Aluminum A535.0-F (As fabricated)
Temper · default condition
AA A535.0 · UNS A15350
Standard supply condition: sand-cast and used as-cast for corrosion-resistant, dimensionally stable, easily machined parts.
Values for the F condition
Other A535.0 tempers and conditions
A535.0 is listed in 3 conditions; see the grade overview at A535.0.
Compare all 3 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
FDefaultThis page As fabricated | Standard supply condition: sand-cast and used as-cast for corrosion-resistant, dimensionally stable, easily machined parts. | 125 | 275 | 12 | 65 HB | 23 % IACS |
F | Used for near-net aerospace/instrument housings where surface finish and thin walls matter more than peak strength. | 125 | 265 | 10 | 65 HB | 23 % IACS |
F | Choose for higher-volume, thinner-section parts where the chill of a metal mould raises strength and refines the structure. | 130 | 275 | 9 | 70 HB | 23 % IACS |
What is A535.0-F?
A535.0-F is A535.0 in the F temper — standard supply condition: sand-cast and used as-cast for corrosion-resistant, dimensionally stable, easily machined parts. A535.0-F has a yield strength of 125 MPa (18.1 ksi) and a tensile strength of 275 MPa (39.9 ksi) — weaker than 75% of aluminum grades. Elongation at break is 12% and the elastic modulus is 70 GPa (10.2 Msi). A535.0-F has a density of 2.62 g/cm³ (0.0947 lb/in³), lighter than 96% of aluminum grades. It melts at 549°C (1,020 °F).
Advantages
- Good corrosion resistance — 85/100, better than 100% of aluminum grades
- Polishes to a fine finish — 90/100, better than 98% of aluminum grades
- Easy to machine — 88/100, better than 96% of aluminum grades
Limitations
- Low electrical conductivity — 23 % IACS, worse than 97% of aluminum grades
- Poor heat conductor — 96 W/m·K (55.5 BTU/hr·ft·°F), worse than 95% of aluminum grades
- Limited service temperature — 120°C (248 °F), worse than 79% of aluminum grades
- Low strength — 125 MPa (18.1 ksi), worse than 75% of aluminum grades
A535.0-F properties
Typical room-temperature values for A535.0-F; 10 are specific to this condition. Other listed values are A535.0 reference data and may not represent this condition. Bars are the position among aluminum grades.
Physical3
A535.0-F has a density of 2.62 g/cm³ (0.0947 lb/in³), lighter than 96% of aluminum grades. It melts at 549°C (1,020 °F).
Mechanical11
A535.0-F has a yield strength of 125 MPa (18.1 ksi) and a tensile strength of 275 MPa (39.9 ksi) — weaker than 75% of aluminum grades. Elongation at break is 12% and the elastic modulus is 70 GPa (10.2 Msi).
Thermal6
A535.0-F is rated for continuous service to 120°C (248 °F). It conducts heat at 96 W/m·K (55.5 BTU/hr·ft·°F), worse than 95% of aluminum grades. Thermal expansion is 24.5 µm/m·K (13.6 µin/in·°F).
Electrical3
A535.0-F conducts electricity at 23 % IACS, worse than 97% of aluminum grades.
Chemical & Environmental3
Corrosion resistance is excellent (85/100), better than 100% of aluminum grades.
Sustainability4
Producing a kilogram of A535.0-F takes about 200 MJ of energy and emits 12 kg of CO₂ — less than 60% of aluminum grades. Typical recycled content is 30%.
Manufacturability8
A535.0-F's machinability is excellent (88/100, better than 96% of aluminum grades); weldability very good (70/100); formability poor (15/100).
Common Calculations5
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with A535.0-F
Is A535.0 easy to machine?
Machines very freely with sharp positive-rake tools and high speeds; gives clean chips and excellent surface finish with minimal built-up edge.
Can A535.0 be welded?
Readily GTAW/GMAW welded with 5356 or matching Al-Mg filler; use clean, dry surfaces and low heat input to limit Mg loss and porosity.
Can A535.0 be formed, bent or molded?
Foundry-critical alloy: melt under protective flux/cover gas, keep low turbulence gating with generous risers, and expect low fluidity plus hot-tearing risk in thin or restrained sections.
What surface finishes work on A535.0?
Outstanding bright polishing and clear/colour anodising; chromate or trivalent conversion coatings and paint adhere well, but avoid flux brazing and Hg-bearing chemicals.
A535.0 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Si | ≤ 0.2 | — |
| Fe | ≤ 0.2 | — |
| Cu | ≤ 0.1 | — |
| Mn | 0.1 – 0.25 | 0.18 |
| Mgprincipal alloying element | 6.5 – 7.5 | 7 |
| Tigrain refiner | 0.15 – 0.25 | 0.2 |
| Others (each) | ≤ 0.05 | — |
| Others (total) | ≤ 0.15 | — |
| Al | balance | — |
A535.0-F — frequently asked
What is A535.0-F used for?
A535.0-F is typically used for marine hardware, food-processing equipment and decorative castings. In short: corrosion-resistant cast aluminum; free-machining as-cast; bright-anodizing casting alloy.
What is the yield strength of A535.0-F?
A535.0-F has a typical yield strength of 125 MPa (18.1 ksi) and a tensile strength of 275 MPa (39.9 ksi) — weaker than 75% of aluminum grades. Strength varies by condition: see the 3 listed tempers.
Is A535.0-F easy to machine?
Yes — machinability is rated excellent (88/100, better than 96% of aluminum grades). Machines very freely with sharp positive-rake tools and high speeds; gives clean chips and excellent surface finish with minimal built-up edge.
Can A535.0-F be welded?
Yes — weldability is rated very good (70/100). Readily GTAW/GMAW welded with 5356 or matching Al-Mg filler; use clean, dry surfaces and low heat input to limit Mg loss and porosity.
What surface finishes work on A535.0-F?
Outstanding bright polishing and clear/colour anodising; chromate or trivalent conversion coatings and paint adhere well, but avoid flux brazing and Hg-bearing chemicals.
Can A535.0-F be formed, bent or molded?
Foundry-critical alloy: melt under protective flux/cover gas, keep low turbulence gating with generous risers, and expect low fluidity plus hot-tearing risk in thin or restrained sections.
What is the maximum service temperature of A535.0-F?
A535.0-F is rated for continuous use to about 120°C (248 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between A535.0-F and A535.0 F-PM?
F is the default condition — standard supply condition: sand-cast and used as-cast for corrosion-resistant, dimensionally stable, easily machined parts. F-PM: choose for higher-volume, thinner-section parts where the chill of a metal mould raises strength and refines the structure. Yield strength is 125 MPa in F versus 130 MPa in F-PM.
Sources
- ASTM B26/B26M — Aluminum-Alloy Sand Castings — ASTM International (2018)
- Aluminum Association Teal Sheets — Registration Record of Aluminum Casting Alloys — The Aluminum Association (2018)
- ASM Handbook Vol. 2 — Properties and Selection: Nonferrous Alloys — ASM International (1990)
- ASM Handbook Vol. 15 — Casting — ASM International (2008)
- ASM Handbook Vol. 13B — Corrosion: Materials — ASM International (2005)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.