Steel A387 Gr 12 CL1-ANN
Heat-treated state
ASTM A387 Gr 12 · UNS K11757
CL1-ANN = class 1, Annealed
Softest, most formable and weld-friendly condition; pick for heavy cold forming or when only Class 1 minimum strength is required.
Values for the CL1-ANN condition
Other A387 Gr 12 tempers and conditions
A387 Gr 12 is listed in 4 conditions; see the grade overview at A387 Gr 12.
Compare all 4 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
CL1-ANNThis page Class 1, Annealed | Softest, most formable and weld-friendly condition; pick for heavy cold forming or when only Class 1 minimum strength is required. | 270 | 430 | 28 | 137 HB | — |
Class 1, Normalized and Tempered | Class 1 strength with a refined normalized structure — better toughness than the annealed plate at the same strength level. | 290 | 460 | 27 | 145 HB | — |
CL2-NTDefault Class 2, Normalized and Tempered | The standard stocked condition for refinery and boiler pressure vessels — higher allowable stress than Class 1 with good toughness. | 330 | 500 | 24 | 160 HB | — |
Class 2, Quenched and Tempered | Accelerated-cooled (liquid quenched) and tempered heavy plate — used when Class 2 properties must be met through thick sections or when low-temperature Charpy values are specified. | 370 | 530 | 23 | 175 HB | — |
What is A387 Gr 12 CL1-ANN?
A387 Gr 12 CL1-ANN is A387 Gr 12 heat treated to CL1-ANN — softest, most formable and weld-friendly condition; pick for heavy cold forming or when only Class 1 minimum strength is required. A387 Gr 12 CL1-ANN has a yield strength of 270 MPa (39.2 ksi) and a tensile strength of 430 MPa (62.4 ksi) — weaker than 91% of steel grades. Elongation at break is 28% and the elastic modulus is 205 GPa (29.7 Msi). A387 Gr 12 CL1-ANN has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,425°C (2,597 °F). CL2-NT is the default condition FabDigit quotes; CL1-ANN is available on request or by drawing note.
Advantages
- Tough — resists crack growth — 150 MPa·√m (136.5 ksi·√in), better than 96% of steel grades
- High service temperature — 540°C (1,004 °F), better than 93% of steel grades
- Ductile — tolerates forming and impact — 28%, better than 89% of steel grades
- Forms and bends easily — 68/100, better than 83% of steel grades
Limitations
- Low strength — 270 MPa (39.2 ksi), worse than 91% of steel grades
- Hard to polish — 45/100, worse than 84% of steel grades
A387 Gr 12 CL1-ANN properties
Typical room-temperature values for A387 Gr 12 CL1-ANN; 17 are specific to this condition. Other listed values are A387 Gr 12 reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
A387 Gr 12 CL1-ANN has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,425°C (2,597 °F).
Mechanical16
A387 Gr 12 CL1-ANN has a yield strength of 270 MPa (39.2 ksi) and a tensile strength of 430 MPa (62.4 ksi) — weaker than 91% of steel grades. Elongation at break is 28% and the elastic modulus is 205 GPa (29.7 Msi).
Thermal6
A387 Gr 12 CL1-ANN is rated for continuous service to 540°C (1,004 °F). It conducts heat at 42 W/m·K (24.3 BTU/hr·ft·°F), worse than 56% of steel grades. Thermal expansion is 12.3 µm/m·K (6.83 µin/in·°F).
Electrical3
A387 Gr 12 CL1-ANN conducts electricity at 7.8 % IACS, worse than 57% of steel grades.
Chemical & Environmental3
Corrosion resistance is poor (16/100), better than 79% of steel grades.
Sustainability4
Producing a kilogram of A387 Gr 12 CL1-ANN takes about 29 MJ of energy and emits 2.3 kg of CO₂ — less than 53% of steel grades. Typical recycled content is 25%.
Manufacturability7
A387 Gr 12 CL1-ANN's machinability is good (60/100, better than 83% of steel grades); weldability good (65/100); formability good (68/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with A387 Gr 12 CL1-ANN
Is A387 Gr 12 easy to machine?
Machines like a medium-carbon low-alloy steel at ~60% of 1212; use rigid setups, carbide tooling and moderate speeds — the bainitic Class 2 plate work-hardens the cut surface if feeds are too light.
Can A387 Gr 12 be welded?
Readily weldable with matching B2/E8018-B2 (or low-carbon B2L) consumables, but requires 150–250 °C preheat/interpass and PWHT at ~690–730 °C; keep hydrogen low to avoid delayed cracking.
Can A387 Gr 12 be formed, bent or molded?
Cold-form with generous bend radii (≥3t) in the annealed condition; hot forming at 900–1000 °C is preferred for heads and thick shells, followed by re-normalizing and tempering.
What surface finishes work on A387 Gr 12?
No anodizing; shot-blast and paint, metallize or alonize for oxidation and atmospheric protection — bare plate rusts quickly in humid storage.
A387 Gr 12 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Cheat analysis, ASTM A387 | 0.05 – 0.17 | 0.12 |
| Mn | 0.4 – 0.65 | 0.52 |
| Si | 0.15 – 0.4 | 0.27 |
| P | ≤ 0.03 | 0.01 |
| S | ≤ 0.03 | 0.01 |
| Cr | 0.8 – 1.15 | 1 |
| Mo | 0.45 – 0.6 | 0.52 |
| Fe | balance | — |
A387 Gr 12 CL1-ANN — frequently asked
What is A387 Gr 12 CL1-ANN used for?
A387 Gr 12 CL1-ANN is typically used for boiler drums, steam piping flanges, refinery reactor plate and heat exchanger shells. In short: leanest Cr-Mo A387 plate; best weldability in A387; 540 °C service temperature.
What is the yield strength of A387 Gr 12 CL1-ANN?
A387 Gr 12 CL1-ANN has a typical yield strength of 270 MPa (39.2 ksi) and a tensile strength of 430 MPa (62.4 ksi) — weaker than 91% of steel grades. Strength varies by condition: see the 4 listed tempers.
Is A387 Gr 12 CL1-ANN easy to machine?
Reasonably — machinability is rated good (60/100, better than 83% of steel grades). Machines like a medium-carbon low-alloy steel at ~60% of 1212; use rigid setups, carbide tooling and moderate speeds — the bainitic Class 2 plate work-hardens the cut surface if feeds are too light.
Can A387 Gr 12 CL1-ANN be welded?
Yes — weldability is rated good (65/100). Readily weldable with matching B2/E8018-B2 (or low-carbon B2L) consumables, but requires 150–250 °C preheat/interpass and PWHT at ~690–730 °C; keep hydrogen low to avoid delayed cracking.
What surface finishes work on A387 Gr 12 CL1-ANN?
No anodizing; shot-blast and paint, metallize or alonize for oxidation and atmospheric protection — bare plate rusts quickly in humid storage.
Can A387 Gr 12 CL1-ANN be formed, bent or molded?
Cold-form with generous bend radii (≥3t) in the annealed condition; hot forming at 900–1000 °C is preferred for heads and thick shells, followed by re-normalizing and tempering.
What is the maximum service temperature of A387 Gr 12 CL1-ANN?
A387 Gr 12 CL1-ANN is rated for continuous use to about 540°C (1,004 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between A387 Gr 12 CL2-NT and A387 Gr 12 CL1-ANN?
CL2-NT is the default condition — the standard stocked condition for refinery and boiler pressure vessels — higher allowable stress than Class 1 with good toughness. CL1-ANN: softest, most formable and weld-friendly condition; pick for heavy cold forming or when only Class 1 minimum strength is required. Yield strength is 330 MPa in CL2-NT versus 270 MPa in CL1-ANN.
Sources
- ASTM A387/A387M — Pressure Vessel Plates, Alloy Steel, Chromium-Molybdenum — ASTM International (2021)
- EN 10028-2 (13CrMo4-5, 1.7335) — CEN (2017)
- ASME BPVC Section II Part D — Materials Properties — ASME (2023)
- ASM Handbook Vol.1 — Properties and Selection: Irons, Steels and High-Performance Alloys — ASM International (1990)
- API RP 941 — Steels for Hydrogen Service at Elevated Temperatures — API (2016)
- GB 713 / GB/T 3077 (12CrMo, 15CrMo ) — SAC (2014)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.