Precious Metal Ag134-AB (As built (as printed))
Print state
EN L-Ag34Sn · GB BAg34CuZnSn
Reference this condition for design checks on real joints: typical lap-shear strength and service temperature for steel or copper joints with a 0.05–0.15 mm brazing gap.
Values for the AB condition
Other Ag134 tempers and conditions
Ag134 is listed in 4 conditions; see the grade overview at Ag134.
Compare all 4 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
ABThis page As built (as printed) | Reference this condition for design checks on real joints: typical lap-shear strength and service temperature for steel or copper joints with a 0.05–0.15 mm brazing gap. | 180 | 350 | 22 | 90 HB | 15 % IACS |
Strip / foil, annealed | Use annealed strip or foil for stamped shims, rings and furnace-brazing interlayers, where 32% elongation eases forming and close contact but yield drops to 200 MPa. | 200 | 380 | 32 | 90 HB | 17 % IACS |
RDefault Bare rod / straight length | Choose the most widely stocked form, bright straight lengths of Ø1.5–3.0 mm × 500 mm, for manual flame brazing with a separately applied borax-fluoride flux. | 250 | 420 | 28 | 100 HB | 16 % IACS |
Hard-drawn wire | Choose spooled hard-drawn wire for automatic wire-feed induction or robotic brazing; cold work raises stiffness and feed stability but cuts elongation to 8%. | 430 | 520 | 8 | 138 HB | 15.5 % IACS |
What is Ag134-AB?
Ag134-AB is Ag134 in the AB condition — reference this condition for design checks on real joints: typical lap-shear strength and service temperature for steel or copper joints with a 0.05–0.15 mm brazing gap. Ag134-AB has a yield strength of 180 MPa (26.1 ksi) and a tensile strength of 350 MPa (50.8 ksi) — weaker than 59% of precious metal grades. Elongation at break is 22% and the elastic modulus is 85 GPa (12.3 Msi). Ag134-AB has a density of 8.8 g/cm³ (0.318 lb/in³), lighter than 94% of precious metal grades. It melts at 630°C (1,166 °F). R is the default condition FabDigit quotes; AB is available on request or by drawing note.
Advantages
- Low embodied carbon — 40 kg CO₂/kg, better than 96% of precious metal grades
- Lightweight — 8.8 g/cm³ (0.318 lb/in³), better than 94% of precious metal grades
- Easy to machine — 55/100, better than 86% of precious metal grades
Limitations
- Limited service temperature — 180°C (356 °F), worse than 100% of precious metal grades
- Difficult to weld — 15/100, worse than 96% of precious metal grades
- Needs corrosion protection — 55/100, worse than 94% of precious metal grades
- Limited formability — 35/100, worse than 92% of precious metal grades
- Hard to polish — 60/100, worse than 92% of precious metal grades
Ag134-AB properties
Typical room-temperature values for Ag134-AB; 17 are specific to this condition. Other listed values are Ag134 reference data and may not represent this condition. Bars are the position among precious metal grades.
Physical3
Ag134-AB has a density of 8.8 g/cm³ (0.318 lb/in³), lighter than 94% of precious metal grades. It melts at 630°C (1,166 °F).
Mechanical13
Ag134-AB has a yield strength of 180 MPa (26.1 ksi) and a tensile strength of 350 MPa (50.8 ksi) — weaker than 59% of precious metal grades. Elongation at break is 22% and the elastic modulus is 85 GPa (12.3 Msi).
Thermal6
Ag134-AB is rated for continuous service to 180°C (356 °F). It conducts heat at 85 W/m·K (49.1 BTU/hr·ft·°F), worse than 53% of precious metal grades. Thermal expansion is 18.5 µm/m·K (10.3 µin/in·°F).
Electrical3
Ag134-AB conducts electricity at 15 % IACS, worse than 65% of precious metal grades.
Chemical & Environmental3
Corrosion resistance is good (55/100), worse than 94% of precious metal grades.
Sustainability4
Producing a kilogram of Ag134-AB takes about 550 MJ of energy and emits 40 kg of CO₂ — less than 94% of precious metal grades. Typical recycled content is 40%.
Manufacturability8
Ag134-AB's machinability is good (55/100, better than 86% of precious metal grades); weldability poor (15/100); formability fair (35/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with Ag134-AB
Is Ag134 easy to machine?
The filler itself is rarely machined; rod is soft and grabs the tool, so use sharp edges with large positive rake and low speed. Dress excess braze metal by filing or grinding rather than turning.
Can Ag134 be welded?
Not a fusion-weld material. Used as a braze filler at 730–800 °C with FH10 / AWS Type 3A borax-fluoride flux and a joint gap of 0.05–0.15 mm; the zinc content makes it unsuitable for vacuum furnace brazing, and local extraction is needed to control zinc fume.
Can Ag134 be formed, bent or molded?
Ductile in the annealed condition: it draws to 0.3 mm diameter wire, rolls to 0.1 mm strip and stamps into preform rings, with intermediate annealing at about 600 °C.
What surface finishes work on Ag134?
Remove residual flux after brazing with hot water or an acid pickle, as fluoride-bearing residues are corrosive. Joints can be polished, nickel plated or silver plated to prevent sulphide tarnish; anodizing is not applicable.
Ag134 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Agnominal 34% silver | 33 – 35 | 34 |
| Cu | 34 – 37 | 36 |
| Snreplaces cadmium; lowers liquidus and improves wetting | 2 – 3 | 2.5 |
| Cdcadmium-free grade, Cd ≤ 0.010% (RoHS/EU limit) | ≤ 0.01 | 0 |
| Pbimpurity limit | ≤ 0.03 | — |
| EN ISO 17672 total impurity limit | ≤ 0.15 | — |
| Znbalance, about 27-28% | balance | — |
Ag134-AB — frequently asked
What is Ag134-AB used for?
Ag134-AB is typically used for copper/brass pipe joints, refrigeration components, electrical/electronics brazing and sheet-metal duct fittings. In short: cadmium-free BAg-7 equivalent; most ductile deposit, 28 %; balanced cost and flow.
What is the yield strength of Ag134-AB?
Ag134-AB has a typical yield strength of 180 MPa (26.1 ksi) and a tensile strength of 350 MPa (50.8 ksi) — weaker than 59% of precious metal grades. Strength varies by condition: see the 4 listed tempers.
Is Ag134-AB easy to machine?
Reasonably — machinability is rated good (55/100, better than 86% of precious metal grades). The filler itself is rarely machined; rod is soft and grabs the tool, so use sharp edges with large positive rake and low speed. Dress excess braze metal by filing or grinding rather than turning.
Can Ag134-AB be welded?
Not readily — weldability is rated poor (15/100). Not a fusion-weld material. Used as a braze filler at 730–800 °C with FH10 / AWS Type 3A borax-fluoride flux and a joint gap of 0.05–0.15 mm; the zinc content makes it unsuitable for vacuum furnace brazing, and local extraction is needed to control zinc fume.
What surface finishes work on Ag134-AB?
Remove residual flux after brazing with hot water or an acid pickle, as fluoride-bearing residues are corrosive. Joints can be polished, nickel plated or silver plated to prevent sulphide tarnish; anodizing is not applicable.
Can Ag134-AB be formed, bent or molded?
Ductile in the annealed condition: it draws to 0.3 mm diameter wire, rolls to 0.1 mm strip and stamps into preform rings, with intermediate annealing at about 600 °C.
What is the maximum service temperature of Ag134-AB?
Ag134-AB is rated for continuous use to about 180°C (356 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between Ag134-R and Ag134 W-HD?
R is the default condition — choose the most widely stocked form, bright straight lengths of Ø1.5–3.0 mm × 500 mm, for manual flame brazing with a separately applied borax-fluoride flux. W-HD: choose spooled hard-drawn wire for automatic wire-feed induction or robotic brazing; cold work raises stiffness and feed stability but cuts elongation to 8%. Yield strength is 250 MPa in R versus 430 MPa in W-HD.
Sources
- EN ISO 17672 Brazing — Filler metals (Ag134) — ISO/CEN (2016)
- AWS A5.8/A5.8M Specification for Filler Metals for Brazing and Braze Welding — AWS (2019)
- GB/T 10046 — SAC (2018)
- ASM Handbook Vol. 6 — Welding, Brazing and Soldering (Silver brazing filler metals) — ASM International (1993)
- Cadmium-free silver brazing alloy datasheets (Ag34Sn class) — Umicore / Lucas-Milhaupt / (2023)