Stainless Steel Nitronic 32 Cold Drawn
Supply condition
UNS S24100
Choose for straight, close-tolerance bar with a strength bump over annealed; typical for shafts and fasteners.
Values for the Cold Drawn condition
Other Nitronic 32 tempers and conditions
Nitronic 32 is listed in 6 conditions; see the grade overview at Nitronic 32.
Compare all 6 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
AnnealedDefault solution annealed ~1065 °C, water quenched | Standard stocked condition for sheet, plate and bar; best ductility, corrosion resistance and formability. | 415 | 830 | 48 | 220 HB | — |
Quarter hard | Light cold-rolled temper for parts needing extra strength while still allowing moderate bending. | 690 | 965 | 25 | 30 HRC | 2.3 % IACS |
Cold DrawnThis page annealed then cold drawn bar/wire (light draft) | Choose for straight, close-tolerance bar with a strength bump over annealed; typical for shafts and fasteners. | 760 | 1,000 | 25 | 31 HRC | 2.3 % IACS |
Half hard | Mid cold-rolled temper for stamped structural parts, clamps and springy brackets. | 860 | 1,105 | 18 | 34 HRC | 2.3 % IACS |
Three-quarter hard | High-strength strip temper for flat springs, shims and wear strips with only gentle forming. | 1,035 | 1,240 | 12 | 38 HRC | 2.3 % IACS |
heavily cold rolled strip/sheet | Maximum as-rolled strength and wear resistance; essentially flat-form only, very limited bending. | 1,210 | 1,380 | 8 | 42 HRC | 2.3 % IACS |
What is Nitronic 32 Cold Drawn?
Nitronic 32 Cold Drawn is Nitronic 32 supplied in the Cold Drawn condition — choose for straight, close-tolerance bar with a strength bump over annealed; typical for shafts and fasteners. Nitronic 32 Cold Drawn has a yield strength of 760 MPa (110 ksi) and a tensile strength of 1,000 MPa (145 ksi) — stronger than 94% of stainless steel grades. Elongation at break is 25% and the elastic modulus is 197 GPa (28.6 Msi). Nitronic 32 Cold Drawn has a density of 7.8 g/cm³ (0.282 lb/in³), heavier than 50% of stainless steel grades. It melts at 1,400°C (2,552 °F). Annealed is the default condition FabDigit quotes; Cold Drawn is available on request or by drawing note.
Advantages
- High strength — 760 MPa (110 ksi), better than 94% of stainless steel grades
Nitronic 32 Cold Drawn properties
Typical room-temperature values for Nitronic 32 Cold Drawn; 23 are specific to this condition. Other listed values are Nitronic 32 reference data and may not represent this condition. Bars are the position among stainless steel grades.
Physical3
Nitronic 32 Cold Drawn has a density of 7.8 g/cm³ (0.282 lb/in³), heavier than 50% of stainless steel grades. It melts at 1,400°C (2,552 °F).
Mechanical13
Nitronic 32 Cold Drawn has a yield strength of 760 MPa (110 ksi) and a tensile strength of 1,000 MPa (145 ksi) — stronger than 94% of stainless steel grades. Elongation at break is 25% and the elastic modulus is 197 GPa (28.6 Msi).
Thermal6
Nitronic 32 Cold Drawn is rated for continuous service to 425°C (797 °F). It conducts heat at 14.5 W/m·K (8.38 BTU/hr·ft·°F), worse than 72% of stainless steel grades. Thermal expansion is 15.5 µm/m·K (8.61 µin/in·°F).
Electrical3
Nitronic 32 Cold Drawn conducts electricity at 2.3 % IACS, better than 55% of stainless steel grades.
Chemical & Environmental3
Corrosion resistance is fair (54/100), worse than 75% of stainless steel grades.
Sustainability4
Producing a kilogram of Nitronic 32 Cold Drawn takes about 45 MJ of energy and emits 4.2 kg of CO₂ — less than 91% of stainless steel grades. Typical recycled content is 70%.
Manufacturability7
Nitronic 32 Cold Drawn's machinability is fair (35/100, better than 51% of stainless steel grades); weldability very good (70/100); formability fair (45/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with Nitronic 32 Cold Drawn
Is Nitronic 32 easy to machine?
Treat like a high-work-hardening austenitic: rigid setups, sharp positive-rake carbide, heavy positive feeds, slow speeds (~60–70 % of 304) and flood coolant to avoid glazing.
Can Nitronic 32 be welded?
Readily welded by GTAW/GMAW/SMAW without preheat or post-weld heat treatment; use over-alloyed austenitic filler such as 209, 240 or 308L/309L and keep interpass temperature low.
Can Nitronic 32 be formed, bent or molded?
Cold forms well but needs ~2× the press load of 304 and generous bend radii with springback allowance; hot work 1150–1230 °C and finish above ~950 °C, then solution anneal ~1040–1090 °C and quench.
What surface finishes work on Nitronic 32?
Passivate per ASTM A967 or electropolish for best corrosion performance; polishes to a bright finish, and hard chrome or nitriding can be added for extreme wear duty.
Nitronic 32 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| C | ≤ 0.15 | 0.06 |
| Mnprimary austenite stabiliser replacing Ni | 11 – 14 | 12 |
| Si | ≤ 1 | 0.5 |
| P | ≤ 0.06 | — |
| S | ≤ 0.03 | — |
| Cr | 16.5 – 19 | 17.75 |
| Ni | 0.5 – 2.5 | 1.6 |
| Nsolid-solution strengthener | 0.2 – 0.45 | 0.3 |
| Fe | balance | — |
Nitronic 32 Cold Drawn — frequently asked
What is Nitronic 32 Cold Drawn used for?
Nitronic 32 Cold Drawn is typically used for fasteners, structural components, cryogenic equipment and high-strength tie rods. In short: low-nickel 300-series substitute; double 304 yield strength; corrosion below 304.
What is the yield strength of Nitronic 32 Cold Drawn?
Nitronic 32 Cold Drawn has a typical yield strength of 760 MPa (110 ksi) and a tensile strength of 1,000 MPa (145 ksi) — stronger than 94% of stainless steel grades. Strength varies by condition: see the 6 listed tempers.
Is Nitronic 32 Cold Drawn easy to machine?
Not especially — machinability is rated fair (35/100, better than 51% of stainless steel grades). Treat like a high-work-hardening austenitic: rigid setups, sharp positive-rake carbide, heavy positive feeds, slow speeds (~60–70 % of 304) and flood coolant to avoid glazing.
Can Nitronic 32 Cold Drawn be welded?
Yes — weldability is rated very good (70/100). Readily welded by GTAW/GMAW/SMAW without preheat or post-weld heat treatment; use over-alloyed austenitic filler such as 209, 240 or 308L/309L and keep interpass temperature low.
What surface finishes work on Nitronic 32 Cold Drawn?
Passivate per ASTM A967 or electropolish for best corrosion performance; polishes to a bright finish, and hard chrome or nitriding can be added for extreme wear duty.
Can Nitronic 32 Cold Drawn be formed, bent or molded?
Cold forms well but needs ~2× the press load of 304 and generous bend radii with springback allowance; hot work 1150–1230 °C and finish above ~950 °C, then solution anneal ~1040–1090 °C and quench.
What is the maximum service temperature of Nitronic 32 Cold Drawn?
Nitronic 32 Cold Drawn is rated for continuous use to about 425°C (797 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- ASTM A240/A240M — Chromium and Chromium-Nickel Stainless Steel Plate, Sheet and Strip (UNS S24100) — ASTM International (2023)
- ASTM A276/A276M — Stainless Steel Bars and Shapes — ASTM International (2023)
- Nitronic 32 (S24100) high-manganese austenitic stainless alloy data — Armco/AK Steel — Nitronic alloy series (2015)
- ASM Handbook Vol. 1: Properties and Selection — Irons, Steels, and High-Performance Alloys — ASM International (1990)
- UNS S24100 alloy property summary — SAE/ASTM Unified Numbering System (2020)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.