Nickel Alloy CW2M HIP+SA
Heat-treated state
UNS J26455, N06200 · ASTM A494 CW2M
HIP+SA = hot isostatically pressed then solution annealed
Choose for pressure-containing or fatigue-loaded castings where residual microporosity must be closed (pump casings, valve bodies for severe service).
Values for the HIP+SA condition
Other CW2M tempers and conditions
CW2M is listed in 3 conditions; see the grade overview at CW2M.
Compare all 3 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Spheroidize annealed | Rarely accepted for corrosion duty - interdendritic carbide/mu-phase network lowers ductility and localised-corrosion resistance; used only for non-wetted or trial parts. | 285 | 480 | 22 | 14 HRC | 1.4 % IACS |
SADefault Solution annealed and rapidly quenched | Standard delivery condition for all ASTM A494 CW-2M castings; maximum corrosion resistance and ductility. | 300 | 540 | 45 | 190 HB | — |
HIP+SAThis page Hot isostatically pressed then solution annealed | Choose for pressure-containing or fatigue-loaded castings where residual microporosity must be closed (pump casings, valve bodies for severe service). | 305 | 555 | 50 | 190 HB | 1.4 % IACS |
What is CW2M HIP+SA?
CW2M HIP+SA is CW2M heat treated to HIP+SA — choose for pressure-containing or fatigue-loaded castings where residual microporosity must be closed (pump casings, valve bodies for severe service). CW2M HIP+SA has a yield strength of 305 MPa (44.2 ksi) and a tensile strength of 555 MPa (80.5 ksi) — weaker than 77% of nickel alloy grades. Elongation at break is 50% and the elastic modulus is 202 GPa (29.3 Msi). CW2M HIP+SA has a density of 8.6 g/cm³ (0.311 lb/in³), heavier than 67% of nickel alloy grades. It melts at 1,325°C (2,417 °F). SA is the default condition FabDigit quotes; HIP+SA is available on request or by drawing note.
Advantages
- Polishes to a fine finish — 80/100, better than 97% of nickel alloy grades
- Good corrosion resistance — 93/100, better than 95% of nickel alloy grades
- Ductile — tolerates forming and impact — 50%, better than 88% of nickel alloy grades
Limitations
- Low strength — 305 MPa (44.2 ksi), worse than 77% of nickel alloy grades
CW2M HIP+SA properties
Typical room-temperature values for CW2M HIP+SA; 23 are specific to this condition. Other listed values are CW2M reference data and may not represent this condition. Bars are the position among nickel alloy grades.
Physical3
CW2M HIP+SA has a density of 8.6 g/cm³ (0.311 lb/in³), heavier than 67% of nickel alloy grades. It melts at 1,325°C (2,417 °F).
Mechanical13
CW2M HIP+SA has a yield strength of 305 MPa (44.2 ksi) and a tensile strength of 555 MPa (80.5 ksi) — weaker than 77% of nickel alloy grades. Elongation at break is 50% and the elastic modulus is 202 GPa (29.3 Msi).
Thermal5
CW2M HIP+SA is rated for continuous service to 650°C (1,202 °F). It conducts heat at 10 W/m·K (5.78 BTU/hr·ft·°F), worse than 88% of nickel alloy grades. Thermal expansion is 11.2 µm/m·K (6.22 µin/in·°F).
Electrical3
CW2M HIP+SA conducts electricity at 1.4 % IACS, worse than 65% of nickel alloy grades.
Chemical & Environmental3
Corrosion resistance is excellent (93/100), better than 95% of nickel alloy grades.
Sustainability4
Producing a kilogram of CW2M HIP+SA takes about 175 MJ of energy and emits 14 kg of CO₂ — more than 65% of nickel alloy grades. Typical recycled content is 45%.
Manufacturability8
CW2M HIP+SA's machinability is poor (20/100, better than 53% of nickel alloy grades); weldability very good (78/100); formability poor (25/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with CW2M HIP+SA
Is CW2M easy to machine?
Tough, gummy and strongly work-hardening: use rigid setups, positive-rake carbide or ceramic tooling, low speed with heavy positive feed, flood coolant and never dwell in the cut.
Can CW2M be welded?
Readily GTAW/GMAW welded with matching low-carbon Ni-Cr-Mo filler (ERNiCrMo type); keep interpass temperature low, use low heat input and no preheat; re-solution anneal heavily repaired castings.
Can CW2M be formed, bent or molded?
Supplied as sand or investment castings - design generous fillets and directional solidification with chills/risers to avoid hot tears and interdendritic shrinkage; solution treat and water quench after pouring.
What surface finishes work on CW2M?
Grit blast and pickle/passivate wetted surfaces to remove casting scale and any iron contamination; mechanical polishing improves corrosion behaviour; no anodizing or plating required.
CW2M chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Cr | 15 – 17.5 | 16 |
| Mo | 15 – 17.5 | 16 |
| Fe | ≤ 2 | 1 |
| W | ≤ 1 | 0.3 |
| Clow carbon for as-welded/as-cast corrosion resistance | ≤ 0.02 | 0.01 |
| Si | ≤ 0.8 | 0.5 |
| Mn | ≤ 1 | 0.6 |
| P | ≤ 0.03 | — |
| S | ≤ 0.03 | — |
| Ni | balance | — |
CW2M HIP+SA — frequently asked
What is CW2M HIP+SA used for?
CW2M HIP+SA is typically used for pump casings for mixed acid service, valve trim and flue gas desulfurization components. In short: cast Alloy C-2000; widest acid range cast grade; oxidising and reducing service.
What is the yield strength of CW2M HIP+SA?
CW2M HIP+SA has a typical yield strength of 305 MPa (44.2 ksi) and a tensile strength of 555 MPa (80.5 ksi) — weaker than 77% of nickel alloy grades. Strength varies by condition: see the 3 listed tempers.
Is CW2M HIP+SA easy to machine?
Not especially — machinability is rated poor (20/100, better than 53% of nickel alloy grades). Tough, gummy and strongly work-hardening: use rigid setups, positive-rake carbide or ceramic tooling, low speed with heavy positive feed, flood coolant and never dwell in the cut.
Can CW2M HIP+SA be welded?
Yes — weldability is rated very good (78/100). Readily GTAW/GMAW welded with matching low-carbon Ni-Cr-Mo filler (ERNiCrMo type); keep interpass temperature low, use low heat input and no preheat; re-solution anneal heavily repaired castings.
What surface finishes work on CW2M HIP+SA?
Grit blast and pickle/passivate wetted surfaces to remove casting scale and any iron contamination; mechanical polishing improves corrosion behaviour; no anodizing or plating required.
Can CW2M HIP+SA be formed, bent or molded?
Supplied as sand or investment castings - design generous fillets and directional solidification with chills/risers to avoid hot tears and interdendritic shrinkage; solution treat and water quench after pouring.
What is the maximum service temperature of CW2M HIP+SA?
CW2M HIP+SA is rated for continuous use to about 650°C (1,202 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between CW2M-SA and CW2M-AC?
SA is the default condition — standard delivery condition for all ASTM A494 CW-2M castings; maximum corrosion resistance and ductility. AC: rarely accepted for corrosion duty - interdendritic carbide/mu-phase network lowers ductility and localised-corrosion resistance; used only for non-wetted or trial parts. Yield strength is 300 MPa in SA versus 285 MPa in AC.
Sources
- ASTM A494/A494M - Castings, Nickel and Nickel Alloy — ASTM International (2023)
- ASM Handbook Vol. 2 - Properties and Selection: Nonferrous Alloys and Special-Purpose Materials — ASM International (1990)
- ASM Specialty Handbook: Nickel, Cobalt and Their Alloys — ASM International (2000)
- Ni-Cr-Mo corrosion-resistant alloy technical data (C-type alloys) — Alloy producers/foundries (2022)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.