Copper Alloy M2
M2 is the Russian commercial-grade copper (minimum 99.70 % Cu), one purity step below M1 in the wrought pure-copper family and cross-referenced to C11000.
Reference datasheet — M2 is not in the instant-quote catalog. Upload your part and an engineer will quote it in this grade or suggest the closest stocked equivalent.
Values for the M condition
M2 tempers and conditions
M2 is supplied in 4 conditions, soft to hard. M is the default FabDigit quotes; the values on this page are for it.
Compare all 4 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
MDefault Thermomechanically controlled processed | Pick for deep drawing, bending, gaskets and flexible conductors where maximum ductility and conductivity matter. | 70 | 220 | 45 | 45 HB | 97 % IACS |
М2р | Choose when the part must be welded or brazed in reducing atmosphere — residual P removes oxygen and prevents hydrogen embrittlement, at the cost of conductivity. | 70 | 220 | 42 | 45 HB | 85 % IACS |
М2П | Compromise temper for busbars, terminals and stamped parts that need some stiffness but still moderate bending ability. | 240 | 300 | 14 | 85 HB | 96 % IACS |
М2Т | Pick for hard-drawn wire, rods, rigid busbars and contact parts needing highest strength and straightness. | 320 | 370 | 6 | 100 HB | 95 % IACS |
Supply forms, finishes and certifications
Ways M2 is supplied — form, process route, surface or paperwork — without a datasheet of their own. The property values above apply.
| Option | What it is | Type |
|---|---|---|
PRESSED | Hot extruded / hot rolled | Surface finish |
What is M2?
M2 is the Russian commercial-grade copper (minimum 99.70 % Cu), one purity step below M1 in the wrought pure-copper family and cross-referenced to C11000. It is used for non-critical electrical and mechanical parts and general sheet fabrication, with 97 % IACS electrical conductivity, 388 W/m·K thermal conductivity, 45 % elongation and a 95 formability score in the soft temper. The higher impurity level slightly lowers conductivity and the copper is oxygen-bearing, so fusion welding risks hydrogen embrittlement; use M1 for conductors or the deoxidized M2r variant for welded assemblies. M2 has a density of 8.9 g/cm³ (0.322 lb/in³), heavier than 77% of copper alloy grades. It melts at 1,065°C (1,949 °F). M2 has a yield strength of 70 MPa (10.2 ksi) and a tensile strength of 220 MPa (31.9 ksi) — weaker than 93% of copper alloy grades. Elongation at break is 45% and the elastic modulus is 110 GPa (16 Msi).
What is M2 used for?
- general fittings
- roofing and flashing
- non-critical electrical parts
Advantages
- Conducts heat well — 388 W/m·K (224.2 BTU/hr·ft·°F), better than 95% of copper alloy grades
- Forms and bends easily — 95/100, better than 94% of copper alloy grades
- High electrical conductivity — 97 % IACS, better than 92% of copper alloy grades
- Ductile — tolerates forming and impact — 45%, better than 91% of copper alloy grades
- Tough — resists crack growth — 60 MPa·√m (54.6 ksi·√in), better than 90% of copper alloy grades
Limitations
- Low strength — 70 MPa (10.2 ksi), worse than 93% of copper alloy grades
M2 properties
Typical room-temperature values for M2-M; bars are the position among copper alloy grades.
Physical3
M2 has a density of 8.9 g/cm³ (0.322 lb/in³), heavier than 77% of copper alloy grades. It melts at 1,065°C (1,949 °F).
Mechanical14
M2 has a yield strength of 70 MPa (10.2 ksi) and a tensile strength of 220 MPa (31.9 ksi) — weaker than 93% of copper alloy grades. Elongation at break is 45% and the elastic modulus is 110 GPa (16 Msi).
Thermal6
M2 is rated for continuous service to 200°C (392 °F). It conducts heat at 388 W/m·K (224.2 BTU/hr·ft·°F), better than 95% of copper alloy grades. Thermal expansion is 17 µm/m·K (9.44 µin/in·°F).
Electrical3
M2 conducts electricity at 97 % IACS, better than 92% of copper alloy grades.
Chemical & Environmental3
Corrosion resistance is good (55/100), worse than 86% of copper alloy grades.
Sustainability4
Producing a kilogram of M2 takes about 57 MJ of energy and emits 3.8 kg of CO₂ — less than 52% of copper alloy grades. Typical recycled content is 35%.
Manufacturability8
M2's machinability is poor (30/100, worse than 67% of copper alloy grades); weldability fair (40/100); formability excellent (95/100).
Common Calculations5
Values are nominal handbook figures for design screening. Certified mill or lot data ships with every FabDigit order on request.
Strength versus weight in the copper alloy family
Yield strength against density for every copper alloy grade FabDigit runs. M2 is highlighted; hover a dot for its name, or open the interactive family chart.
Working with M2
Is M2 easy to machine?
Gummy and long-chipping — use sharp positive-rake tools, high speed, low feed and generous coolant; expect ~20 % of AISI 1212 rate, prefer free-cutting brass if heavy machining is needed.
Can M2 be welded?
Oxygen-bearing copper is prone to hydrogen embrittlement and porosity — braze/solder or use GTAW/GMAW with high preheat and deoxidized filler (or specify М2р) rather than gas welding in reducing atmosphere.
Can M2 be formed, bent or molded?
Excellent cold formability in the soft temper (deep drawing, bending, riveting); interanneal at 450–600 °C when total cold reduction exceeds ~60 %.
M2 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Ooxygen-bearing (tough pitch) grade | ≤ 0.07 | 0.04 |
| Bi | ≤ 0 | |
| Sb | ≤ 0.01 | |
| As | ≤ 0.01 | |
| Fe | ≤ 0.05 | |
| Ni | ≤ 0.2 | |
| Pb | ≤ 0.01 | |
| Sn | ≤ 0.05 | |
| Zn | ≤ 0.04 | |
| S | ≤ 0.01 | |
| Pup to ~0.04 residual P in the М2р deoxidized variant | ≤ 0.01 | |
| Total impurities | ≤ 0.3 | |
| CuCu + Ag combined, per GOST 859 | ≥ 99.7 (balance) |
What surface finishes work on M2?
Not anodizable; polishes to a bright finish but tarnishes quickly — protect with benzotriazole lacquer, tin/nickel/silver plating, or allow natural patina outdoors.
Surface treatments FabDigit runs on copper alloy parts — pick them in the quote configurator or call them out on the drawing. Each links to its datasheet in the surface-finish library (thickness, specs, call-out, material verdicts).
Equivalent designations
Standards and trade names that resolve to Copper Alloy M2 in FabDigit's catalog. Equivalence is nominal — check the exact specification when certification matters.
- Similar grades
- C11000
How much does M2 cost?
M2 is a high-cost copper alloy ($$$$), pricier than about 78% of the materials FabDigit quotes. Part price depends far more on geometry, tolerance and quantity than on the raw stock — upload a CAD file for a live quote.
M2 — frequently asked
What is M2 used for?
M2 is typically used for general fittings, roofing and flashing and non-critical electrical parts. In short: commercial-grade CIS copper; lower purity than M1; non-critical electrical use.
What is the yield strength of M2?
M2 has a typical yield strength of 70 MPa (10.2 ksi) and a tensile strength of 220 MPa (31.9 ksi) — weaker than 93% of copper alloy grades. Strength varies by condition: see the 4 listed tempers.
Is M2 easy to machine?
Not especially — machinability is rated poor (30/100, worse than 67% of copper alloy grades). Gummy and long-chipping — use sharp positive-rake tools, high speed, low feed and generous coolant; expect ~20 % of AISI 1212 rate, prefer free-cutting brass if heavy machining is needed.
Can M2 be welded?
With care — weldability is rated fair (40/100). Oxygen-bearing copper is prone to hydrogen embrittlement and porosity — braze/solder or use GTAW/GMAW with high preheat and deoxidized filler (or specify М2р) rather than gas welding in reducing atmosphere.
What surface finishes work on M2?
Not anodizable; polishes to a bright finish but tarnishes quickly — protect with benzotriazole lacquer, tin/nickel/silver plating, or allow natural patina outdoors.
Can M2 be formed, bent or molded?
Excellent cold formability in the soft temper (deep drawing, bending, riveting); interanneal at 450–600 °C when total cold reduction exceeds ~60 %.
What is the maximum service temperature of M2?
M2 is rated for continuous use to about 200°C (392 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between M2-M and M2-T?
M is the default condition — pick for deep drawing, bending, gaskets and flexible conductors where maximum ductility and conductivity matter. T: pick for hard-drawn wire, rods, rigid busbars and contact parts needing highest strength and straightness. Yield strength is 70 MPa in M versus 320 MPa in T.
How much does M2 cost?
M2 is a high-cost copper alloy ($$$$), pricier than about 78% of the materials FabDigit quotes. Part price depends far more on geometry, tolerance and quantity than on the raw stock — upload a CAD file for a live quote.
Sources
- GOST 859-2014 Copper. Grades (М00, М1, М2, М3, М2р…) — Rosstandart (2014)
- GOST 1173 / GOST 495 — copper sheet, strip and foil (tempers М, П, Т) — Rosstandart (2006)
- C11000 Electrolytic Tough Pitch Copper alloy datasheet — Copper Development Association (copper.org) (2023)
- ASM Handbook Vol. 2 — Properties and Selection: Nonferrous Alloys — ASM International (1990)
- ASM Handbook Vol. 13B — Corrosion: Materials (copper alloys) — ASM International (2005)
Property data is compiled from published supplier and standards handbooks and normalised for comparison; hardness values on non-Brinell scales are converted approximately for charting only. Manufacturability limits are FabDigit quote-engine defaults and may be relaxed by engineering review. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.