Stainless Steel S44725 CR-Temper
Supply condition
UNS S44725
Use light cold rolling after annealing to lift yield to 620 MPa and improve flatness on stiff or springy thin-gauge parts; toughness and formability fall to 14 % elongation.
Values for the CR-Temper condition
Other S44725 tempers and conditions
S44725 is listed in 3 conditions; see the grade overview at S44725.
Compare all 3 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
As-welded deposit | Use these values to assess field-welded GTAW joints without PWHT: Ti/Nb stabilization keeps intergranular attack low, but HAZ grain coarsening cuts toughness to 18 % elongation. | 450 | 600 | 18 | 190 HB | 2.4 % IACS |
AnnealedDefault mill annealed ( / / , ) | Pick this most-stocked state — annealed at 1010–1065 °C, rapidly cooled and pickled — for heat-exchanger tubing and sheet work balancing corrosion resistance with forming. | 480 | 620 | 27 | 180 HB | 2.4 % IACS |
CR-TemperThis page light cold work | Use light cold rolling after annealing to lift yield to 620 MPa and improve flatness on stiff or springy thin-gauge parts; toughness and formability fall to 14 % elongation. | 620 | 720 | 14 | 21 HRC | 2.4 % IACS |
What is S44725 CR-Temper?
S44725 CR-Temper is S44725 supplied in the CR-Temper condition — use light cold rolling after annealing to lift yield to 620 MPa and improve flatness on stiff or springy thin-gauge parts; toughness and formability fall to 14 % elongation. S44725 CR-Temper has a yield strength of 620 MPa (89.9 ksi) and a tensile strength of 720 MPa (104 ksi) — stronger than 88% of stainless steel grades. Elongation at break is 14% and the elastic modulus is 200 GPa (29 Msi). S44725 CR-Temper has a density of 7.67 g/cm³ (0.277 lb/in³), lighter than 95% of stainless steel grades. It melts at 1,420°C (2,588 °F). Annealed is the default condition FabDigit quotes; CR-Temper is available on request or by drawing note.
Advantages
- High strength — 620 MPa (89.9 ksi), better than 88% of stainless steel grades
- Good corrosion resistance — 80/100, better than 88% of stainless steel grades
Limitations
- Limited ductility — 14%, worse than 91% of stainless steel grades
- Limited service temperature — 300°C (572 °F), worse than 90% of stainless steel grades
- Difficult to weld — 50/100, worse than 77% of stainless steel grades
- High embodied carbon — 5.5 kg CO₂/kg, worse than 77% of stainless steel grades
S44725 CR-Temper properties
Typical room-temperature values for S44725 CR-Temper; 23 are specific to this condition. Other listed values are S44725 reference data and may not represent this condition. Bars are the position among stainless steel grades.
Physical3
S44725 CR-Temper has a density of 7.67 g/cm³ (0.277 lb/in³), lighter than 95% of stainless steel grades. It melts at 1,420°C (2,588 °F).
Mechanical15
S44725 CR-Temper has a yield strength of 620 MPa (89.9 ksi) and a tensile strength of 720 MPa (104 ksi) — stronger than 88% of stainless steel grades. Elongation at break is 14% and the elastic modulus is 200 GPa (29 Msi).
Thermal6
S44725 CR-Temper is rated for continuous service to 300°C (572 °F). It conducts heat at 16.5 W/m·K (9.53 BTU/hr·ft·°F), better than 70% of stainless steel grades. Thermal expansion is 10.4 µm/m·K (5.78 µin/in·°F).
Electrical3
S44725 CR-Temper conducts electricity at 2.4 % IACS, better than 67% of stainless steel grades.
Chemical & Environmental3
Corrosion resistance is very good (80/100), better than 88% of stainless steel grades.
Sustainability4
Producing a kilogram of S44725 CR-Temper takes about 62 MJ of energy and emits 5.5 kg of CO₂ — more than 75% of stainless steel grades. Typical recycled content is 40%.
Manufacturability7
S44725 CR-Temper's machinability is fair (43/100, better than 81% of stainless steel grades); weldability fair (50/100); formability fair (35/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with S44725 CR-Temper
Is S44725 easy to machine?
Run lower speeds with heavy feeds in rigid fixtures; the high Mo content promotes tool adhesion and flank wear. Use coated carbide with ample emulsion coolant at roughly 70 % of the cutting speed used for 304.
Can S44725 be welded?
Autogenous GTAW or a Ni-base filler such as ERNiCrMo-3 is recommended, with strict inert gas shielding including argon backing, low heat input and interpass temperature at or below 150 °C. Avoid heavy sections to prevent coarse-grain HAZ embrittlement.
Can S44725 be formed, bent or molded?
Cold bending, roll forming and light stretch forming are practical; use bend radii of 2t or more and bend along the rolling direction. Deep drawing capability is limited and springback exceeds austenitic steels, so avoid excessive cold work.
What surface finishes work on S44725?
Nitric-acid pickling and passivation or electropolishing restores the passive film. It can be mechanically polished to a mirror finish; avoid chloride-bearing cleaners and carbon steel tooling to prevent iron contamination.
S44725 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Clow carbon, with Ti/Nb stabilization | ≤ 0.03 | 0.02 |
| Cr | 28 – 30 | 29 |
| Mo | 3.6 – 4.2 | 3.9 |
| Ni | ≤ 1 | 0.3 |
| Mn | ≤ 1 | 0.3 |
| Si | ≤ 1 | 0.4 |
| N | ≤ 0.05 | 0.02 |
| Ti+Nbtotal stabilizers, usually required ≥6×(C+N) | 0.2 – 1 | 0.5 |
| P | ≤ 0.04 | — |
| S | ≤ 0.03 | — |
| Curesidual element, limited by some specifications | ≤ 0.5 | — |
| Febalance; per 29Cr-4Mo stabilized group (S44735/29-4C); verify heat | balance | — |
S44725 CR-Temper — frequently asked
What is S44725 CR-Temper used for?
S44725 CR-Temper is typically used for seawater equipment, chemical process piping and heat exchangers. In short: stabilized 29Cr-4Mo ferritic; better weld toughness than S44700; 400 °C service ceiling.
What is the yield strength of S44725 CR-Temper?
S44725 CR-Temper has a typical yield strength of 620 MPa (89.9 ksi) and a tensile strength of 720 MPa (104 ksi) — stronger than 88% of stainless steel grades. Strength varies by condition: see the 3 listed tempers.
Is S44725 CR-Temper easy to machine?
Not especially — machinability is rated fair (43/100, better than 81% of stainless steel grades). Run lower speeds with heavy feeds in rigid fixtures; the high Mo content promotes tool adhesion and flank wear. Use coated carbide with ample emulsion coolant at roughly 70 % of the cutting speed used for 304.
Can S44725 CR-Temper be welded?
With care — weldability is rated fair (50/100). Autogenous GTAW or a Ni-base filler such as ERNiCrMo-3 is recommended, with strict inert gas shielding including argon backing, low heat input and interpass temperature at or below 150 °C. Avoid heavy sections to prevent coarse-grain HAZ embrittlement.
What surface finishes work on S44725 CR-Temper?
Nitric-acid pickling and passivation or electropolishing restores the passive film. It can be mechanically polished to a mirror finish; avoid chloride-bearing cleaners and carbon steel tooling to prevent iron contamination.
Can S44725 CR-Temper be formed, bent or molded?
Cold bending, roll forming and light stretch forming are practical; use bend radii of 2t or more and bend along the rolling direction. Deep drawing capability is limited and springback exceeds austenitic steels, so avoid excessive cold work.
What is the maximum service temperature of S44725 CR-Temper?
S44725 CR-Temper is rated for continuous use to about 300°C (572 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between S44725 Annealed and S44725-AW?
Annealed is the default condition — pick this most-stocked state — annealed at 1010–1065 °C, rapidly cooled and pickled — for heat-exchanger tubing and sheet work balancing corrosion resistance with forming. AW: use these values to assess field-welded GTAW joints without PWHT: Ti/Nb stabilization keeps intergranular attack low, but HAZ grain coarsening cuts toughness to 18 % elongation. Yield strength is 480 MPa in Annealed versus 450 MPa in AW.
Sources
- ASTM A240/A240M — Chromium and Chromium-Nickel Stainless Steel Plate, Sheet and Strip — ASTM International (2023)
- ASTM A268/A268M — Seamless and Welded Ferritic Stainless Steel Tubing — ASTM International (2022)
- ASTM A803/A803M — Welded Ferritic Stainless Steel Feedwater Heater Tubes — ASTM International (2021)
- ASM Handbook Vol.1 — Properties and Selection: Irons, Steels, and High-Performance Alloys — ASM International (1990)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.