Copper Alloy C28500-H01
Supply condition
UNS C28500
H01 = quarter hard
Light cold work for better straightness, surface finish and moderate strength in rod and sheet.
Values for the H01 condition
Other C28500 tempers and conditions
C28500 is listed in 8 conditions; see the grade overview at C28500.
Compare all 8 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Soft annealed | Pick for maximum ductility when the part still needs some cold bending or upsetting after annealing. | 115 | 355 | 52 | 58 HB | 28 % IACS |
Annealed | General-purpose annealed condition for plate, sheet and rod that will be formed or machined then finished. | 140 | 370 | 48 | 65 HB | 28 % IACS |
M30Default As hot extruded | The usual stocked form: hot-extruded rod/bar sold as forging blanks and hardware stock. | 145 | 380 | 45 | 70 HB | 28 % IACS |
As hot rolled | Standard mill condition for Muntz-type plate used in marine sheathing, tube sheets and heavy hardware. | 150 | 380 | 45 | 72 HB | 28 % IACS |
As hot forged and air cooled | Condition of finished hot forgings (valve bodies, fittings) taken directly from the die with no post-heat treatment. | 155 | 385 | 40 | 75 HB | 28 % IACS |
H01This page Quarter hard | Light cold work for better straightness, surface finish and moderate strength in rod and sheet. | 275 | 420 | 28 | 105 HB | 27 % IACS |
Half hard | Choose when higher yield strength and wear resistance are needed and only mild bending is required. | 350 | 470 | 18 | 125 HB | 27 % IACS |
Full hard | Maximum strength condition for straight rod, springs-free hardware and wear surfaces; very little remaining ductility. | 410 | 540 | 10 | 150 HB | 26 % IACS |
What is C28500-H01?
C28500-H01 is C28500 supplied in the H01 condition — light cold work for better straightness, surface finish and moderate strength in rod and sheet. C28500-H01 has a yield strength of 275 MPa (39.9 ksi) and a tensile strength of 420 MPa (60.9 ksi) — stronger than 57% of copper alloy grades. Elongation at break is 28% and the elastic modulus is 105 GPa (15.2 Msi). C28500-H01 has a density of 8.39 g/cm³ (0.303 lb/in³), lighter than 76% of copper alloy grades. It melts at 899°C (1,650 °F). M30 is the default condition FabDigit quotes; H01 is available on request or by drawing note.
Advantages
- Low embodied carbon — 3.3 kg CO₂/kg, better than 90% of copper alloy grades
Limitations
- Needs corrosion protection — 43/100, worse than 99% of copper alloy grades
- Limited service temperature — 150°C (302 °F), worse than 96% of copper alloy grades
C28500-H01 properties
Typical room-temperature values for C28500-H01; 20 are specific to this condition. Other listed values are C28500 reference data and may not represent this condition. Bars are the position among copper alloy grades.
Physical3
C28500-H01 has a density of 8.39 g/cm³ (0.303 lb/in³), lighter than 76% of copper alloy grades. It melts at 899°C (1,650 °F).
Mechanical14
C28500-H01 has a yield strength of 275 MPa (39.9 ksi) and a tensile strength of 420 MPa (60.9 ksi) — stronger than 57% of copper alloy grades. Elongation at break is 28% and the elastic modulus is 105 GPa (15.2 Msi).
Thermal6
C28500-H01 is rated for continuous service to 150°C (302 °F). It conducts heat at 121 W/m·K (69.9 BTU/hr·ft·°F), better than 68% of copper alloy grades. Thermal expansion is 20.8 µm/m·K (11.6 µin/in·°F).
Electrical3
C28500-H01 conducts electricity at 27 % IACS, better than 67% of copper alloy grades.
Chemical & Environmental3
Corrosion resistance is fair (43/100), worse than 99% of copper alloy grades.
Sustainability4
Producing a kilogram of C28500-H01 takes about 55 MJ of energy and emits 3.3 kg of CO₂ — less than 72% of copper alloy grades. Typical recycled content is 50%.
Manufacturability8
C28500-H01's machinability is fair (50/100, better than 69% of copper alloy grades); weldability fair (42/100); formability poor (28/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with C28500-H01
Is C28500 easy to machine?
Machines like a duplex brass — roughly 40 % of free-cutting C36000: use sharp positive-rake tools, high speed, light feeds and coolant; the β phase chips well but is gummier than leaded brass.
Can C28500 be welded?
Best joined by brazing or soldering; TIG/MIG with silicon-bronze filler is possible but zinc fuming, porosity and dezincified weld zones require extraction and low heat input.
Can C28500 be formed, bent or molded?
Excellent hot working at 620–780 °C (forge, extrude, hot roll); cold formability is limited — anneal at 425–600 °C between severe cold operations and stress-relieve to avoid SCC.
What surface finishes work on C28500?
Takes a bright mechanical polish and accepts Ni/Cr or decorative plating; not anodizable — protect with lacquer or chemical bronze/black finishes, and stress-relieve before plating to prevent cracking.
C28500 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Cu60/40 Muntz-type range; verify exact limits against the current CDA/ASTM registration for C28500 | 59 – 62 | 60.5 |
| Pbresidual/intentional low lead for hot-working and machining | ≤ 0.3 | 0.1 |
| Fe | ≤ 0.15 | 0.05 |
| Snresidual from scrap | ≤ 0.1 | — |
| Alresidual | ≤ 0.05 | — |
| Znnominally ~40 % | balance | — |
C28500-H01 — frequently asked
What is C28500-H01 used for?
C28500-H01 is typically used for forging blanks, hardware and structural extrusions. In short: hot-forgeable duplex brass; high elongation, 45%; strong hot-worked hardware alloy.
What is the yield strength of C28500-H01?
C28500-H01 has a typical yield strength of 275 MPa (39.9 ksi) and a tensile strength of 420 MPa (60.9 ksi) — stronger than 57% of copper alloy grades. Strength varies by condition: see the 8 listed tempers.
Is C28500-H01 easy to machine?
Reasonably — machinability is rated fair (50/100, better than 69% of copper alloy grades). Machines like a duplex brass — roughly 40 % of free-cutting C36000: use sharp positive-rake tools, high speed, light feeds and coolant; the β phase chips well but is gummier than leaded brass.
Can C28500-H01 be welded?
With care — weldability is rated fair (42/100). Best joined by brazing or soldering; TIG/MIG with silicon-bronze filler is possible but zinc fuming, porosity and dezincified weld zones require extraction and low heat input.
What surface finishes work on C28500-H01?
Takes a bright mechanical polish and accepts Ni/Cr or decorative plating; not anodizable — protect with lacquer or chemical bronze/black finishes, and stress-relieve before plating to prevent cracking.
Can C28500-H01 be formed, bent or molded?
Excellent hot working at 620–780 °C (forge, extrude, hot roll); cold formability is limited — anneal at 425–600 °C between severe cold operations and stress-relieve to avoid SCC.
What is the maximum service temperature of C28500-H01?
C28500-H01 is rated for continuous use to about 150°C (302 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between C28500-M30 and C28500-H04?
M30 is the default condition — the usual stocked form: hot-extruded rod/bar sold as forging blanks and hardware stock. H04: maximum strength condition for straight rod, springs-free hardware and wear surfaces; very little remaining ductility. Yield strength is 145 MPa in M30 versus 410 MPa in H04.
Sources
- ASM Handbook Vol.2 — Properties and Selection: Nonferrous Alloys (Cu–Zn alloys) — ASM International (1990)
- CDA Copper Alloy Database — Muntz metal / 60-40 brass (C28000 family) — Copper Development Association (2023)
- ASTM B124/B124M — Copper and Copper-Alloy Forging Rod, Bar, and Shapes — ASTM (2020)
- ASTM B601 — Temper Designations for Copper and Copper Alloys — ASTM (2019)
- ASM Handbook Vol.13 — Corrosion (dezincification, SCC of brasses) — ASM International (2005)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.