Heat Resistant AL · 4xxx
Aluminum 4006
Aluminum 4006 is a heat resistant aluminum — casting and welding stock, good fluidity. Typical values: 90 MPa yield, 2.71 g/cm³, rated to 200 °C. Available for Sheet metal at FabDigit.
Properties
Typical room-temperature values for the default supply condition. Metric first, imperial in gray. The bars show where 4006 sits against the other 163 aluminum grades in the catalog.
Datasheet
| Yield strength | 90 MPa13 ksi |
|---|---|
| Tensile strength | 175 MPa25 ksi |
| Hardness | 50 HB |
| Density | 2.71 g/cm³0.098 lb/in³ |
| Specific strength (yield ÷ density) | 33 |
| Min service temp | -200 °C-328 °F |
| Max service temp | 200 °C392 °F |
| Electrical conductivity | 48 % IACS27.8 MS/m |
| Machinability | Good60 / 100 |
| Weldability | Excellent95 / 100 |
| Formability | Very good80 / 100 |
| ISO 513 machining group | N |
Values are nominal handbook figures for design screening. Certified mill or lot data ships with every FabDigit order on request.
Against other aluminum grades
Strength versus weight in the aluminum family
Yield strength against density for every aluminum grade FabDigit runs. 4006 is highlighted; hover a dot for its name, or open the interactive family chart.
Manufacturability
The process limits FabDigit's quote engine applies to 4006. Design inside these and the part quotes instantly; outside them it routes to an engineer.
Sheet metal
| Formability | Excellent80 / 100 |
|---|---|
| Weldability | Excellent95 / 100 |
Conditions and tempers
How 4006 is supplied and what each state is for. The default is what FabDigit quotes unless your drawing says otherwise.
| Condition | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
O Annealed (O) | Softest — parts you will bend or deep-form; not for carrying load | — | — | — | — |
H14 Strain hardened, half hard (H14) | Mid-stiffness sheet — enclosures and panels with simple bends | — | — | — | — |
H24 Strain hardened, partially annealed (H24) | Bend + stiffness balance — general sheet-metal work | — | — | — | — |
Heat treatment and post-processing
Operations FabDigit's suppliers routinely run on 4006, ranked by how often they make sense for this grade.
Heat treatment
| Age T6 (Aluminum) | Solution + artificial age to peak strength |
|---|---|
| Age T651 (Aluminum) | T6 + stress relief stretch (plate) |
| Full Anneal | Restore ductility; relieve residual stress; coarsen grain |
| Stress Relief | Reduce residual stress without changing structure |
| Age T73 (Aluminum) | Over-age 7000 for SCC resistance |
Post-processing
| Manual Deburr | Deburrstandard |
|---|---|
| Edge Break (0.5mm) | Deburr |
| Glass Bead Blast | Blast |
| Laser Mark | Marking |
| Sand Blast | Blast |
| Vibratory Tumble | Tumble |
| CMM Inspection | Inspection |
| Masking | Masking |
| Tap After Finish | Finish Fix |
| FAI Report | Inspection |
Surface finishes for 4006
Coatings and treatments compatible with aluminum on the processes 4006 runs on. Pick them in the quote configurator or call them out on the drawing.
Passivation
- Electropolishing
Conversion Coating
- Anodizing Type II
- Chem Film (Alodine)
- Hard Anodize Type III w/ PTFE
- Hard Anodizing Type III
Plating
- Electroless Nickel (EN)
- Gold Plating
- Nickel Plating
- Silver Plating
Organic Coating
- Cerakote
- E-Coating
- Epoxy Coating
- Painting
- Powder Coating
- PTFE Coating
PVD Coating
- DLC
Marking / Decoration
- Chemical Etching
- Dot Peen Marking
- Electro-chemical Etching
- Embossing / Debossing
- Ink Stamping
- Laser Marking
- Mechanical Engraving
- Steel Stamping
- Vibro Engraving / Scribing
Equivalent designations
Standards and trade names that resolve to Aluminum 4006 in FabDigit's catalog. Equivalence is nominal — check the exact specification when certification matters.
- Aluminum Association
- AA4006
- EN / DIN / Werkstoff-Nr.
- AW-4006AW 4006
- Other
- AW4006
Stock forms
Raw-material forms FabDigit sources 4006 in.
Property data is compiled from published supplier and standards handbooks and normalised for comparison; hardness values on non-Brinell scales are converted approximately for charting only. Manufacturability limits are FabDigit quote-engine defaults and may be relaxed by engineering review. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.