ASTM A369 FP22
A369 FP22 is a 2.25Cr-1Mo forged and bored alloy steel pipe to ASTM A369, the forged equivalent of the widely used A335 P22 seamless pipe and of 10CrMo9-10 / 1.7380.
Reference datasheet — A369 FP22 is not in the instant-quote catalog. Upload your part and an engineer will quote it in this grade or suggest the closest stocked equivalent.
Values for the Annealed condition
A369 FP22 tempers and conditions
A369 FP22 is supplied in 4 conditions, soft to hard. Annealed is the default FabDigit quotes; the values on this page are for it.
Compare all 4 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Isothermal annealed | Pick when very uniform low hardness and dimensional stability across heavy wall sections are needed for machining or field bending. | 300 | 490 | 30 | 140 HB | 7.6 % IACS |
AnnealedDefault full anneal per ASTM A369 (heat above upper critical, slow cool) | Standard stocked condition for FP22 forged-and-bored pipe: softest, most machinable, easiest to bend and weld, meets 415/205 MPa minimums. | 305 | 500 | 28 | 145 HB | — |
Normalized and tempered | Choose for higher room-temperature strength and toughness in thick-wall header/piping forgings; bainitic structure with better creep-rupture consistency. | 400 | 585 | 24 | 175 HB | — |
Quenched and tempered | Supplemental condition for heavy-wall hydroprocessing forgings where higher yield strength and low-temperature toughness are specified; requires temper well above service temperature. | 500 | 660 | 22 | 19 HRC | — |
What is A369 FP22?
A369 FP22 is a 2.25Cr-1Mo forged and bored alloy steel pipe to ASTM A369, the forged equivalent of the widely used A335 P22 seamless pipe and of 10CrMo9-10 / 1.7380. It is the default choice for boiler and refinery service to 580 °C, supplied annealed, isothermally annealed, N+T or Q&T with 305 MPa yield, 500 MPa tensile, 28% elongation and 145 HB. Machinability (55) and formability (55) are moderate and PWHT is mandatory; use FP9 or FP5 when sulfidation or higher metal temperatures govern. A369 FP22 has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,450°C (2,642 °F). A369 FP22 has a yield strength of 305 MPa (44.2 ksi) and a tensile strength of 500 MPa (72.5 ksi) — weaker than 84% of steel grades. Elongation at break is 28% and the elastic modulus is 207 GPa (30 Msi).
What is A369 FP22 used for?
- Superheater and reheater headers
- Refinery high-temperature piping
- Hydroprocessing and hydrogen-service lines
- Main steam and hot reheat piping
- Forged fittings and valve bodies for Cr-Mo systems
- Fired heater transfer lines
Advantages
- Tough — resists crack growth — 170 MPa·√m (154.7 ksi·√in), better than 98% of steel grades
- High service temperature — 580°C (1,076 °F), better than 97% of steel grades
- Ductile — tolerates forming and impact — 28%, better than 89% of steel grades
Limitations
- Low strength — 305 MPa (44.2 ksi), worse than 84% of steel grades
A369 FP22 properties
Typical room-temperature values for A369 FP22-Annealed; bars are the position among steel grades.
Physical3
A369 FP22 has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,450°C (2,642 °F).
Mechanical16
A369 FP22 has a yield strength of 305 MPa (44.2 ksi) and a tensile strength of 500 MPa (72.5 ksi) — weaker than 84% of steel grades. Elongation at break is 28% and the elastic modulus is 207 GPa (30 Msi).
Thermal6
A369 FP22 is rated for continuous service to 580°C (1,076 °F). It conducts heat at 36 W/m·K (20.8 BTU/hr·ft·°F), worse than 73% of steel grades. Thermal expansion is 12.1 µm/m·K (6.72 µin/in·°F).
Electrical3
A369 FP22 conducts electricity at 7.5 % IACS, worse than 67% of steel grades.
Chemical & Environmental3
Corrosion resistance is poor (20/100), better than 87% of steel grades.
Sustainability4
Producing a kilogram of A369 FP22 takes about 29 MJ of energy and emits 2.3 kg of CO₂ — less than 53% of steel grades. Typical recycled content is 25%.
Manufacturability7
A369 FP22's machinability is good (55/100, better than 62% of steel grades); weldability good (55/100); formability good (55/100).
Common Calculations5
Values are nominal handbook figures for design screening. Certified mill or lot data ships with every FabDigit order on request.
Strength versus weight in the steel family
Yield strength against density for every steel grade FabDigit runs. A369 FP22 is highlighted; hover a dot for its name, or open the interactive family chart.
Working with A369 FP22
Is A369 FP22 easy to machine?
Machines like annealed 4140 at ~60 % of 1212 — carbide tooling, rigid setups and generous coolant; keep speeds down in the N+T/Q&T conditions.
Can A369 FP22 be welded?
Weldable with 2.25Cr-1Mo filler (E9018-B3 / ER90S-B3): preheat 200–250 °C, low-hydrogen practice, interpass control, and mandatory PWHT 690–760 °C to avoid hard HAZ and temper embrittlement.
Can A369 FP22 be formed, bent or molded?
Hot bend/form at 900–1050 °C followed by re-heat treatment; cold bending is limited and should be followed by stress relief.
A369 FP22 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| C | 0.05 – 0.15 | 0.11 |
| Mn | 0.3 – 0.6 | 0.45 |
| Si | ≤ 0.5 | 0.3 |
| P | ≤ 0.03 | 0.01 |
| S | ≤ 0.03 | 0.01 |
| Cr | 1.9 – 2.6 | 2.25 |
| Mo | 0.87 – 1.13 | 1 |
| Fe | balance |
What surface finishes work on A369 FP22?
Not anodizable — use shot blast plus high-temperature aluminium or silicone paint, phosphate, or aluminizing/cladding for steam and sulfidation service.
Surface treatments FabDigit runs on steel parts — pick them in the quote configurator or call them out on the drawing. Each links to its datasheet in the surface-finish library (thickness, specs, call-out, material verdicts).
Organic Coating
Black / Phosphate
Thermal Spray
Equivalent designations
Standards and trade names that resolve to Steel A369 FP22 in FabDigit's catalog. Equivalence is nominal — check the exact specification when certification matters.
- ASTM
- A335 P22
- Similar grades
- 10CrMo9-101.7380
How much does A369 FP22 cost?
A369 FP22 is a premium-cost steel ($$$), cheaper than about 51% of the materials FabDigit quotes. Part price depends far more on geometry, tolerance and quantity than on the raw stock — upload a CAD file for a live quote.
A369 FP22 — frequently asked
What is A369 FP22 used for?
A369 FP22 is typically used for superheater and reheater headers, refinery high-temperature piping, hydroprocessing and hydrogen-service lines, main steam and hot reheat piping, forged fittings and valve bodies for Cr-Mo systems and fired heater transfer lines. In short: most available Cr-Mo pipe; forged equivalent of P22; standard boiler header grade.
What is the yield strength of A369 FP22?
A369 FP22 has a typical yield strength of 305 MPa (44.2 ksi) and a tensile strength of 500 MPa (72.5 ksi) — weaker than 84% of steel grades. Strength varies by condition: see the 4 listed tempers.
Is A369 FP22 easy to machine?
Reasonably — machinability is rated good (55/100, better than 62% of steel grades). Machines like annealed 4140 at ~60 % of 1212 — carbide tooling, rigid setups and generous coolant; keep speeds down in the N+T/Q&T conditions.
Can A369 FP22 be welded?
Yes — weldability is rated good (55/100). Weldable with 2.25Cr-1Mo filler (E9018-B3 / ER90S-B3): preheat 200–250 °C, low-hydrogen practice, interpass control, and mandatory PWHT 690–760 °C to avoid hard HAZ and temper embrittlement.
What surface finishes work on A369 FP22?
Not anodizable — use shot blast plus high-temperature aluminium or silicone paint, phosphate, or aluminizing/cladding for steam and sulfidation service.
Can A369 FP22 be formed, bent or molded?
Hot bend/form at 900–1050 °C followed by re-heat treatment; cold bending is limited and should be followed by stress relief.
What is the maximum service temperature of A369 FP22?
A369 FP22 is rated for continuous use to about 580°C (1,076 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between A369 FP22 Annealed and A369 FP22-IA?
Annealed is the default condition — standard stocked condition for FP22 forged-and-bored pipe: softest, most machinable, easiest to bend and weld, meets 415/205 MPa minimums. IA: pick when very uniform low hardness and dimensional stability across heavy wall sections are needed for machining or field bending. Yield strength is 305 MPa in Annealed versus 300 MPa in IA.
How much does A369 FP22 cost?
A369 FP22 is a premium-cost steel ($$$), cheaper than about 51% of the materials FabDigit quotes. Part price depends far more on geometry, tolerance and quantity than on the raw stock — upload a CAD file for a live quote.
Sources
- ASTM A369/A369M — Carbon and Ferritic Alloy Steel Forged and Bored Pipe for High-Temperature Service — ASTM International (2018)
- ASTM A335/A335M — Seamless Ferritic Alloy-Steel Pipe for High-Temperature Service (P22) — ASTM International (2022)
- EN 10216-2 — Seamless steel tubes for pressure purposes (10CrMo9-10, 1.7380) — CEN (2020)
- ASME BPVC Section II Part D — Material properties (2.25Cr-1Mo) — ASME (2023)
- ASM Handbook Vol.1 — Properties and Selection: Irons, Steels, and High-Performance Alloys — ASM International (1990)
- API RP 941 — Steels for Hydrogen Service at Elevated Temperatures (Nelson curves) — API (2016)
- GB/T 5310 — Seamless steel tubes for high pressure boiler (12Cr2Mo1G) — SAC (2017)
Property data is compiled from published supplier and standards handbooks and normalised for comparison; hardness values on non-Brinell scales are converted approximately for charting only. Manufacturability limits are FabDigit quote-engine defaults and may be relaxed by engineering review. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.