Nickel Alloy ERNiCr-3 CD-SPOOL
Supply condition
UNS N06082 · ASTM A5.14 ERNiCr-3 · also Inconel Filler Metal 82, Filler Metal 82
As-drawn/temper-drawn layer-wound wire for GMAW and mechanized welding; the higher wire strength is for feedability/column strength, not for joint design.
Values for the CD-SPOOL condition
Other ERNiCr-3 tempers and conditions
ERNiCr-3 is listed in 4 conditions; see the grade overview at ERNiCr-3.
Compare all 4 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Solution annealed weld metal / annealed cut-length rod | Condition of straight-length GTAW rod as supplied and of weld metal given a full solution anneal (~1010–1100 °C) — softest, most ductile state. | 320 | 590 | 45 | 160 HB | 1.6 % IACS |
As Welded + PWHT | Pick when the joint must follow the base-metal PWHT cycle (e.g. Alloy 600 to low-alloy steel); slight strength drop, ductility retained. | 370 | 600 | 40 | 170 HB | 1.6 % IACS |
AWDefault As-welded deposit | Default reported condition: undiluted all-weld-metal properties per AWS A5.14 qualification, used for design of as-welded joints and overlays. | 400 | 620 | 38 | 180 HB | 1.6 % IACS |
CD-SPOOLThis page Cold drawn spooled wire (MIG/MAG, hard temper) | As-drawn/temper-drawn layer-wound wire for GMAW and mechanized welding; the higher wire strength is for feedability/column strength, not for joint design. | 700 | 830 | 20 | 24 HRC | 1.5 % IACS |
What is ERNiCr-3 CD-SPOOL?
ERNiCr-3 CD-SPOOL is ERNiCr-3 supplied in the CD-SPOOL condition — as-drawn/temper-drawn layer-wound wire for GMAW and mechanized welding; the higher wire strength is for feedability/column strength, not for joint design. ERNiCr-3 CD-SPOOL has a yield strength of 700 MPa (102 ksi) and a tensile strength of 830 MPa (120 ksi) — stronger than 81% of nickel alloy grades. Elongation at break is 20% and the elastic modulus is 205 GPa (29.7 Msi). ERNiCr-3 CD-SPOOL has a density of 8.3 g/cm³ (0.3 lb/in³), lighter than 52% of nickel alloy grades. It melts at 1,354°C (2,469 °F). AW is the default condition FabDigit quotes; CD-SPOOL is available on request or by drawing note.
Advantages
- Readily welded — 92/100, better than 98% of nickel alloy grades
- High strength — 700 MPa (102 ksi), better than 81% of nickel alloy grades
Limitations
- Limited service temperature — 400°C (752 °F), worse than 94% of nickel alloy grades
- Limited ductility — 20%, worse than 76% of nickel alloy grades
ERNiCr-3 CD-SPOOL properties
Typical room-temperature values for ERNiCr-3 CD-SPOOL; 23 are specific to this condition. Other listed values are ERNiCr-3 reference data and may not represent this condition. Bars are the position among nickel alloy grades.
Physical3
ERNiCr-3 CD-SPOOL has a density of 8.3 g/cm³ (0.3 lb/in³), lighter than 52% of nickel alloy grades. It melts at 1,354°C (2,469 °F).
Mechanical16
ERNiCr-3 CD-SPOOL has a yield strength of 700 MPa (102 ksi) and a tensile strength of 830 MPa (120 ksi) — stronger than 81% of nickel alloy grades. Elongation at break is 20% and the elastic modulus is 205 GPa (29.7 Msi).
Thermal6
ERNiCr-3 CD-SPOOL is rated for continuous service to 400°C (752 °F). It conducts heat at 12 W/m·K (6.93 BTU/hr·ft·°F), better than 65% of nickel alloy grades. Thermal expansion is 13.5 µm/m·K (7.5 µin/in·°F).
Electrical3
ERNiCr-3 CD-SPOOL conducts electricity at 1.5 % IACS, better than 59% of nickel alloy grades.
Chemical & Environmental3
Corrosion resistance is very good (74/100), worse than 66% of nickel alloy grades.
Sustainability4
Producing a kilogram of ERNiCr-3 CD-SPOOL takes about 160 MJ of energy and emits 12.5 kg of CO₂ — less than 53% of nickel alloy grades. Typical recycled content is 30%.
Manufacturability7
ERNiCr-3 CD-SPOOL's machinability is poor (20/100, better than 53% of nickel alloy grades); weldability excellent (92/100); formability fair (35/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with ERNiCr-3 CD-SPOOL
Is ERNiCr-3 easy to machine?
Weld deposits work-harden fast and are gummy: use rigid setups, positive-rake carbide, low speed / heavy feed and flood coolant; grinding of overlays needs soft aluminum-oxide wheels.
Can ERNiCr-3 be welded?
Designed as filler: GTAW/GMAW/PAW/SAW with Ar or Ar-He shielding, stringer beads, interpass ≤150 °C, no preheat needed on nickel base metals; keep dilution from carbon steel low to avoid Fe pickup.
Can ERNiCr-3 be formed, bent or molded?
Supplied as drawn wire — cold drawing and coiling only; re-straightened rod bends easily in the annealed state but work-hardens rapidly.
What surface finishes work on ERNiCr-3?
Remove all oxide/heat tint by pickling, stainless wire brushing or grinding before further passes or service; electropolish or passivate for nuclear/clean-service cleanliness; not anodizable.
ERNiCr-3 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| C | ≤ 0.1 | 0.03 |
| Cr | 18 – 22 | 20 |
| Mnhot-crack resistance | 2.5 – 3.5 | 3 |
| Fe | ≤ 3 | 1.5 |
| Nb+Tacarbide stabilization | 2 – 3 | 2.5 |
| Ti | ≤ 0.75 | 0.35 |
| Si | ≤ 0.5 | 0.15 |
| Cu | ≤ 0.5 | 0.05 |
| S | ≤ 0.02 | 0 |
| P | ≤ 0.03 | 0.01 |
| Nibalance, 67 % min per AWS A5.14 | ≥ 67 (balance) | — |
ERNiCr-3 CD-SPOOL — frequently asked
What is ERNiCr-3 CD-SPOOL used for?
ERNiCr-3 CD-SPOOL is typically used for nuclear dissimilar metal welding, alloy 600/690 pipe welding and root pass welding before covered electrode fill. In short: bare-wire partner to 182; service to 815 °C; standard nuclear root filler.
What is the yield strength of ERNiCr-3 CD-SPOOL?
ERNiCr-3 CD-SPOOL has a typical yield strength of 700 MPa (102 ksi) and a tensile strength of 830 MPa (120 ksi) — stronger than 81% of nickel alloy grades. Strength varies by condition: see the 4 listed tempers.
Is ERNiCr-3 CD-SPOOL easy to machine?
Not especially — machinability is rated poor (20/100, better than 53% of nickel alloy grades). Weld deposits work-harden fast and are gummy: use rigid setups, positive-rake carbide, low speed / heavy feed and flood coolant; grinding of overlays needs soft aluminum-oxide wheels.
Can ERNiCr-3 CD-SPOOL be welded?
Yes — weldability is rated excellent (92/100). Designed as filler: GTAW/GMAW/PAW/SAW with Ar or Ar-He shielding, stringer beads, interpass ≤150 °C, no preheat needed on nickel base metals; keep dilution from carbon steel low to avoid Fe pickup.
What surface finishes work on ERNiCr-3 CD-SPOOL?
Remove all oxide/heat tint by pickling, stainless wire brushing or grinding before further passes or service; electropolish or passivate for nuclear/clean-service cleanliness; not anodizable.
Can ERNiCr-3 CD-SPOOL be formed, bent or molded?
Supplied as drawn wire — cold drawing and coiling only; re-straightened rod bends easily in the annealed state but work-hardens rapidly.
What is the maximum service temperature of ERNiCr-3 CD-SPOOL?
ERNiCr-3 CD-SPOOL is rated for continuous use to about 400°C (752 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between ERNiCr-3-AW and ERNiCr-3 SOL-ANN?
AW is the default condition — default reported condition: undiluted all-weld-metal properties per AWS A5.14 qualification, used for design of as-welded joints and overlays. SOL-ANN: condition of straight-length GTAW rod as supplied and of weld metal given a full solution anneal (~1010–1100 °C) — softest, most ductile state. Yield strength is 400 MPa in AW versus 320 MPa in SOL-ANN.
Sources
- AWS A5.14/A5.14M — Nickel and Nickel-Alloy Bare Welding Electrodes and Rods — AWS (2018)
- ASME BPVC Section II Part C, SFA-5.14 — ASME (2023)
- INCONEL Filler Metal 82 — Special Metals Corporation (2020)
- Nickel alloy welding consumables — Alloy 82 (ERNiCr-3) — Böhler Welding / voestalpine (2022)
- ASM Handbook Vol.6 — Welding, Brazing and Soldering (nickel alloys) — ASM International (1993)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.