Nickel Alloy Inconel 600 vs N06110
Nickel Alloy · grade comparison
Nickel Alloy Inconel 600 and N06110 are both nickel alloy grades. N06110 is the stronger of the two: yield strength 390 MPa (56.6 ksi) against 255 MPa (37 ksi) for Inconel 600, about 53% more; tensile strength follows at 790 MPa (115 ksi) vs 620 MPa (89.9 ksi). N06110 is the more ductile: elongation 50% versus 42% for Inconel 600, and N06110 is harder (200 HB vs 150 HB). Inconel 600 runs hotter in service (1,100°C vs 650°C continuous) and Inconel 600 conducts heat better (14.9 W/m·K vs 9 W/m·K). On the shop floor, Inconel 600 machines more easily (28 vs 16 out of 100) and Inconel 600 welds better (80 vs 70 out of 100).
Inconel 600Choose it when the part sees heat, or when the part is machined in volume.
N06110Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
Inconel 600 vs N06110: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all nickel alloy grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Reduction in Area 60%
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 290 J/g125 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 150 MJ/kg64,488 BTU/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 3
Strength versus weight
Yield strength against density for every nickel alloy grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | Inconel 600 | N06110 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$$ High | $$$$ High |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 3 finishes: Gold Plating, Plasma Spray, Silver Plating.
Inconel 600 vs N06110 — frequently asked
Is N06110 stronger than Inconel 600?
Yes. N06110 has a typical yield strength of 390 MPa (56.6 ksi) against 255 MPa (37 ksi) for Inconel 600 — about 53% more. Tensile strength is 790 MPa (115 ksi) vs 620 MPa (89.9 ksi).
Which is cheaper, Inconel 600 or N06110?
Both sit in the same relative cost tier ($$$$, high); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, Inconel 600 or N06110?
Inconel 600, by a small margin. Both rate poor for machinability — 28/100 against 16/100 for N06110; for welding the order is Inconel 600 first (very good, 80/100) then N06110 (very good, 70/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in Inconel 600 and N06110 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.