Steel 30CrMnSiNi2A CD+A
Supply condition
EN 30CrMnSiNi2A
CD+A = cold drawn + annealed bar
Small-diameter precision bar for fasteners and pins, machined then heat treated to final strength.
Values for the CD+A condition
Other 30CrMnSiNi2A tempers and conditions
30CrMnSiNi2A is listed in 10 conditions; see the grade overview at 30CrMnSiNi2A.
Compare all 10 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
(mill delivery condition for bar/forging stock) | Soft delivery condition for machining, cold straightening and forging stock before final quench and temper. | 560 | 800 | 18 | 217 HB | — |
CD+AThis page Cold drawn + annealed bar | Small-diameter precision bar for fasteners and pins, machined then heat treated to final strength. | 720 | 900 | 12 | 25 HRC | 6.4 % IACS |
Normalized + high-temperature temper | Alternative pre-machining condition giving a uniform sorbitic structure and better machined surface than full anneal. | 750 | 950 | 16 | 27 HRC | 6.4 % IACS |
Q&T 500–550 °C | Use when maximum toughness, machinability and reduced SCC/hydrogen sensitivity matter more than peak strength. | 1,150 | 1,280 | 15 | 39 HRC | — |
Isothermal quench (austemper, lower bainite) | Choose for complex thin-section forgings where distortion and quench cracking must be minimised and impact toughness maximised. | 1,300 | 1,550 | 14 | 45 HRC | — |
Q&T 400 °C | Listed for reference only — tempering near 350–450 °C causes a sharp drop in impact energy and should be avoided. | 1,350 | 1,500 | 12 | 44 HRC | 5.9 % IACS |
Q&T 300 °C | Slightly lower strength with improved toughness and hot-strength retention; upper limit before temper embrittlement. | 1,400 | 1,630 | 13 | 46 HRC | — |
QT260Default Q&T 260 °C | Standard aerospace condition — best balance of 1620–1800 MPa strength, ductility and K_IC for landing gear and structural fittings. | 1,450 | 1,700 | 12 | 48 HRC | — |
As-quenched (untempered martensite) | Intermediate condition only — never used in service because untempered martensite is brittle and quench-crack prone. | 1,550 | 2,000 | 5 | 54 HRC | 4.5 % IACS |
Q&T 200 °C | Maximum-strength condition for short-life or stiffness-critical parts where toughness and SCC resistance are less critical. | 1,550 | 1,820 | 10 | 51 HRC | — |
What is 30CrMnSiNi2A CD+A?
30CrMnSiNi2A CD+A is 30CrMnSiNi2A supplied in the CD+A condition — small-diameter precision bar for fasteners and pins, machined then heat treated to final strength. 30CrMnSiNi2A CD+A has a yield strength of 720 MPa (104 ksi) and a tensile strength of 900 MPa (131 ksi) — stronger than 82% of steel grades. Elongation at break is 12% and the elastic modulus is 200 GPa (29 Msi). 30CrMnSiNi2A CD+A has a density of 7.8 g/cm³ (0.282 lb/in³), lighter than 87% of steel grades. It melts at 1,420°C (2,588 °F). QT260 is the default condition FabDigit quotes; CD+A is available on request or by drawing note.
Advantages
- Polishes to a fine finish — 70/100, better than 87% of steel grades
- High strength — 720 MPa (104 ksi), better than 82% of steel grades
Limitations
- Limited ductility — 12%, worse than 84% of steel grades
- High embodied carbon — 2.5 kg CO₂/kg, worse than 82% of steel grades
- Low electrical conductivity — 6.4 % IACS, worse than 77% of steel grades
30CrMnSiNi2A CD+A properties
Typical room-temperature values for 30CrMnSiNi2A CD+A; 22 are specific to this condition. Other listed values are 30CrMnSiNi2A reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
30CrMnSiNi2A CD+A has a density of 7.8 g/cm³ (0.282 lb/in³), lighter than 87% of steel grades. It melts at 1,420°C (2,588 °F).
Mechanical15
30CrMnSiNi2A CD+A has a yield strength of 720 MPa (104 ksi) and a tensile strength of 900 MPa (131 ksi) — stronger than 82% of steel grades. Elongation at break is 12% and the elastic modulus is 200 GPa (29 Msi).
Thermal6
30CrMnSiNi2A CD+A is rated for continuous service to 350°C (662 °F). It conducts heat at 36 W/m·K (20.8 BTU/hr·ft·°F), worse than 73% of steel grades. Thermal expansion is 11.5 µm/m·K (6.39 µin/in·°F).
Electrical3
30CrMnSiNi2A CD+A conducts electricity at 6.4 % IACS, worse than 77% of steel grades.
Chemical & Environmental3
Corrosion resistance is not recommended (12/100), worse than 53% of steel grades.
Sustainability4
Producing a kilogram of 30CrMnSiNi2A CD+A takes about 34 MJ of energy and emits 2.5 kg of CO₂ — more than 82% of steel grades. Typical recycled content is 20%.
Manufacturability7
30CrMnSiNi2A CD+A's machinability is fair (45/100, worse than 65% of steel grades); weldability poor (32/100); formability poor (25/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with 30CrMnSiNi2A CD+A
Is 30CrMnSiNi2A easy to machine?
Rough-machine in the annealed condition (HB ≤229); finish cuts on hardened 48 HRC material need rigid setups, coated carbide or CBN, low feeds and generous coolant, leaving stock for grinding.
Can 30CrMnSiNi2A be welded?
Poor weldability — if unavoidable use TIG/EB with matching or low-hydrogen filler, 250–350 °C preheat, and re-quench-and-temper the whole part; never weld in the final heat-treated state.
Can 30CrMnSiNi2A be formed, bent or molded?
Hot forge 1150→900 °C with slow post-forge cooling and immediate anneal; cold forming is limited to gentle straightening in the annealed state.
What surface finishes work on 30CrMnSiNi2A?
Shot-peen highly stressed fillets, then cadmium, Zn-Ni or IVD aluminium plate plus primer; bake 190–200 °C for 8–24 h after plating or acid pickling to relieve hydrogen, and avoid grinding burns.
30CrMnSiNi2A chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| C | 0.27 – 0.34 | 0.3 |
| Siraises tempering resistance | 0.9 – 1.2 | 1.05 |
| Mn | 1 – 1.3 | 1.15 |
| Cr | 0.9 – 1.2 | 1.05 |
| Nitoughness and hardenability | 1.4 – 1.8 | 1.6 |
| Curesidual | ≤ 0.2 | — |
| Saerospace melt practice, often ≤0.008 | ≤ 0.01 | — |
| P | ≤ 0.02 | — |
| Fe | balance | — |
30CrMnSiNi2A CD+A — frequently asked
What is 30CrMnSiNi2A CD+A used for?
30CrMnSiNi2A CD+A is typically used for landing gear, aircraft structural forgings and high-strength shafts. In short: 300M-class strength level; silicon-modified temper resistance; landing gear workhorse grade.
What is the yield strength of 30CrMnSiNi2A CD+A?
30CrMnSiNi2A CD+A has a typical yield strength of 720 MPa (104 ksi) and a tensile strength of 900 MPa (131 ksi) — stronger than 82% of steel grades. Strength varies by condition: see the 10 listed tempers.
Is 30CrMnSiNi2A CD+A easy to machine?
Reasonably — machinability is rated fair (45/100, worse than 65% of steel grades). Rough-machine in the annealed condition (HB ≤229); finish cuts on hardened 48 HRC material need rigid setups, coated carbide or CBN, low feeds and generous coolant, leaving stock for grinding.
Can 30CrMnSiNi2A CD+A be welded?
Not readily — weldability is rated poor (32/100). Poor weldability — if unavoidable use TIG/EB with matching or low-hydrogen filler, 250–350 °C preheat, and re-quench-and-temper the whole part; never weld in the final heat-treated state.
What surface finishes work on 30CrMnSiNi2A CD+A?
Shot-peen highly stressed fillets, then cadmium, Zn-Ni or IVD aluminium plate plus primer; bake 190–200 °C for 8–24 h after plating or acid pickling to relieve hydrogen, and avoid grinding burns.
Can 30CrMnSiNi2A CD+A be formed, bent or molded?
Hot forge 1150→900 °C with slow post-forge cooling and immediate anneal; cold forming is limited to gentle straightening in the annealed state.
What is the maximum service temperature of 30CrMnSiNi2A CD+A?
30CrMnSiNi2A CD+A is rated for continuous use to about 350°C (662 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between 30CrMnSiNi2A-QT260 and 30CrMnSiNi2A-QT520?
QT260 is the default condition — standard aerospace condition — best balance of 1620–1800 MPa strength, ductility and K_IC for landing gear and structural fittings. QT520: use when maximum toughness, machinability and reduced SCC/hydrogen sensitivity matter more than peak strength. Yield strength is 1,450 MPa in QT260 versus 1,150 MPa in QT520.
Sources
- GJB / (30CrMnSiNi2A) (1994)
- ASM Handbook Vol.1: Properties and Selection — Irons, Steels, and High-Performance Alloys — ASM International (1990)
- MMPDS-17 (300M / AMS 6417 comparison data) — Battelle (2022)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.