Nickel Alloy Incoloy 800HT HW-ANN
Heat-treated state
UNS N08811 · EN 1.4959
HW-ANN = hot-worked and annealed bar
Use for bar that must be code-qualified for elevated-temperature/creep service or heavily machined without distortion.
Values for the HW-ANN condition
Other Incoloy 800HT tempers and conditions
Incoloy 800HT is listed in 7 conditions; see the grade overview at Incoloy 800HT.
Compare all 7 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Solution annealed 1150 °C | Choose for long-term service above 900 °C (cracking coils, reformer and radiant tubes) where creep-rupture life dominates over room-temperature strength. | 215 | 500 | 48 | 130 HB | 1.8 % IACS |
ANNDefault Annealed | Standard stocked condition for pressure vessels, furnace parts and formed components; best combination of ductility and creep strength. | 240 | 520 | 45 | 140 HB | — |
HW-ANNThis page Hot-worked and annealed bar | Use for bar that must be code-qualified for elevated-temperature/creep service or heavily machined without distortion. | 240 | 520 | 45 | 145 HB | 1.8 % IACS |
Cold-worked and annealed | Standard condition for seamless heat-exchanger and furnace tubing: annealed properties with cold-finished dimensional accuracy and bright surface. | 250 | 540 | 43 | 150 HB | 1.8 % IACS |
Hot-worked | Economical bar/forging condition for machined furnace fixtures where slightly higher yield and lower ductility are acceptable. | 280 | 560 | 38 | 160 HB | 1.8 % IACS |
As-welded deposit | Reference condition for fabricated assemblies; joint strength approaches annealed base metal but creep strength of the weld is lower than 800HT base. | 300 | 550 | 33 | 165 HB | 1.7 % IACS |
Cold drawn | Pick for close-tolerance fasteners, pins and instrument tubing needing higher room-temperature strength; not for creep service without re-anneal. | 500 | 680 | 25 | 210 HB | — |
What is Incoloy 800HT HW-ANN?
Incoloy 800HT HW-ANN is Incoloy 800HT heat treated to HW-ANN — use for bar that must be code-qualified for elevated-temperature/creep service or heavily machined without distortion. Incoloy 800HT HW-ANN has a yield strength of 240 MPa (34.8 ksi) and a tensile strength of 520 MPa (75.4 ksi) — weaker than 90% of nickel alloy grades. Elongation at break is 45% and the elastic modulus is 196 GPa (28.4 Msi). Incoloy 800HT HW-ANN has a density of 7.94 g/cm³ (0.287 lb/in³), lighter than 88% of nickel alloy grades. It melts at 1,357°C (2,475 °F). ANN is the default condition FabDigit quotes; HW-ANN is available on request or by drawing note.
Advantages
- Low embodied carbon — 7.5 kg CO₂/kg, better than 96% of nickel alloy grades
- High service temperature — 1,100°C (2,012 °F), better than 88% of nickel alloy grades
- High electrical conductivity — 1.8 % IACS, better than 81% of nickel alloy grades
Limitations
- Low strength — 240 MPa (34.8 ksi), worse than 90% of nickel alloy grades
Incoloy 800HT HW-ANN properties
Typical room-temperature values for Incoloy 800HT HW-ANN; 22 are specific to this condition. Other listed values are Incoloy 800HT reference data and may not represent this condition. Bars are the position among nickel alloy grades.
Physical3
Incoloy 800HT HW-ANN has a density of 7.94 g/cm³ (0.287 lb/in³), lighter than 88% of nickel alloy grades. It melts at 1,357°C (2,475 °F).
Mechanical13
Incoloy 800HT HW-ANN has a yield strength of 240 MPa (34.8 ksi) and a tensile strength of 520 MPa (75.4 ksi) — weaker than 90% of nickel alloy grades. Elongation at break is 45% and the elastic modulus is 196 GPa (28.4 Msi).
Thermal6
Incoloy 800HT HW-ANN is rated for continuous service to 1,100°C (2,012 °F). It conducts heat at 11.5 W/m·K (6.64 BTU/hr·ft·°F), better than 57% of nickel alloy grades. Thermal expansion is 14.4 µm/m·K (8 µin/in·°F).
Electrical3
Incoloy 800HT HW-ANN conducts electricity at 1.8 % IACS, better than 81% of nickel alloy grades.
Chemical & Environmental3
Corrosion resistance is very good (70/100), worse than 77% of nickel alloy grades.
Sustainability4
Producing a kilogram of Incoloy 800HT HW-ANN takes about 110 MJ of energy and emits 7.5 kg of CO₂ — less than 93% of nickel alloy grades. Typical recycled content is 40%.
Manufacturability7
Incoloy 800HT HW-ANN's machinability is poor (28/100, better than 82% of nickel alloy grades); weldability very good (75/100); formability very good (70/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with Incoloy 800HT HW-ANN
Is Incoloy 800HT easy to machine?
Treat like a gummy austenitic Ni alloy: rigid setup, positive-rake carbide or ceramic, low speed with heavy feed, flood coolant and never dwell — it work-hardens instantly.
Can Incoloy 800HT be welded?
Readily welded by GTAW/GMAW/SMAW with ERNiCr-3 (Alloy 82) or ENiCrFe-3; no preheat or PWHT needed, keep heat input low and interpass clean to avoid hot cracking.
Can Incoloy 800HT be formed, bent or molded?
Formable hot (1150–900 °C) and cold, but springback and forming loads are high; intermediate anneals at ~980–1050 °C are usual, and final creep parts should be re-annealed at ≥1120 °C for coarse grain.
What surface finishes work on Incoloy 800HT?
Pickle/passivate or grit-blast plus pickling to remove the tenacious Cr-rich scale; can be mechanically polished, but no anodising — a service-formed adherent oxide is the working surface.
Incoloy 800HT chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Ni | 30 – 35 | 32.5 |
| Cr | 19 – 23 | 21 |
| Chigher C than 800H for creep strength | 0.06 – 0.1 | 0.08 |
| Al | 0.25 – 0.6 | 0.45 |
| Ti | 0.25 – 0.6 | 0.45 |
| Al+Tikey 800HT requirement | 0.85 – 1.2 | 1 |
| Mn | ≤ 1.5 | 0.8 |
| Si | ≤ 1 | 0.4 |
| Cu | ≤ 0.75 | 0.3 |
| S | ≤ 0.02 | 0 |
| Febalance, 39.5 % min per ASTM | ≥ 39.5 (balance) | — |
Incoloy 800HT HW-ANN — frequently asked
What is Incoloy 800HT HW-ANN used for?
Incoloy 800HT HW-ANN is typically used for ethylene furnace tubes, hydrogen reformer components and catalyst support baskets. In short: highest-creep 800-series grade; stable above 1000 °C; furnace tube standard.
What is the yield strength of Incoloy 800HT HW-ANN?
Incoloy 800HT HW-ANN has a typical yield strength of 240 MPa (34.8 ksi) and a tensile strength of 520 MPa (75.4 ksi) — weaker than 90% of nickel alloy grades. Strength varies by condition: see the 7 listed tempers.
Is Incoloy 800HT HW-ANN easy to machine?
Not especially — machinability is rated poor (28/100, better than 82% of nickel alloy grades). Treat like a gummy austenitic Ni alloy: rigid setup, positive-rake carbide or ceramic, low speed with heavy feed, flood coolant and never dwell — it work-hardens instantly.
Can Incoloy 800HT HW-ANN be welded?
Yes — weldability is rated very good (75/100). Readily welded by GTAW/GMAW/SMAW with ERNiCr-3 (Alloy 82) or ENiCrFe-3; no preheat or PWHT needed, keep heat input low and interpass clean to avoid hot cracking.
What surface finishes work on Incoloy 800HT HW-ANN?
Pickle/passivate or grit-blast plus pickling to remove the tenacious Cr-rich scale; can be mechanically polished, but no anodising — a service-formed adherent oxide is the working surface.
Can Incoloy 800HT HW-ANN be formed, bent or molded?
Formable hot (1150–900 °C) and cold, but springback and forming loads are high; intermediate anneals at ~980–1050 °C are usual, and final creep parts should be re-annealed at ≥1120 °C for coarse grain.
What is the maximum service temperature of Incoloy 800HT HW-ANN?
Incoloy 800HT HW-ANN is rated for continuous use to about 1,100°C (2,012 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between Incoloy 800HT-ANN and Incoloy 800HT-CD?
ANN is the default condition — standard stocked condition for pressure vessels, furnace parts and formed components; best combination of ductility and creep strength. CD: pick for close-tolerance fasteners, pins and instrument tubing needing higher room-temperature strength; not for creep service without re-anneal. Yield strength is 240 MPa in ANN versus 500 MPa in CD.
Sources
- ASTM B409 — Ni-Fe-Cr Alloy Plate, Sheet and Strip — ASTM International (2021)
- ASTM B408 / B407 — Ni-Fe-Cr Alloy Rod & Bar / Seamless Pipe & Tube — ASTM International (2021)
- INCOLOY alloys 800H & 800HT publication SMC-047 — Special Metals Corporation (2004)
- ASME BPVC Section II Part D — allowable stresses and physical properties for N08811 — ASME (2023)
- EN 10095 / DIN 17742 material 1.4959 (X8NiCrAlTi32-21) — CEN / DIN (2018)
- ASM Handbook Vol. 1 — Heat-Resistant and Superalloys — ASM International (1990)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.