Steel 1008 vs 1022
Steel · grade comparison
Steel 1008 and 1022 are both steel grades, both low carbon steel. 1022 is the stronger of the two: yield strength 235 MPa (34.1 ksi) against 175 MPa (25.4 ksi) for 1008, about 34% more; tensile strength follows at 425 MPa (61.6 ksi) vs 300 MPa (43.5 ksi). In exchange, 1008 is the more ductile: elongation 30% versus 23% for 1022, and 1022 is harder (121 HB vs 86 HB). 1008 conducts heat better (60 W/m·K vs 51.9 W/m·K). On the shop floor, 1022 machines more easily (good vs fair).
1008Choose it when the part is bent, formed or impact-loaded.
1022Choose it when strength drives the design, or when the part is machined in volume.
1008 vs 1022: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Fracture Toughness (K_IC)
Hardness, Vickers
Same in both: Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.87 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 247 J/g106 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Same in both: Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 1008 | 1022 |
|---|---|---|
| CNC machining | — | Yes |
| Default condition | HR | HR |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| HVOF Coating | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| TiAlN | — | Yes |
| TiB2 | — | Yes |
| TiCN | — | Yes |
| TiN | — | Yes |
| WC/C | — | Yes |
| ZrN | — | Yes |
Both are offered for Sheet metal. They share 22 finishes: Black Oxide, Cerakote, Chrome Plating, Copper Plating, E-Coating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Hot-Dip Galvanizing, Manganese Phosphate, Nickel Plating and 10 more.
1008 vs 1022 — frequently asked
Is 1022 stronger than 1008?
Yes. 1022 has a typical yield strength of 235 MPa (34.1 ksi) against 175 MPa (25.4 ksi) for 1008 — about 34% more. Tensile strength is 425 MPa (61.6 ksi) vs 300 MPa (43.5 ksi).
Which is cheaper, 1008 or 1022?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 1008 or 1022?
1022. Its machinability rates good (58/100) against fair (48/100) for 1008; for welding the order is 1008 first (excellent, 95/100) then 1022 (excellent, 90/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 1008 and 1022 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.