Stainless Steel 310HCb-CD (Cold drawn)
Supply condition
UNS S31041
Choose for tighter dimensional tolerance and higher room-temperature strength in bar/tube; strength gain is lost above ~600 °C service.
Values for the CD condition
Other 310HCb tempers and conditions
310HCb is listed in 4 conditions; see the grade overview at 310HCb.
Compare all 4 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
AnnealedDefault solution annealed (~1050–1150 °C) and rapidly cooled | Standard supply condition for plate, pipe and tube; maximum ductility and the condition for which ASME creep/allowable stresses apply. | 260 | 590 | 45 | 170 HB | — |
As-welded deposit | Condition of fabricated furnace assemblies welded with matching Nb-bearing 310 filler; Nb keeps HAZ sensitization-resistant so PWHT is usually unnecessary. | 300 | 570 | 32 | 185 HB | 2.1 % IACS |
CDThis page Cold drawn | Choose for tighter dimensional tolerance and higher room-temperature strength in bar/tube; strength gain is lost above ~600 °C service. | 450 | 690 | 30 | 17 HRC | 2.2 % IACS |
1/4 Hard | Occasional strip/wire condition where extra room-temperature strength and springback are needed; not used for creep-governed hot service. | 515 | 760 | 20 | 22 HRC | 2.2 % IACS |
What is 310HCb-CD?
310HCb-CD is 310HCb supplied in the CD condition — choose for tighter dimensional tolerance and higher room-temperature strength in bar/tube; strength gain is lost above ~600 °C service. 310HCb-CD has a yield strength of 450 MPa (65.3 ksi) and a tensile strength of 690 MPa (100 ksi) — stronger than 70% of stainless steel grades. Elongation at break is 30% and the elastic modulus is 200 GPa (29 Msi). 310HCb-CD has a density of 7.98 g/cm³ (0.288 lb/in³), heavier than 85% of stainless steel grades. It melts at 1,400°C (2,552 °F). Annealed is the default condition FabDigit quotes; CD is available on request or by drawing note.
Advantages
- High service temperature — 1,100°C (2,012 °F), better than 96% of stainless steel grades
Limitations
- High embodied carbon — 5.8 kg CO₂/kg, worse than 86% of stainless steel grades
310HCb-CD properties
Typical room-temperature values for 310HCb-CD; 23 are specific to this condition. Other listed values are 310HCb reference data and may not represent this condition. Bars are the position among stainless steel grades.
Physical3
310HCb-CD has a density of 7.98 g/cm³ (0.288 lb/in³), heavier than 85% of stainless steel grades. It melts at 1,400°C (2,552 °F).
Mechanical16
310HCb-CD has a yield strength of 450 MPa (65.3 ksi) and a tensile strength of 690 MPa (100 ksi) — stronger than 70% of stainless steel grades. Elongation at break is 30% and the elastic modulus is 200 GPa (29 Msi).
Thermal6
310HCb-CD is rated for continuous service to 1,100°C (2,012 °F). It conducts heat at 14.2 W/m·K (8.2 BTU/hr·ft·°F), worse than 76% of stainless steel grades. Thermal expansion is 15.9 µm/m·K (8.83 µin/in·°F).
Electrical3
310HCb-CD conducts electricity at 2.2 % IACS, worse than 61% of stainless steel grades.
Chemical & Environmental3
Corrosion resistance is very good (70/100), better than 68% of stainless steel grades.
Sustainability4
Producing a kilogram of 310HCb-CD takes about 68 MJ of energy and emits 5.8 kg of CO₂ — more than 80% of stainless steel grades. Typical recycled content is 60%.
Manufacturability7
310HCb-CD's machinability is fair (35/100, better than 51% of stainless steel grades); weldability good (65/100); formability fair (45/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with 310HCb-CD
Is 310HCb easy to machine?
Slow speeds, heavy positive-rake carbide, rigid setups and flood coolant — the alloy work-hardens fast and produces stringy chips; avoid dwelling to prevent glazing.
Can 310HCb be welded?
GTAW/SMAW/FCAW with matching 310 or Nb-bearing 310 filler, low heat input, interpass ≤150 °C; keep ferrite-free weld pools clean to avoid hot cracking and no PWHT normally needed thanks to Nb stabilization.
Can 310HCb be formed, bent or molded?
Cold forms readily but with high force and springback (work-hardening rate ~2× carbon steel); hot work at 1150–1200 °C and finish above 950 °C, then solution anneal 1050–1150 °C and cool fast.
What surface finishes work on 310HCb?
Pickle/passivate or bead-blast after hot work to restore the Cr₂O₃ film; can be electropolished or mechanically polished, no anodizing — protect from chloride-bearing residues before high-temperature service.
310HCb chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Ccontrolled high carbon for creep strength | 0.04 – 0.1 | 0.07 |
| Cr | 24 – 26 | 25 |
| Ni | 19 – 22 | 20.5 |
| Nbstabilizer; forms NbC and prevents sensitization | 0.2 – 1 | 0.5 |
| Mn | ≤ 2 | 1.5 |
| Siaids oxidation resistance | ≤ 1.5 | 0.8 |
| N | ≤ 0.03 | 0.02 |
| P | ≤ 0.05 | 0.03 |
| S | ≤ 0.03 | 0.01 |
| Fe | balance | — |
310HCb-CD — frequently asked
What is 310HCb-CD used for?
310HCb-CD is typically used for high-temperature pressure vessels, petrochemical furnace piping, welded reformer internals, superheater and reheater tubing, furnace hangers and supports and hot-gas ducting and expansion joints. In short: stabilized high-carbon 310; creep strength with stabilization; welded high-temperature pressure parts.
What is the yield strength of 310HCb-CD?
310HCb-CD has a typical yield strength of 450 MPa (65.3 ksi) and a tensile strength of 690 MPa (100 ksi) — stronger than 70% of stainless steel grades. Strength varies by condition: see the 4 listed tempers.
Is 310HCb-CD easy to machine?
Not especially — machinability is rated fair (35/100, better than 51% of stainless steel grades). Slow speeds, heavy positive-rake carbide, rigid setups and flood coolant — the alloy work-hardens fast and produces stringy chips; avoid dwelling to prevent glazing.
Can 310HCb-CD be welded?
Yes — weldability is rated good (65/100). GTAW/SMAW/FCAW with matching 310 or Nb-bearing 310 filler, low heat input, interpass ≤150 °C; keep ferrite-free weld pools clean to avoid hot cracking and no PWHT normally needed thanks to Nb stabilization.
What surface finishes work on 310HCb-CD?
Pickle/passivate or bead-blast after hot work to restore the Cr₂O₃ film; can be electropolished or mechanically polished, no anodizing — protect from chloride-bearing residues before high-temperature service.
Can 310HCb-CD be formed, bent or molded?
Cold forms readily but with high force and springback (work-hardening rate ~2× carbon steel); hot work at 1150–1200 °C and finish above 950 °C, then solution anneal 1050–1150 °C and cool fast.
What is the maximum service temperature of 310HCb-CD?
310HCb-CD is rated for continuous use to about 1,100°C (2,012 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between 310HCb Annealed and 310HCb-CD?
Annealed is the default condition — standard supply condition for plate, pipe and tube; maximum ductility and the condition for which ASME creep/allowable stresses apply. CD: choose for tighter dimensional tolerance and higher room-temperature strength in bar/tube; strength gain is lost above ~600 °C service. Yield strength is 260 MPa in Annealed versus 450 MPa in CD.
Sources
- ASTM A240/A240M — Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip (UNS S31041) — ASTM International (2023)
- ASTM A213/A213M — Seamless Ferritic and Austenitic Alloy-Steel Boiler, Superheater and Heat-Exchanger Tubes — ASTM International (2022)
- ASTM A312/A312M — Seamless, Welded and Heavily Cold Worked Austenitic Stainless Steel Pipes — ASTM International (2022)
- ASME BPVC Section II Part D — Allowable stresses for S31041 — ASME (2023)
- ASM Handbook Vol.1 — Properties and Selection: Irons, Steels, and High-Performance Alloys — ASM International (1990)
- 310S/310H/310HCb heat-resisting austenitic stainless datasheets — Outokumpu / Sandmeyer Steel / Sandvik (2022)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.