.2 % IACS, worse than 61% of stainless steel grades.
Chemical & Environmental3
Corrosion resistance is very good (81/100), better than 89% of stainless steel grades.
Sustainability4
Producing a kilogram of 317L Cold Rolled Annealed 2B takes about 62 MJ of energy and emits 4.6 kg of CO₂ — more than 75% of stainless steel grades. Typical recycled content is 60%.
Manufacturability8
317L Cold Rolled Annealed 2B's machinability is fair (37/100, better than 57% of stainless steel grades); weldability excellent (90/100); formability excellent (85/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with 317L Cold Rolled Annealed 2B
Is 317L easy to machine?
Gummy and strongly work-hardening — use rigid setups, sharp positive-rake carbide, heavy positive feed, no dwell, and flood coolant; roughly 45 % of AISI 1212 speeds.
Can 317L be welded?
Excellent by GTAW/GMAW/SMAW with 317L or overmatched 317L/Mo-rich filler; keep interpass below ~150 °C, no preheat and no PWHT required, back-purge for full corrosion resistance.
Can 317L be formed, bent or molded?
Deep drawable and readily roll-formed, but springback and press loads are higher than carbon steel; anneal between severe cold-forming steps.
What surface finishes work on 317L?
Pickle and passivate (ASTM A967) or electropolish after fabrication to restore the passive film; not anodizable, takes mechanical No.4 or mirror No.8 finishes well.
317L chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Clow carbon for weld sensitization resistance | ≤ 0.03 | 0.02 |
| Mn | ≤ 2 | 1.5 |
| Si | ≤ 1 | 0.5 |
| P | ≤ 0.05 | 0.03 |
| S | ≤ 0.03 | 0.01 |
| Cr | 18 – 20 | 18.5 |
| Ni | 11 – 15 | 13 |
| Mo | 3 – 4 | 3.4 |
| N | ≤ 0.1 | 0.05 |
| Fe | balance | — |
317L Cold Rolled Annealed 2B — frequently asked
What is 317L Cold Rolled Annealed 2B used for?
317L Cold Rolled Annealed 2B is typically used for welded bleaching tanks and washers, FGD scrubber vessels and spray headers, chemical and pharmaceutical process piping, heat exchanger tube bundles, seawater and brine handling equipment and acid storage tanks. In short: pitting-resistant low-carbon stainless.
What is the yield strength of 317L Cold Rolled Annealed 2B?
317L Cold Rolled Annealed 2B has a typical yield strength of 275 MPa (39.9 ksi) and a tensile strength of 590 MPa (85.6 ksi) — weaker than 77% of stainless steel grades. Strength varies by condition: see the 7 listed tempers.
Is 317L Cold Rolled Annealed 2B easy to machine?
Not especially — machinability is rated fair (37/100, better than 57% of stainless steel grades). Gummy and strongly work-hardening — use rigid setups, sharp positive-rake carbide, heavy positive feed, no dwell, and flood coolant; roughly 45 % of AISI 1212 speeds.
Can 317L Cold Rolled Annealed 2B be welded?
Yes — weldability is rated excellent (90/100). Excellent by GTAW/GMAW/SMAW with 317L or overmatched 317L/Mo-rich filler; keep interpass below ~150 °C, no preheat and no PWHT required, back-purge for full corrosion resistance.
What surface finishes work on 317L Cold Rolled Annealed 2B?
Pickle and passivate (ASTM A967) or electropolish after fabrication to restore the passive film; not anodizable, takes mechanical No.4 or mirror No.8 finishes well.
Can 317L Cold Rolled Annealed 2B be formed, bent or molded?
Deep drawable and readily roll-formed, but springback and press loads are higher than carbon steel; anneal between severe cold-forming steps.
What is the maximum service temperature of 317L Cold Rolled Annealed 2B?
317L Cold Rolled Annealed 2B is rated for continuous use to about 870°C (1,598 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Can FabDigit make parts in 317L Cold Rolled Annealed 2B?
Yes — 317L Cold Rolled Annealed 2B is available for CNC machining and sheet metal; every part is priced by an engineer rather than instantly. Upload a STEP file to get a price and a DFM check.
Sources
- ASTM A240/A240M — Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip — ASTM International (2023)
- ASTM A312/A312M — Seamless, Welded and Heavily Cold Worked Austenitic Stainless Steel Pipes — ASTM International (2022)
- ASTM A666 — Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate and Flat Bar — ASTM International (2015)
- EN 10088-2 (1.4438 / X2CrNiMo18-15-4) — CEN (2014)
- JIS G 4304 / G 4305 (SUS317L) — JSA (2021)
- GB/T 4237 / GB/T 3280 (022Cr19Ni13Mo3) — SAC (2015)
- ASM Handbook Vol.1 — Properties and Selection: Irons, Steels, and High-Performance Alloys — ASM International (1990)
- Outokumpu / Sandvik austenitic stainless steel datasheets (4438 / 317L) — Outokumpu, Alleima (2023)
- SMM / Mysteel — SMM / Mysteel (2025)