Stainless Steel 317LN As Welded
Finish state
AISI/SAE 317LN · UNS S31753
Represents fabricated weldments; low carbon and N keep sensitisation risk low but weld metal ferrite/δ affects toughness.
Values for the As Welded condition
Other 317LN tempers and conditions
317LN is listed in 7 conditions; see the grade overview at 317LN.
Compare all 7 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
AnnealedDefault solution annealed and quenched (1040–1120 °C, rapid cool) | Standard stocked condition for plate, sheet, pipe and bar; maximum corrosion resistance and ductility. | 320 | 620 | 48 | 170 HB | — |
As WeldedThis page autogenous/filler weld metal and HAZ, no post-weld anneal | Represents fabricated weldments; low carbon and N keep sensitisation risk low but weld metal ferrite/δ affects toughness. | 330 | 600 | 35 | 185 HB | 2.2 % IACS |
annealed then cold drawn bar/wire (light draft) | Choose for straight, close-tolerance bar with a strength bump over annealed; slightly reduced ductility. | 500 | 720 | 30 | 18 HRC | 2.2 % IACS |
Quarter hard | Light cold-rolled strip/sheet where extra yield strength is needed but some bending is still required. | 620 | 900 | 20 | 25 HRC | 2.2 % IACS |
Half hard | Structural strip/sheet needing high yield with only mild forming; springback and magnetic permeability rise. | 790 | 1,035 | 12 | 32 HRC | 2.2 % IACS |
Three-quarter hard | Flat parts and clips requiring very high yield with essentially no forming. | 930 | 1,170 | 8 | 36 HRC | 2.2 % IACS |
heavily cold rolled strip | Maximum strength thin strip for shims and flat springs; not formable, most magnetic condition. | 1,000 | 1,280 | 6 | 40 HRC | 2.2 % IACS |
What is 317LN As Welded?
317LN As Welded is 317LN supplied in the As Welded condition — represents fabricated weldments; low carbon and N keep sensitisation risk low but weld metal ferrite/δ affects toughness. 317LN As Welded has a yield strength of 330 MPa (47.9 ksi) and a tensile strength of 600 MPa (87 ksi) — weaker than 57% of stainless steel grades. Elongation at break is 35% and the elastic modulus is 196 GPa (28.4 Msi). 317LN As Welded has a density of 7.98 g/cm³ (0.288 lb/in³), heavier than 85% of stainless steel grades. It melts at 1,375°C (2,507 °F). Annealed is the default condition FabDigit quotes; As Welded is available on request or by drawing note.
Advantages
- Polishes to a fine finish — 80/100, better than 89% of stainless steel grades
- Readily welded — 85/100, better than 87% of stainless steel grades
317LN As Welded properties
Typical room-temperature values for 317LN As Welded; 23 are specific to this condition. Other listed values are 317LN reference data and may not represent this condition. Bars are the position among stainless steel grades.
Physical3
317LN As Welded has a density of 7.98 g/cm³ (0.288 lb/in³), heavier than 85% of stainless steel grades. It melts at 1,375°C (2,507 °F).
Mechanical16
317LN As Welded has a yield strength of 330 MPa (47.9 ksi) and a tensile strength of 600 MPa (87 ksi) — weaker than 57% of stainless steel grades. Elongation at break is 35% and the elastic modulus is 196 GPa (28.4 Msi).
Thermal6
317LN As Welded is rated for continuous service to 425°C (797 °F). It conducts heat at 14.5 W/m·K (8.38 BTU/hr·ft·°F), worse than 72% of stainless steel grades. Thermal expansion is 16 µm/m·K (8.89 µin/in·°F).
Electrical3
317LN As Welded conducts electricity at 2.2 % IACS, worse than 61% of stainless steel grades.
Chemical & Environmental3
Corrosion resistance is very good (72/100), better than 73% of stainless steel grades.
Sustainability4
Producing a kilogram of 317LN As Welded takes about 60 MJ of energy and emits 4.5 kg of CO₂ — more than 70% of stainless steel grades. Typical recycled content is 65%.
Manufacturability8
317LN As Welded's machinability is poor (30/100, worse than 70% of stainless steel grades); weldability excellent (85/100); formability good (58/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with 317LN As Welded
Is 317LN easy to machine?
Gummy and strongly work-hardening — use rigid setups, positive-rake carbide, heavy positive feed, 20–35 % lower speeds than 304 and flood coolant.
Can 317LN be welded?
Excellent with GTAW/GMAW/SMAW using 317L/317LMn or overalloyed 625-type filler; keep heat input low, interpass <150 °C, no post-weld anneal needed for corrosion service.
Can 317LN be formed, bent or molded?
Cold forms well but nitrogen raises yield and springback versus 317L — allow higher press tonnage and generous bend radii; hot work 1150–1200 °C then solution anneal and water quench.
What surface finishes work on 317LN?
Pickle and passivate (ASTM A967) or electropolish after fabrication to restore the passive film; not anodizable, polishes to No.4/mirror finishes.
317LN chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Clow carbon for intergranular corrosion resistance | ≤ 0.03 | 0.02 |
| Mn | ≤ 2 | 1.5 |
| Si | ≤ 0.75 | 0.5 |
| P | ≤ 0.05 | 0.03 |
| S | ≤ 0.03 | 0 |
| Cr | 18 – 20 | 18.7 |
| Ni | 11 – 15 | 13 |
| Mo | 3 – 4 | 3.3 |
| Nsolid-solution strengthening + pitting resistance | 0.1 – 0.22 | 0.15 |
| Fe | balance | — |
317LN As Welded — frequently asked
What is 317LN As Welded used for?
317LN As Welded is typically used for chemical processing, pressure vessels and pulp and paper equipment. In short: higher-strength 317L; no post-weld anneal needed; nitrogen-boosted pitting resistance.
What is the yield strength of 317LN As Welded?
317LN As Welded has a typical yield strength of 330 MPa (47.9 ksi) and a tensile strength of 600 MPa (87 ksi) — weaker than 57% of stainless steel grades. Strength varies by condition: see the 7 listed tempers.
Is 317LN As Welded easy to machine?
Not especially — machinability is rated poor (30/100, worse than 70% of stainless steel grades). Gummy and strongly work-hardening — use rigid setups, positive-rake carbide, heavy positive feed, 20–35 % lower speeds than 304 and flood coolant.
Can 317LN As Welded be welded?
Yes — weldability is rated excellent (85/100). Excellent with GTAW/GMAW/SMAW using 317L/317LMn or overalloyed 625-type filler; keep heat input low, interpass <150 °C, no post-weld anneal needed for corrosion service.
What surface finishes work on 317LN As Welded?
Pickle and passivate (ASTM A967) or electropolish after fabrication to restore the passive film; not anodizable, polishes to No.4/mirror finishes.
Can 317LN As Welded be formed, bent or molded?
Cold forms well but nitrogen raises yield and springback versus 317L — allow higher press tonnage and generous bend radii; hot work 1150–1200 °C then solution anneal and water quench.
What is the maximum service temperature of 317LN As Welded?
317LN As Welded is rated for continuous use to about 425°C (797 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- ASTM A240/A240M — Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip — ASTM International (2023)
- ASTM A312/A312M — Seamless and Welded Austenitic Stainless Steel Pipes (TP317LN) — ASTM International (2022)
- ASTM A666 — Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate and Flat Bar — ASTM International (2015)
- GB/T 24511 / GB/T 4237 — SAC (2017)
- ASM Handbook Vol. 1 — Properties and Selection: Irons, Steels and High-Performance Alloys — ASM International (1990)
- Austenitic stainless 317L/317LN data sheets — Outokumpu / Sandvik (2021)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.