Steel CQ15-N (Normalized)
Heat-treated state
also CHQ
Used to homogenise grain size and restore toughness after hot forging or heavy welding.
Values for the N condition
Other CQ15 tempers and conditions
CQ15 is listed in 6 conditions; see the grade overview at CQ15.
Compare all 6 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
HRDefault Hot rolled | Cheapest as-supplied condition for structural stampings, weldments and as feedstock for cold drawing. | 190 | 340 | 28 | 101 HB | — |
spheroidize/subcritical annealed CHQ wire and bar | Softest condition, chosen for severe multi-station cold heading and thread rolling of fasteners. | 200 | 330 | 40 | 92 HB | 10.8 % IACS |
NThis page Normalized | Used to homogenise grain size and restore toughness after hot forging or heavy welding. | 200 | 345 | 30 | 100 HB | 10.8 % IACS |
Cold rolled | Pick for clean surface, tight thickness tolerance and deep-drawn or bent stampings. | 210 | 320 | 38 | 95 HB | 10.8 % IACS |
Cold drawn | Cold-work strengthened condition for bright bar, shafts and screws formed with modest deformation. | 360 | 440 | 14 | 126 HB | 10.5 % IACS |
Carburized & quenched (case hardened, ~58-62 HRC case) | Choose when a wear-resistant hard case over a tough low-carbon core is needed (pins, small gears, self-drilling screws). | 480 | 700 | 12 | 60 HRC | 10.5 % IACS |
What is CQ15-N?
CQ15-N is CQ15 heat treated to N — used to homogenise grain size and restore toughness after hot forging or heavy welding. CQ15-N has a yield strength of 200 MPa (29 ksi) and a tensile strength of 345 MPa (50 ksi) — weaker than 98% of steel grades. Elongation at break is 30% and the elastic modulus is 205 GPa (29.7 Msi). CQ15-N has a density of 7.87 g/cm³ (0.284 lb/in³), heavier than 92% of steel grades. It melts at 1,470°C (2,678 °F). HR is the default condition FabDigit quotes; N is available on request or by drawing note.
Advantages
- Forms and bends easily — 88/100, better than 98% of steel grades
- Readily welded — 95/100, better than 97% of steel grades
- Conducts heat well — 51.9 W/m·K (30 BTU/hr·ft·°F), better than 96% of steel grades
- High electrical conductivity — 10.8 % IACS, better than 94% of steel grades
- Ductile — tolerates forming and impact — 30%, better than 93% of steel grades
Limitations
- Low strength — 200 MPa (29 ksi), worse than 98% of steel grades
- Hard to polish — 45/100, worse than 84% of steel grades
CQ15-N properties
Typical room-temperature values for CQ15-N; 22 are specific to this condition. Other listed values are CQ15 reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
CQ15-N has a density of 7.87 g/cm³ (0.284 lb/in³), heavier than 92% of steel grades. It melts at 1,470°C (2,678 °F).
Mechanical13
CQ15-N has a yield strength of 200 MPa (29 ksi) and a tensile strength of 345 MPa (50 ksi) — weaker than 98% of steel grades. Elongation at break is 30% and the elastic modulus is 205 GPa (29.7 Msi).
Thermal6
CQ15-N is rated for continuous service to 400°C (752 °F). It conducts heat at 51.9 W/m·K (30 BTU/hr·ft·°F), better than 96% of steel grades. Thermal expansion is 12 µm/m·K (6.67 µin/in·°F).
Electrical3
CQ15-N conducts electricity at 10.8 % IACS, better than 94% of steel grades.
Chemical & Environmental3
Corrosion resistance is not recommended (10/100), worse than 86% of steel grades.
Sustainability4
Producing a kilogram of CQ15-N takes about 25 MJ of energy and emits 1.9 kg of CO₂ — less than 82% of steel grades. Typical recycled content is 30%.
Manufacturability6
CQ15-N's machinability is good (57/100, better than 71% of steel grades); weldability excellent (95/100); formability excellent (88/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with CQ15-N
Is CQ15 easy to machine?
Soft and gummy — use sharp positive-rake tools, high speed with coolant to avoid built-up edge; cold-drawn condition machines noticeably better than annealed.
Can CQ15 be welded?
Excellent weldability by all arc, resistance and MIG/spot processes with no preheat or PWHT below ~25 mm; remove zinc coating locally and ventilate when welding galvanized material.
Can CQ15 be formed, bent or molded?
Outstanding cold formability — suited to deep drawing, multi-station cold heading and thread rolling; interstage spheroidize annealing recommended for reductions above ~70 %.
What surface finishes work on CQ15?
Not anodizable; protect with hot-dip or electro-galvanizing, zinc-nickel, phosphate + paint or e-coat; rusts within days if stored bare and unoiled.
CQ15 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| C0.15 % nominal; CHQ grades often held to a narrower ±0.02 range | 0.12 – 0.18 | 0.15 |
| Mn | 0.3 – 0.6 | 0.45 |
| Sikept low for cold heading; Si-killed variants up to 0.30 | ≤ 0.1 | 0.05 |
| P | ≤ 0.03 | 0.02 |
| Slow S preferred for CHQ to avoid heading cracks | ≤ 0.04 | 0.02 |
| Alaluminium-killed, fine grain | 0.02 – 0.07 | 0.04 |
| Nlow free N to avoid ageing | ≤ 0.01 | 0.01 |
| Curesidual | ≤ 0.2 | 0.05 |
| Fe | balance | — |
CQ15-N — frequently asked
What is CQ15-N used for?
CQ15-N is typically used for fasteners, bolts and studs. In short: cold-heading low-carbon wire.
What is the yield strength of CQ15-N?
CQ15-N has a typical yield strength of 200 MPa (29 ksi) and a tensile strength of 345 MPa (50 ksi) — weaker than 98% of steel grades. Strength varies by condition: see the 6 listed tempers.
Is CQ15-N easy to machine?
Reasonably — machinability is rated good (57/100, better than 71% of steel grades). Soft and gummy — use sharp positive-rake tools, high speed with coolant to avoid built-up edge; cold-drawn condition machines noticeably better than annealed.
Can CQ15-N be welded?
Yes — weldability is rated excellent (95/100). Excellent weldability by all arc, resistance and MIG/spot processes with no preheat or PWHT below ~25 mm; remove zinc coating locally and ventilate when welding galvanized material.
What surface finishes work on CQ15-N?
Not anodizable; protect with hot-dip or electro-galvanizing, zinc-nickel, phosphate + paint or e-coat; rusts within days if stored bare and unoiled.
Can CQ15-N be formed, bent or molded?
Outstanding cold formability — suited to deep drawing, multi-station cold heading and thread rolling; interstage spheroidize annealing recommended for reductions above ~70 %.
What is the maximum service temperature of CQ15-N?
CQ15-N is rated for continuous use to about 400°C (752 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between CQ15-HR and CQ15-CD?
HR is the default condition — cheapest as-supplied condition for structural stampings, weldments and as feedstock for cold drawing. CD: cold-work strengthened condition for bright bar, shafts and screws formed with modest deformation. Yield strength is 190 MPa in HR versus 360 MPa in CD.
Can FabDigit make parts in CQ15-N?
Yes — CQ15-N is available for CNC machining and sheet metal; every part is priced by an engineer rather than instantly. Upload a STEP file to get a price and a DFM check.
Sources
- ASTM A1011/A1008 (CS Type B hot- and cold-rolled sheet) — ASTM (2018)
- ASTM A510 / SAE J403 (grade 1015 wire rod and bar) — ASTM/SAE (2018)
- GB/T 6478 / GB/T 700 Q195-Q215 — SAC (2015)
- ASM Handbook Vol.1 — Properties and Selection: Irons, Steels — ASM International (1990)
- ASM Handbook Vol.16 — Machining — ASM International (1989)
- Mysteel / 1688 — Mysteel (2025)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.