Stainless Steel CX Stress Relieved
Heat-treated state
also Corrax-like, Corrax
Use to remove build stresses before plate removal; note the hold overlaps the aging window so hardness and strength rise.
Values for the Stress Relieved condition
Other CX tempers and conditions
CX is listed in 6 conditions; see the grade overview at CX.
- HIP
- Solution Annealed
- As Printed
- Stress Relieved
- Aged 560
- Hardened & Tempered
Compare all 6 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Hot isostatic pressed | Choose for fatigue- or pressure-critical parts where residual LPBF porosity must be closed before aging. | 790 | 1,030 | 16 | 34 HRC | 2.2 % IACS |
~850–900 °C, air/gas cooled to soft martensite | Resets the microstructure and homogenises AM texture before aging; softest, most machinable condition. | 800 | 1,050 | 14 | 34 HRC | 2.2 % IACS |
As PrintedDefault as-built LPBF, soft martensitic condition | Pick for parts that will be machined/EDM'd first and aged afterwards; already ~33 HRC with good machinability. | 900 | 1,100 | 11 | 33 HRC | 2.2 % IACS |
Stress RelievedThis page 500–560 °C hold (partially ages the alloy) | Use to remove build stresses before plate removal; note the hold overlaps the aging window so hardness and strength rise. | 1,300 | 1,450 | 8 | 45 HRC | 2.3 % IACS |
Aged 560 °C | Pick when impact toughness and crack resistance matter more than peak hardness (large inserts, shock-loaded tooling). | 1,330 | 1,450 | 8 | 45 HRC | 2.4 % IACS |
aged ~525 °C / 4–6 h, ≈50 HRC | Standard service condition for injection-mould inserts: peak hardness and wear resistance with minimal dimensional change. | 1,550 | 1,670 | 5 | 50 HRC | — |
What is CX Stress Relieved?
CX Stress Relieved is CX heat treated to Stress Relieved — use to remove build stresses before plate removal; note the hold overlaps the aging window so hardness and strength rise. CX Stress Relieved has a yield strength of 1,300 MPa (189 ksi) and a tensile strength of 1,450 MPa (210 ksi) — stronger than 99% of stainless steel grades. Elongation at break is 8% and the elastic modulus is 190 GPa (27.6 Msi). CX Stress Relieved has a density of 7.7 g/cm³ (0.278 lb/in³), lighter than 83% of stainless steel grades. It melts at 1,400°C (2,552 °F). As Printed is the default condition FabDigit quotes; Stress Relieved is available on request or by drawing note.
Advantages
- High strength — 1,300 MPa (189 ksi), better than 99% of stainless steel grades
- Polishes to a fine finish — 85/100, better than 97% of stainless steel grades
Limitations
- Limited ductility — 8%, worse than 99% of stainless steel grades
- High embodied carbon — 6.8 kg CO₂/kg, worse than 95% of stainless steel grades
- Limited formability — 12/100, worse than 93% of stainless steel grades
- Low fracture toughness — 55 MPa·√m (50.1 ksi·√in), worse than 91% of stainless steel grades
- Limited service temperature — 400°C (752 °F), worse than 78% of stainless steel grades
CX Stress Relieved properties
Typical room-temperature values for CX Stress Relieved; 22 are specific to this condition. Other listed values are CX reference data and may not represent this condition. Bars are the position among stainless steel grades.
Physical3
CX Stress Relieved has a density of 7.7 g/cm³ (0.278 lb/in³), lighter than 83% of stainless steel grades. It melts at 1,400°C (2,552 °F).
Mechanical16
CX Stress Relieved has a yield strength of 1,300 MPa (189 ksi) and a tensile strength of 1,450 MPa (210 ksi) — stronger than 99% of stainless steel grades. Elongation at break is 8% and the elastic modulus is 190 GPa (27.6 Msi).
Thermal6
CX Stress Relieved is rated for continuous service to 400°C (752 °F). It conducts heat at 19 W/m·K (11 BTU/hr·ft·°F), better than 73% of stainless steel grades. Thermal expansion is 10.8 µm/m·K (6 µin/in·°F).
Electrical3
CX Stress Relieved conducts electricity at 2.3 % IACS, better than 55% of stainless steel grades.
Chemical & Environmental3
Corrosion resistance is good (58/100), worse than 62% of stainless steel grades.
Sustainability4
Producing a kilogram of CX Stress Relieved takes about 78 MJ of energy and emits 6.8 kg of CO₂ — more than 87% of stainless steel grades. Typical recycled content is 25%.
Manufacturability8
CX Stress Relieved's machinability is poor (30/100, worse than 70% of stainless steel grades); weldability good (55/100); formability not recommended (12/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with CX Stress Relieved
Is CX easy to machine?
Machine in the as-printed or solution-annealed state (~33 HRC) with carbide/coated tools and rigid setups; after aging to 50 HRC switch to hard-milling, grinding or EDM.
Can CX be welded?
Weldable without preheat using matching low-carbon maraging stainless filler or TIG autogenous repair; re-age at 525 °C to restore weld-zone hardness.
Can CX be formed, bent or molded?
LPBF only in practice — print with parameter sets for 12Cr-9Ni-Al, keep build plate warm and stress relieve before plate removal; cold forming of finished parts is not viable.
What surface finishes work on CX?
Takes a mirror polish for optical mould surfaces; passivate after machining, and PVD or nitriding can be applied below the aging temperature to avoid softening.
CX chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Clow carbon, maraging type | ≤ 0.03 | 0.02 |
| Si | 0.1 – 0.5 | 0.3 |
| Mn | 0.1 – 0.5 | 0.3 |
| Crpassivity | 11.5 – 12.5 | 12 |
| Nimartensite + Ni-Al precipitates | 8.5 – 9.5 | 9 |
| Mopitting resistance | 1.2 – 1.6 | 1.4 |
| AlNiAl precipitation hardening | 1.4 – 1.8 | 1.6 |
| Ogas-atomized powder | ≤ 0.05 | 0.03 |
| Fe | balance |
CX Stress Relieved — frequently asked
What is CX Stress Relieved used for?
CX Stress Relieved is typically used for conformally cooled injection mould inserts, mould cores and cavities, optical-grade moulding surfaces, blow and extrusion mould tooling, medical device moulding tools and tooling for corrosive polymers such as PVC. In short: printed corrosion tool steel.
What is the yield strength of CX Stress Relieved?
CX Stress Relieved has a typical yield strength of 1,300 MPa (189 ksi) and a tensile strength of 1,450 MPa (210 ksi) — stronger than 99% of stainless steel grades. Strength varies by condition: see the 6 listed tempers.
Is CX Stress Relieved easy to machine?
Not especially — machinability is rated poor (30/100, worse than 70% of stainless steel grades). Machine in the as-printed or solution-annealed state (~33 HRC) with carbide/coated tools and rigid setups; after aging to 50 HRC switch to hard-milling, grinding or EDM.
Can CX Stress Relieved be welded?
Yes — weldability is rated good (55/100). Weldable without preheat using matching low-carbon maraging stainless filler or TIG autogenous repair; re-age at 525 °C to restore weld-zone hardness.
What surface finishes work on CX Stress Relieved?
Takes a mirror polish for optical mould surfaces; passivate after machining, and PVD or nitriding can be applied below the aging temperature to avoid softening.
Can CX Stress Relieved be formed, bent or molded?
LPBF only in practice — print with parameter sets for 12Cr-9Ni-Al, keep build plate warm and stress relieve before plate removal; cold forming of finished parts is not viable.
What is the maximum service temperature of CX Stress Relieved?
CX Stress Relieved is rated for continuous use to about 400°C (752 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between CX As Printed and CX-HIP?
As Printed is the default condition — pick for parts that will be machined/EDM'd first and aged afterwards; already ~33 HRC with good machinability. HIP: choose for fatigue- or pressure-critical parts where residual LPBF porosity must be closed before aging. Yield strength is 900 MPa in As Printed versus 790 MPa in HIP.
Can FabDigit make parts in CX Stress Relieved?
Yes — CX Stress Relieved is available for 3D printing with instant online pricing. Upload a STEP file to get a price and a DFM check.
Sources
- Uddeholm Corrax — precipitation hardening stainless mould steel — Uddeholm / voestalpine (2020)
- EOS StainlessSteel CX material data sheet — EOS GmbH (2021)
- ASM Handbook Vol.1 — Properties and Selection: Irons, Steels, and High-Performance Alloys — ASM International (1990)
- ASTM F3184 / ASTM F3055-series practice for PBF stainless steels (analogous requirements) — ASTM (2016)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.