Steel DC03 vs DC06
Steel · grade comparison
Steel DC03 and DC06 are both steel grades. DC03 is the stronger of the two: yield strength 195 MPa (28.3 ksi) against 150 MPa (21.8 ksi) for DC06, about 30% more. DC03 is harder — 95 HB against 88 HB for DC06 — which matters for wear surfaces and threads. DC03 runs hotter in service (350°C vs 250°C continuous) and DC06 conducts electricity better (13 % IACS vs 11 % IACS). On the shop floor, DC06 forms better (99 vs 88 out of 100).
DC03Choose it when strength drives the design, or when surface hardness matters.
DC03 vs DC06: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Fatigue Strength (Endurance Limit) 145 MPa21 ksi
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 247 J/g106 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Weldability 95 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Specific Stiffness (E / density) 26.8 MN·m/kg · Thermal Shock Resistance Index 7
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | DC03 | DC06 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
DC03 vs DC06 — frequently asked
Is DC03 stronger than DC06?
Yes. DC03 has a typical yield strength of 195 MPa (28.3 ksi) against 150 MPa (21.8 ksi) for DC06 — about 30% more. Tensile strength is 310 MPa (45 ksi) vs 300 MPa (43.5 ksi).
Which is cheaper, DC03 or DC06?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, DC03 or DC06?
DC03, by a small margin. Both rate fair for machinability — 50/100 against 45/100 for DC06.
Ready to make it?
Upload a CAD file and FabDigit prices the part in DC03 and DC06 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.