Steel DC06 +Z
Finish state
EN DC06
+Z = hot-dip galvanized extra-deep-drawing sheet
Ordered when heavier zinc (Z100–Z275) corrosion protection is required; zinc layer slightly raises friction and reduces the achievable draw ratio versus bare DC06.
Values for the +Z condition
Other DC06 tempers and conditions
DC06 is listed in 5 conditions; see the grade overview at DC06.
Compare all 5 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Annealed last (not skin-passed), maximum softness | Ordered when the very lowest yield and no roughness imprint are needed; must be formed promptly and can show slight stretcher-strain risk on non-IF grades (IF chemistry makes DC06 essentially non-aging). | 130 | 285 | 45 | 82 HB | 13 % IACS |
CRDefault Cold rolled | Standard stock condition: continuous-annealed and skin-passed coil/sheet, non-aging for 6 months, for general deep-drawn body and appliance panels. | 150 | 300 | 42 | 88 HB | 13 % IACS |
Surface quality B, matt finish | Pick for class-A painted exterior panels where surface defects are not permitted on one side and Ra ≈ 0.6–1.9 µm matt texture aids press lubrication and paint appearance. | 150 | 300 | 42 | 88 HB | 13 % IACS |
+ZThis page Hot-dip galvanized extra-deep-drawing sheet | Ordered when heavier zinc (Z100–Z275) corrosion protection is required; zinc layer slightly raises friction and reduces the achievable draw ratio versus bare DC06. | 150 | 300 | 41 | 88 HB | 13 % IACS |
Electrolytically zinc coated (EN 10152), e.g. ZE25/25 | Choose for painted automotive body panels needing corrosion protection with the smoothest coated surface; thin zinc layer keeps deep-drawing behaviour almost unchanged. | 155 | 305 | 41 | 90 HB | 13 % IACS |
What is DC06 +Z?
DC06 +Z is DC06 supplied in the +Z condition — ordered when heavier zinc (Z100–Z275) corrosion protection is required; zinc layer slightly raises friction and reduces the achievable draw ratio versus bare DC06. DC06 +Z has a yield strength of 150 MPa (21.8 ksi) and a tensile strength of 300 MPa (43.5 ksi) — weaker than 100% of steel grades. Elongation at break is 41% and the elastic modulus is 210 GPa (30.5 Msi). DC06 +Z has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,500°C (2,732 °F). CR is the default condition FabDigit quotes; +Z is available on request or by drawing note.
Advantages
- High electrical conductivity — 13 % IACS, better than 100% of steel grades
- Ductile — tolerates forming and impact — 41%, better than 99% of steel grades
- Conducts heat well — 58 W/m·K (33.5 BTU/hr·ft·°F), better than 99% of steel grades
- Forms and bends easily — 95/100, better than 99% of steel grades
- Good corrosion resistance — 35/100, better than 97% of steel grades
Limitations
- Low strength — 150 MPa (21.8 ksi), worse than 100% of steel grades
- Limited service temperature — 200°C (392 °F), worse than 93% of steel grades
- Difficult to machine — 40/100, worse than 77% of steel grades
DC06 +Z properties
Typical room-temperature values for DC06 +Z; 21 are specific to this condition. Other listed values are DC06 reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
DC06 +Z has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,500°C (2,732 °F).
Mechanical16
DC06 +Z has a yield strength of 150 MPa (21.8 ksi) and a tensile strength of 300 MPa (43.5 ksi) — weaker than 100% of steel grades. Elongation at break is 41% and the elastic modulus is 210 GPa (30.5 Msi).
Thermal6
DC06 +Z is rated for continuous service to 200°C (392 °F). It conducts heat at 58 W/m·K (33.5 BTU/hr·ft·°F), better than 99% of steel grades. Thermal expansion is 12 µm/m·K (6.67 µin/in·°F).
Electrical3
DC06 +Z conducts electricity at 13 % IACS, better than 100% of steel grades.
Chemical & Environmental3
Corrosion resistance is fair (35/100), better than 97% of steel grades.
Sustainability4
Producing a kilogram of DC06 +Z takes about 26 MJ of energy and emits 2.2 kg of CO₂ — less than 64% of steel grades. Typical recycled content is 20%.
Manufacturability7
DC06 +Z's machinability is fair (40/100, worse than 77% of steel grades); weldability very good (80/100); formability excellent (95/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with DC06 +Z
Is DC06 easy to machine?
Very soft and gummy — use sharp positive-rake tools, high speed and flood coolant to avoid burrs and built-up edge; blanking and laser cutting are preferred over milling.
Can DC06 be welded?
Excellent for resistance spot, MAG and laser welding thanks to ultra-low C, P, S; zinc-coated variants need higher electrode force/current and fume extraction.
Can DC06 be formed, bent or molded?
Best-in-class deep drawing (r₉₀ ≥ 1.8, n₉₀ ≥ 0.22, non-aging) — multi-stage draws, hemming and stretch forming succeed without intermediate annealing; watch low dent resistance and springback-free but low-strength parts.
What surface finishes work on DC06?
Takes phosphating, e-coat and powder paint readily; bare sheet must be oiled or coated immediately as it rusts fast; electro- or hot-dip zinc plus e-coat is the standard automotive system.
DC06 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Cultra-low carbon (IF) | ≤ 0.02 | 0 |
| Mn | ≤ 0.25 | 0.15 |
| P | ≤ 0.02 | 0.01 |
| S | ≤ 0.02 | 0.01 |
| Tistabilizer for C and N; Nb may partly substitute in Ti-Nb IF variants | ≤ 0.3 | 0.06 |
| Alkilled steel, typical mill practice | 0.02 – 0.08 | 0.04 |
| Ntypical mill practice | ≤ 0.01 | 0 |
| Fe | balance | — |
DC06 +Z — frequently asked
What is DC06 +Z used for?
DC06 +Z is typically used for automotive body panels, complex stampings and appliance shells. In short: highest-formability DC grade; non-aging IF steel; class-A panel surface.
What is the yield strength of DC06 +Z?
DC06 +Z has a typical yield strength of 150 MPa (21.8 ksi) and a tensile strength of 300 MPa (43.5 ksi) — weaker than 100% of steel grades. Strength varies by condition: see the 5 listed tempers.
Is DC06 +Z easy to machine?
Not especially — machinability is rated fair (40/100, worse than 77% of steel grades). Very soft and gummy — use sharp positive-rake tools, high speed and flood coolant to avoid burrs and built-up edge; blanking and laser cutting are preferred over milling.
Can DC06 +Z be welded?
Yes — weldability is rated very good (80/100). Excellent for resistance spot, MAG and laser welding thanks to ultra-low C, P, S; zinc-coated variants need higher electrode force/current and fume extraction.
What surface finishes work on DC06 +Z?
Takes phosphating, e-coat and powder paint readily; bare sheet must be oiled or coated immediately as it rusts fast; electro- or hot-dip zinc plus e-coat is the standard automotive system.
Can DC06 +Z be formed, bent or molded?
Best-in-class deep drawing (r₉₀ ≥ 1.8, n₉₀ ≥ 0.22, non-aging) — multi-stage draws, hemming and stretch forming succeed without intermediate annealing; watch low dent resistance and springback-free but low-strength parts.
What is the maximum service temperature of DC06 +Z?
DC06 +Z is rated for continuous use to about 200°C (392 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between DC06-CR and DC06-LC?
CR is the default condition — standard stock condition: continuous-annealed and skin-passed coil/sheet, non-aging for 6 months, for general deep-drawn body and appliance panels. LC: ordered when the very lowest yield and no roughness imprint are needed; must be formed promptly and can show slight stretcher-strain risk on non-IF grades (IF chemistry makes DC06 essentially non-aging). Yield strength is 150 MPa in CR versus 130 MPa in LC.
Sources
- EN 10130 — Cold rolled low carbon steel flat products for cold forming — CEN (2006)
- EN 10152 — Electrolytically zinc coated cold rolled steel flat products — CEN (2017)
- EN 10346 — Continuously hot-dip coated steel flat products — CEN (2015)
- ASM Handbook Vol.1 — Properties and Selection: Irons, Steels — ASM International (1990)
- ASM Handbook Vol.14B — Metalworking: Sheet Forming — ASM International (2006)
- Cold rolled IF / extra-deep-drawing steel grade sheets — ArcelorMittal / thyssenkrupp / Baosteel (2023)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.