Nickel Alloy N06110-AW (As-welded deposit)
Heat-treated state
UNS N06110
Autogenous or matching-filler GTAW joints used without post-weld solution anneal in most fabrications.
Values for the AW condition
Other N06110 tempers and conditions
N06110 is listed in 5 conditions; see the grade overview at N06110.
Compare all 5 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Hot Finished + Annealed | Heavy bar and forged sections annealed after hot work; slightly lower strength scatter than cold-worked stock. | 370 | 770 | 48 | 195 HB | 1.4 % IACS |
SADefault Solution Annealed | Standard stocked condition for plate, sheet, tube and bar — maximum corrosion resistance and ductility. | 390 | 790 | 50 | 200 HB | — |
AWThis page As-welded deposit | Autogenous or matching-filler GTAW joints used without post-weld solution anneal in most fabrications. | 420 | 760 | 35 | 195 HB | 1.4 % IACS |
Cold drawn | Pick for higher-strength downhole tooling and fasteners where 120 ksi-class yield is required in sour service. | 830 | 1,000 | 22 | 32 HRC | 1.4 % IACS |
Heavily Cold Worked, high strength | Maximum-strength condition for springs, wire and small pins; ductility and cold formability are largely exhausted. | 1,100 | 1,250 | 12 | 40 HRC | 1.4 % IACS |
What is N06110-AW?
N06110-AW is N06110 heat treated to AW — autogenous or matching-filler GTAW joints used without post-weld solution anneal in most fabrications. N06110-AW has a yield strength of 420 MPa (60.9 ksi) and a tensile strength of 760 MPa (110 ksi) — stronger than 62% of nickel alloy grades. Elongation at break is 35% and the elastic modulus is 205 GPa (29.7 Msi). N06110-AW has a density of 8.4 g/cm³ (0.303 lb/in³), heavier than 57% of nickel alloy grades. It melts at 1,330°C (2,426 °F). SA is the default condition FabDigit quotes; AW is available on request or by drawing note.
Limitations
- Poor heat conductor — 9 W/m·K (5.2 BTU/hr·ft·°F), worse than 97% of nickel alloy grades
N06110-AW properties
Typical room-temperature values for N06110-AW; 22 are specific to this condition. Other listed values are N06110 reference data and may not represent this condition. Bars are the position among nickel alloy grades.
Physical3
N06110-AW has a density of 8.4 g/cm³ (0.303 lb/in³), heavier than 57% of nickel alloy grades. It melts at 1,330°C (2,426 °F).
Mechanical13
N06110-AW has a yield strength of 420 MPa (60.9 ksi) and a tensile strength of 760 MPa (110 ksi) — stronger than 62% of nickel alloy grades. Elongation at break is 35% and the elastic modulus is 205 GPa (29.7 Msi).
Thermal6
N06110-AW is rated for continuous service to 650°C (1,202 °F). It conducts heat at 9 W/m·K (5.2 BTU/hr·ft·°F), worse than 97% of nickel alloy grades. Thermal expansion is 12.3 µm/m·K (6.83 µin/in·°F).
Electrical3
N06110-AW conducts electricity at 1.4 % IACS, worse than 65% of nickel alloy grades.
Chemical & Environmental3
Corrosion resistance is excellent (85/100), better than 74% of nickel alloy grades.
Sustainability4
Producing a kilogram of N06110-AW takes about 150 MJ of energy and emits 13 kg of CO₂ — less than 68% of nickel alloy grades. Typical recycled content is 35%.
Manufacturability8
N06110-AW's machinability is not recommended (14/100, worse than 81% of nickel alloy grades); weldability very good (70/100); formability fair (40/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with N06110-AW
Is N06110 easy to machine?
Machine like alloy C-276: rigid setup, positive-rake sharp carbide, low surface speed (~15–25 m/min), heavy constant feed to cut under the work-hardened layer, and flood high-pressure coolant.
Can N06110 be welded?
Readily GTAW/GMAW/PAW welded with matching or over-alloyed Ni-Cr-Mo filler; low heat input, interpass <150 °C, no preheat or PWHT, and remove heat tint by pickling to restore passivity.
Can N06110 be formed, bent or molded?
Cold forms well in the annealed state but work-hardens rapidly — allow generous bend radii and interstage solution anneals; hot work 1150–950 °C followed by rapid water quench.
What surface finishes work on N06110?
Pickle/passivate or electropolish after fabrication; not anodizable — for wear surfaces use nitriding-free coatings such as HVOF carbide or electroless nickel.
N06110 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Crhigh Cr for oxidizing acid and pitting resistance | 30 – 33 | 31 |
| Mo | 9 – 11 | 10 |
| W | 1.5 – 3.5 | 3 |
| Feresidual | ≤ 6 | 1 |
| Co | ≤ 2 | — |
| Mn | ≤ 1 | 0.3 |
| Si | ≤ 1 | 0.3 |
| Al | ≤ 0.5 | 0.2 |
| Ti | ≤ 0.5 | 0.2 |
| C | ≤ 0.05 | 0.02 |
| P | ≤ 0.03 | — |
| S | ≤ 0.02 | — |
| Nibalance, nominally ~54% | balance | — |
N06110-AW — frequently asked
What is N06110-AW used for?
N06110-AW is typically used for furnace and heat-treatment components, high-temperature fasteners and process industry fixtures. In short: high-strength Ni-Cr-Fe grade; corrosion score 90; 650 °C service limit.
What is the yield strength of N06110-AW?
N06110-AW has a typical yield strength of 420 MPa (60.9 ksi) and a tensile strength of 760 MPa (110 ksi) — stronger than 62% of nickel alloy grades. Strength varies by condition: see the 5 listed tempers.
Is N06110-AW easy to machine?
Not especially — machinability is rated not recommended (14/100, worse than 81% of nickel alloy grades). Machine like alloy C-276: rigid setup, positive-rake sharp carbide, low surface speed (~15–25 m/min), heavy constant feed to cut under the work-hardened layer, and flood high-pressure coolant.
Can N06110-AW be welded?
Yes — weldability is rated very good (70/100). Readily GTAW/GMAW/PAW welded with matching or over-alloyed Ni-Cr-Mo filler; low heat input, interpass <150 °C, no preheat or PWHT, and remove heat tint by pickling to restore passivity.
What surface finishes work on N06110-AW?
Pickle/passivate or electropolish after fabrication; not anodizable — for wear surfaces use nitriding-free coatings such as HVOF carbide or electroless nickel.
Can N06110-AW be formed, bent or molded?
Cold forms well in the annealed state but work-hardens rapidly — allow generous bend radii and interstage solution anneals; hot work 1150–950 °C followed by rapid water quench.
What is the maximum service temperature of N06110-AW?
N06110-AW is rated for continuous use to about 650°C (1,202 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between N06110-SA and N06110 CW-HS?
SA is the default condition — standard stocked condition for plate, sheet, tube and bar — maximum corrosion resistance and ductility. CW-HS: maximum-strength condition for springs, wire and small pins; ductility and cold formability are largely exhausted. Yield strength is 390 MPa in SA versus 1,100 MPa in CW-HS.
Sources
- ASM Handbook Vol. 2 — Properties and Selection: Nonferrous Alloys and Special-Purpose Materials (Ni-Cr-Mo corrosion-resistant alloys) — ASM International (1990)
- ASTM B575 / B574 / B622 — Ni-Cr-Mo alloy plate, sheet, strip, bar and tube (family standards) — ASTM International (2022)
- UNS Metals & Alloys in the Unified Numbering System (N06110 registration) — SAE/ASTM (2017)
- Ni-Cr-Mo-W corrosion-resistant alloy bar data (ALLCORR-type) — specialty alloy producer (2020)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.