Stainless Steel S44660-CD (Cold drawn)
Supply condition
UNS S44660
Use where higher strength or tighter tolerance/straightness is needed; lower ductility and residual stress, corrosion still good but stress relief preferred.
Values for the CD condition
Other S44660 tempers and conditions
S44660 is listed in 2 conditions; see the grade overview at S44660.
- Annealed
- CD
Compare all 2 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
AnnealedDefault mill annealed (ASTM A240 / A268 plate, sheet, tube) | Standard stocked condition for condenser/heat-exchanger tube, sheet and plate; best combination of ductility and corrosion resistance. | 500 | 620 | 27 | 190 HB | — |
CDThis page Cold drawn | Use where higher strength or tighter tolerance/straightness is needed; lower ductility and residual stress, corrosion still good but stress relief preferred. | 650 | 750 | 14 | 22 HRC | 2.8 % IACS |
What is S44660-CD?
S44660-CD is S44660 supplied in the CD condition — use where higher strength or tighter tolerance/straightness is needed; lower ductility and residual stress, corrosion still good but stress relief preferred. S44660-CD has a yield strength of 650 MPa (94.3 ksi) and a tensile strength of 750 MPa (109 ksi) — stronger than 90% of stainless steel grades. Elongation at break is 14% and the elastic modulus is 200 GPa (29 Msi). S44660-CD has a density of 7.7 g/cm³ (0.278 lb/in³), lighter than 83% of stainless steel grades. It melts at 1,425°C (2,597 °F). Annealed is the default condition FabDigit quotes; CD is available on request or by drawing note.
Advantages
- Good corrosion resistance — 85/100, better than 92% of stainless steel grades
- High strength — 650 MPa (94.3 ksi), better than 90% of stainless steel grades
- High electrical conductivity — 2.8 % IACS, better than 79% of stainless steel grades
Limitations
- Limited service temperature — 250°C (482 °F), worse than 99% of stainless steel grades
- Limited ductility — 14%, worse than 91% of stainless steel grades
- Difficult to weld — 48/100, worse than 77% of stainless steel grades
S44660-CD properties
Typical room-temperature values for S44660-CD; 23 are specific to this condition. Other listed values are S44660 reference data and may not represent this condition. Bars are the position among stainless steel grades.
Physical3
S44660-CD has a density of 7.7 g/cm³ (0.278 lb/in³), lighter than 83% of stainless steel grades. It melts at 1,425°C (2,597 °F).
Mechanical14
S44660-CD has a yield strength of 650 MPa (94.3 ksi) and a tensile strength of 750 MPa (109 ksi) — stronger than 90% of stainless steel grades. Elongation at break is 14% and the elastic modulus is 200 GPa (29 Msi).
Thermal5
S44660-CD is rated for continuous service to 250°C (482 °F). It conducts heat at 15 W/m·K (8.67 BTU/hr·ft·°F), worse than 59% of stainless steel grades. Thermal expansion is 10.4 µm/m·K (5.78 µin/in·°F).
Electrical3
S44660-CD conducts electricity at 2.8 % IACS, better than 79% of stainless steel grades.
Chemical & Environmental3
Corrosion resistance is excellent (85/100), better than 92% of stainless steel grades.
Sustainability4
Producing a kilogram of S44660-CD takes about 68 MJ of energy and emits 4.8 kg of CO₂ — more than 80% of stainless steel grades. Typical recycled content is 50%.
Manufacturability7
S44660-CD's machinability is fair (37/100, better than 57% of stainless steel grades); weldability fair (48/100); formability fair (35/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with S44660-CD
Is S44660 easy to machine?
Machine like a high-Mo ferritic: rigid setups, sharp positive-rake carbide, moderate speed with heavy flood coolant; it work-hardens less than austenitics but is abrasive and tends to burr.
Can S44660 be welded?
Weld autogenously or with matching/Ni-base (e.g. ERNiCrMo) filler at low heat input and no preheat, with tight inert shielding and backing to limit grain coarsening and interstitial pickup.
Can S44660 be formed, bent or molded?
Cold forms and tube-drawns acceptably but has less stretch than austenitic grades — allow larger bend radii, expect higher springback, and stress relieve heavily worked parts (avoid 400–550 °C soaks).
What surface finishes work on S44660?
Pickle and passivate after hot work or welding; bright annealed or mechanically polished surfaces give best fouling and pitting behaviour; no anodizing or plating needed.
S44660 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| C | ≤ 0.03 | 0.02 |
| Mn | ≤ 1 | 0.4 |
| Si | ≤ 1 | 0.4 |
| P | ≤ 0.04 | — |
| S | ≤ 0.03 | — |
| Cr | 25 – 28 | 26 |
| Ni | 1 – 3.5 | 2.5 |
| Mo | 3 – 4 | 3.2 |
| N | ≤ 0.04 | 0.02 |
| Ti+Nbstabilizer, at least 6×(C+N) | 0.2 – 1 | 0.5 |
| Fe | balance | — |
S44660-CD — frequently asked
What is S44660-CD used for?
S44660-CD is typically used for marine condenser tubes, power plant heat exchangers and seawater piping. In short: marine condenser tube grade; super-ferritic pitting resistance; higher strength than 316L.
What is the yield strength of S44660-CD?
S44660-CD has a typical yield strength of 650 MPa (94.3 ksi) and a tensile strength of 750 MPa (109 ksi) — stronger than 90% of stainless steel grades. Strength varies by condition: see the 2 listed tempers.
Is S44660-CD easy to machine?
Not especially — machinability is rated fair (37/100, better than 57% of stainless steel grades). Machine like a high-Mo ferritic: rigid setups, sharp positive-rake carbide, moderate speed with heavy flood coolant; it work-hardens less than austenitics but is abrasive and tends to burr.
Can S44660-CD be welded?
With care — weldability is rated fair (48/100). Weld autogenously or with matching/Ni-base (e.g. ERNiCrMo) filler at low heat input and no preheat, with tight inert shielding and backing to limit grain coarsening and interstitial pickup.
What surface finishes work on S44660-CD?
Pickle and passivate after hot work or welding; bright annealed or mechanically polished surfaces give best fouling and pitting behaviour; no anodizing or plating needed.
Can S44660-CD be formed, bent or molded?
Cold forms and tube-drawns acceptably but has less stretch than austenitic grades — allow larger bend radii, expect higher springback, and stress relieve heavily worked parts (avoid 400–550 °C soaks).
What is the maximum service temperature of S44660-CD?
S44660-CD is rated for continuous use to about 250°C (482 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between S44660 Annealed and S44660-CD?
Annealed is the default condition — standard stocked condition for condenser/heat-exchanger tube, sheet and plate; best combination of ductility and corrosion resistance. CD: use where higher strength or tighter tolerance/straightness is needed; lower ductility and residual stress, corrosion still good but stress relief preferred. Yield strength is 500 MPa in Annealed versus 650 MPa in CD.
Sources
- ASTM A240/A240M — Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip — ASTM (2022)
- ASTM A268/A268M — Seamless and Welded Ferritic and Martensitic Stainless Steel Tubing — ASTM (2023)
- ASTM A803/A803M — Welded Ferritic Stainless Steel Feedwater Heater Tubes — ASTM (2018)
- Sea-Cure (UNS S44660) superferritic condenser tubing data — Plymouth Tube / Crucible (2020)
- ASM Handbook Vol.1 — Properties and Selection: Irons, Steels, and High-Performance Alloys — ASM International (1990)
- ASM Handbook Vol.13B — Corrosion: Materials — ASM International (2005)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.