Steel A285 N&T (Normalized and tempered)
Heat-treated state
ASTM A285
Normalize plus a high temper to soften/stabilize the plate; used when both toughness and dimensional/residual-stress stability are required.
Values for the N&T condition
Other A285 tempers and conditions
A285 is listed in 8 conditions; see the grade overview at A285.
Compare all 8 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Grade A | Softest, most weldable and most formable A285 grade; pick it for deeply dished heads and low design-pressure tanks. | 190 | 350 | 30 | 110 HB | 10.8 % IACS |
Grade B | Middle strength/ductility compromise when Grade A is too weak but full Grade C carbon is unwelcome for welding. | 215 | 400 | 28 | 120 HB | 10.5 % IACS |
full or subcritical anneal / stress relieved | Choose when maximum ductility and lowest residual stress are needed for severe cold forming or after heavy weld fabrication (PWHT). | 225 | 415 | 34 | 118 HB | 10.8 % IACS |
Grade C | Most commonly stocked A285 grade; use for the highest allowable stress of the specification in storage tanks and low-pressure vessels. | 240 | 440 | 27 | 130 HB | 10.1 % IACS |
HRDefault Hot rolled | Standard stock condition for A285 pressure-vessel plate; take it for ordinary welded tanks and boiler shells with no low-temperature requirement. | 250 | 450 | 30 | 130 HB | — |
N&TThis page Normalized and tempered | Normalize plus a high temper to soften/stabilize the plate; used when both toughness and dimensional/residual-stress stability are required. | 255 | 440 | 32 | 128 HB | 10.8 % IACS |
austenitized ~900 °C, air cooled | Specify for heavier plate or when uniform fine grain and better notch toughness are wanted (supplementary impact testing). | 260 | 455 | 31 | 132 HB | 10.8 % IACS |
Quenched and tempered | Rarely used for A285 (carbon too low for real hardenability); ordered only where slightly higher yield and best low-temperature toughness are needed in thin plate. | 320 | 490 | 27 | 145 HB | 10.5 % IACS |
What is A285 N&T?
A285 N&T is A285 heat treated to N&T — normalize plus a high temper to soften/stabilize the plate; used when both toughness and dimensional/residual-stress stability are required. A285 N&T has a yield strength of 255 MPa (37 ksi) and a tensile strength of 440 MPa (63.8 ksi) — weaker than 93% of steel grades. Elongation at break is 32% and the elastic modulus is 200 GPa (29 Msi). A285 N&T has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,460°C (2,660 °F). HR is the default condition FabDigit quotes; N&T is available on request or by drawing note.
Advantages
- Ductile — tolerates forming and impact — 32%, better than 95% of steel grades
- Easy to machine — 68/100, better than 95% of steel grades
- High electrical conductivity — 10.8 % IACS, better than 94% of steel grades
- Forms and bends easily — 82/100, better than 94% of steel grades
- Readily welded — 92/100, better than 93% of steel grades
Limitations
- Hard to polish — 40/100, worse than 96% of steel grades
- Low strength — 255 MPa (37 ksi), worse than 93% of steel grades
A285 N&T properties
Typical room-temperature values for A285 N&T; 23 are specific to this condition. Other listed values are A285 reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
A285 N&T has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,460°C (2,660 °F).
Mechanical15
A285 N&T has a yield strength of 255 MPa (37 ksi) and a tensile strength of 440 MPa (63.8 ksi) — weaker than 93% of steel grades. Elongation at break is 32% and the elastic modulus is 200 GPa (29 Msi).
Thermal6
A285 N&T is rated for continuous service to 425°C (797 °F). It conducts heat at 51 W/m·K (29.5 BTU/hr·ft·°F), better than 92% of steel grades. Thermal expansion is 12 µm/m·K (6.67 µin/in·°F).
Electrical3
A285 N&T conducts electricity at 10.8 % IACS, better than 94% of steel grades.
Chemical & Environmental3
Corrosion resistance is not recommended (10/100), worse than 86% of steel grades.
Sustainability4
Producing a kilogram of A285 N&T takes about 25 MJ of energy and emits 1.9 kg of CO₂ — less than 82% of steel grades. Typical recycled content is 25%.
Manufacturability7
A285 N&T's machinability is good (68/100, better than 95% of steel grades); weldability excellent (92/100); formability very good (82/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with A285 N&T
Is A285 easy to machine?
Machines easily but gummy — use positive rake, sharp tools and generous coolant to avoid built-up edge and torn threads; drilling and plasma/oxy cutting are routine.
Can A285 be welded?
Excellent weldability by SMAW/GMAW/SAW with E70xx-class filler; no preheat below ~25 mm, preheat 100 °C for heavy sections, PWHT per ASME VIII when required by thickness or service.
Can A285 be formed, bent or molded?
Very good cold formability for shells, dished heads and rolled sections; hot form 900–1200 °C and re-normalize if cold strain exceeds code limits.
What surface finishes work on A285?
No passive film — must be blast-cleaned and painted, epoxy-lined, galvanized or metallized; phosphate pretreatment improves paint adhesion.
A285 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Cheat analysis max: Gr A 0.17, Gr B 0.22, Gr C 0.28 | ≤ 0.28 | 0.2 |
| Mnheat analysis max (0.98 product analysis) | ≤ 0.9 | 0.6 |
| P | ≤ 0.04 | 0.02 |
| S | ≤ 0.04 | 0.01 |
| Sinot specified by A285; typical mill practice (killed/semi-killed) | ≤ 0.4 | 0.2 |
| Fe | balance | — |
A285 N&T — frequently asked
What is A285 N&T used for?
A285 N&T is typically used for boilers, storage tanks and petrochemical vessels. In short: pressure-vessel quality plate.
What is the yield strength of A285 N&T?
A285 N&T has a typical yield strength of 255 MPa (37 ksi) and a tensile strength of 440 MPa (63.8 ksi) — weaker than 93% of steel grades. Strength varies by condition: see the 8 listed tempers.
Is A285 N&T easy to machine?
Reasonably — machinability is rated good (68/100, better than 95% of steel grades). Machines easily but gummy — use positive rake, sharp tools and generous coolant to avoid built-up edge and torn threads; drilling and plasma/oxy cutting are routine.
Can A285 N&T be welded?
Yes — weldability is rated excellent (92/100). Excellent weldability by SMAW/GMAW/SAW with E70xx-class filler; no preheat below ~25 mm, preheat 100 °C for heavy sections, PWHT per ASME VIII when required by thickness or service.
What surface finishes work on A285 N&T?
No passive film — must be blast-cleaned and painted, epoxy-lined, galvanized or metallized; phosphate pretreatment improves paint adhesion.
Can A285 N&T be formed, bent or molded?
Very good cold formability for shells, dished heads and rolled sections; hot form 900–1200 °C and re-normalize if cold strain exceeds code limits.
What is the maximum service temperature of A285 N&T?
A285 N&T is rated for continuous use to about 425°C (797 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Can FabDigit make parts in A285 N&T?
Yes — A285 N&T is available for CNC machining and sheet metal; every part is priced by an engineer rather than instantly. Upload a STEP file to get a price and a DFM check.
Sources
- ASTM A285/A285M — Pressure Vessel Plates, Carbon Steel, Low- and Intermediate-Tensile Strength — ASTM International (2017)
- ASME BPVC Section II Part D — Properties (Metric) — ASME (2023)
- ASM Handbook Vol.1: Properties and Selection — Irons, Steels, and High-Performance Alloys — ASM International (1990)
- Machinery's Handbook, 31st ed. (machinability ratings) — Industrial Press (2020)
- GB/T 713 Q245R (comparable grade) — SAC (2014)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.