Steel 1008-DDS (DDS/DDQ)
Grade
AISI/SAE 1008 · UNS G10080 · also CRCA, CRS
Aluminium-killed, non-ageing deep-draw sheet for severe stamping and drawn shells where CS cracks or shows stretcher strain.
Values for the DDS condition
Other 1008 tempers and conditions
1008 is listed in 8 conditions; see the grade overview at 1008.
Compare all 8 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
full/subcritical anneal (softest condition) | Pick for maximum ductility before severe forming, or to relieve cold-work after drawing; lowest strength and hardness. | 170 | 295 | 40 | 85 HB | 12 % IACS |
HRDefault Hot rolled | Cheapest form, mill scale surface and looser thickness tolerance; use for weldments, brackets and parts that will be painted or machined. | 175 | 300 | 30 | 86 HB | — |
DDSThis page DDS/DDQ | Aluminium-killed, non-ageing deep-draw sheet for severe stamping and drawn shells where CS cracks or shows stretcher strain. | 175 | 300 | 42 | 82 HB | 12 % IACS |
Hot Rolled, Pickled and Oiled | Hot-rolled properties with scale removed and an oil film — pick when a hot-rolled price with a paint-ready or laser-friendly surface is wanted. | 185 | 305 | 32 | 88 HB | 11.5 % IACS |
austenitized ~900 °C, air cooled | Used after hot working, welding or forging to give a uniform fine-grain ferrite/pearlite structure and consistent properties. | 195 | 325 | 33 | 90 HB | 11.5 % IACS |
Cold rolled | Default stock condition: cold-rolled, box- or continuous-annealed and temper-rolled sheet for brackets, enclosures, chassis and general fabrication (16–24 GA). | 210 | 330 | 36 | 95 HB | — |
Cold drawn | Cold-drawn bar, wire and welded-tube stock: higher strength, bright surface and tight size, at the cost of ductility and residual stress. | 285 | 340 | 20 | 95 HB | — |
CR Full Hard | Heavily work-hardened cold-rolled coil for flat, stiff, non-formed parts (shims, panels, strapping); bends will crack. | 500 | 550 | 3 | 8 HRC | 11 % IACS |
What is 1008-DDS?
1008-DDS is 1008 in the DDS grade — aluminium-killed, non-ageing deep-draw sheet for severe stamping and drawn shells where CS cracks or shows stretcher strain. 1008-DDS has a yield strength of 175 MPa (25.4 ksi) and a tensile strength of 300 MPa (43.5 ksi) — weaker than 99% of steel grades. Elongation at break is 42% and the elastic modulus is 200 GPa (29 Msi). 1008-DDS has a density of 7.87 g/cm³ (0.284 lb/in³), heavier than 92% of steel grades. It melts at 1,495°C (2,723 °F). HR is the default condition FabDigit quotes; DDS is available on request or by drawing note.
Advantages
- Ductile — tolerates forming and impact — 42%, better than 100% of steel grades
- Conducts heat well — 61 W/m·K (35.2 BTU/hr·ft·°F), better than 100% of steel grades
- Readily welded — 97/100, better than 100% of steel grades
- Forms and bends easily — 98/100, better than 100% of steel grades
- High electrical conductivity — 12 % IACS, better than 99% of steel grades
Limitations
- Low strength — 175 MPa (25.4 ksi), worse than 99% of steel grades
- Difficult to machine — 40/100, worse than 77% of steel grades
1008-DDS properties
Typical room-temperature values for 1008-DDS; 21 are specific to this condition. Other listed values are 1008 reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
1008-DDS has a density of 7.87 g/cm³ (0.284 lb/in³), heavier than 92% of steel grades. It melts at 1,495°C (2,723 °F).
Mechanical13
1008-DDS has a yield strength of 175 MPa (25.4 ksi) and a tensile strength of 300 MPa (43.5 ksi) — weaker than 99% of steel grades. Elongation at break is 42% and the elastic modulus is 200 GPa (29 Msi).
Thermal6
1008-DDS is rated for continuous service to 425°C (797 °F). It conducts heat at 61 W/m·K (35.2 BTU/hr·ft·°F), better than 100% of steel grades. Thermal expansion is 12.2 µm/m·K (6.78 µin/in·°F).
Electrical3
1008-DDS conducts electricity at 12 % IACS, better than 99% of steel grades.
Chemical & Environmental3
Corrosion resistance is not recommended (10/100), worse than 86% of steel grades.
Sustainability4
Producing a kilogram of 1008-DDS takes about 25 MJ of energy and emits 1.9 kg of CO₂ — less than 82% of steel grades. Typical recycled content is 25%.
Manufacturability7
1008-DDS's machinability is fair (40/100, worse than 77% of steel grades); weldability excellent (97/100); formability excellent (98/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with 1008-DDS
Is 1008 easy to machine?
Soft and gummy: use sharp positive-rake tools, high speed, generous coolant and chip breakers to avoid built-up edge and torn threads; expect ~55 % of 1212 and poor surface finish unless carburized or re-drawn.
Can 1008 be welded?
Excellent for all processes (RSW, MIG, TIG, laser, oxy-fuel) with no preheat or PWHT needed at any practical thickness; grind mill scale and remove zinc coating locally on galvanized stock.
Can 1008 be formed, bent or molded?
Best-in-class cold forming: bends to 0–1 t inside radius, deep drawing and roll forming; specify DDS/DDQ Al-killed for severe draws to avoid stretcher strain and ageing.
What surface finishes work on 1008?
Must be protected — iron/zinc phosphate + powder coat, e-coat, zinc or nickel plating, hot-dip galvanizing or black oxide; bare surfaces flash-rust within hours of degreasing.
1008 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| CSAE J403; sheet grades typically 0.02–0.08 | ≤ 0.1 | 0.06 |
| Mn0.30–0.50 for bar/wire per SAE J403; 0.50 max for sheet | ≤ 0.5 | 0.35 |
| P | ≤ 0.03 | 0.01 |
| S | ≤ 0.04 | 0.02 |
| Sinot specified in SAE J403; typical residual for Al-killed/rimmed sheet | ≤ 0.1 | 0.03 |
| Aldeliberate addition in Al-killed (DDS) sheet only | ≤ 0.1 | 0.04 |
| Fe | balance | — |
1008-DDS — frequently asked
What is 1008-DDS used for?
1008-DDS is typically used for stamped covers and enclosure panels, sheet metal brackets, deep-drawn appliance housings, hot-dip galvanized ductwork and roofing sheet, cold-drawn wire and cold-headed fasteners and welded tube. In short: low-cost; easy cold-forming.
What is the yield strength of 1008-DDS?
1008-DDS has a typical yield strength of 175 MPa (25.4 ksi) and a tensile strength of 300 MPa (43.5 ksi) — weaker than 99% of steel grades. Strength varies by condition: see the 8 listed tempers.
Is 1008-DDS easy to machine?
Not especially — machinability is rated fair (40/100, worse than 77% of steel grades). Soft and gummy: use sharp positive-rake tools, high speed, generous coolant and chip breakers to avoid built-up edge and torn threads; expect ~55 % of 1212 and poor surface finish unless carburized or re-drawn.
Can 1008-DDS be welded?
Yes — weldability is rated excellent (97/100). Excellent for all processes (RSW, MIG, TIG, laser, oxy-fuel) with no preheat or PWHT needed at any practical thickness; grind mill scale and remove zinc coating locally on galvanized stock.
What surface finishes work on 1008-DDS?
Must be protected — iron/zinc phosphate + powder coat, e-coat, zinc or nickel plating, hot-dip galvanizing or black oxide; bare surfaces flash-rust within hours of degreasing.
Can 1008-DDS be formed, bent or molded?
Best-in-class cold forming: bends to 0–1 t inside radius, deep drawing and roll forming; specify DDS/DDQ Al-killed for severe draws to avoid stretcher strain and ageing.
What is the maximum service temperature of 1008-DDS?
1008-DDS is rated for continuous use to about 425°C (797 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between 1008-HR and 1008 CR-FH?
HR is the default condition — cheapest form, mill scale surface and looser thickness tolerance; use for weldments, brackets and parts that will be painted or machined. CR-FH: heavily work-hardened cold-rolled coil for flat, stiff, non-formed parts (shims, panels, strapping); bends will crack. Yield strength is 175 MPa in HR versus 500 MPa in CR-FH.
Can FabDigit make parts in 1008-DDS?
Yes — 1008-DDS is available for sheet metal with instant online pricing. Upload a STEP file to get a price and a DFM check.
Sources
- SAE J403 — Chemical Compositions of SAE Carbon Steels — SAE International (2014)
- ASTM A1008/A1008M — Cold-Rolled Carbon Steel Sheet, CS/DS/DDS — ASTM (2021)
- ASTM A1011/A1011M — Hot-Rolled Carbon Steel Sheet and Strip — ASTM (2018)
- ASTM A653/A653M — Zinc-Coated (Galvanized) Steel Sheet — ASTM (2020)
- GB/T 5213 / GB/T 708 — SAC (2019)
- ASM Handbook Vol.1 — Properties and Selection: Irons, Steels — ASM International (1990)
- ASM Handbook Vol.16 — Machining — ASM International (1989)
- worldsteel LCI data for hot- and cold-rolled coil — World Steel Association (2023)
- CRS sheet small-lot pricing — OnlineMetals / Midwest Steel & Aluminum (2026)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.