Aluminum A1N00
A1N00 is a JIS-only high-purity commercially pure aluminum of the 1000-series family, at roughly 99.9%+ Al and formulated for electrolytic capacitor foil where etching must be uniform.
Reference datasheet — A1N00 is not in the instant-quote catalog. Upload your part and an engineer will quote it in this grade or suggest the closest stocked equivalent.
Values for the O condition
A1N00 tempers and conditions
A1N00 is supplied in 9 conditions, soft to hard. O is the default FabDigit quotes; the values on this page are for it.
Compare all 9 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
ODefault Annealed | Softest, most formable condition — deep drawing, foil converting and any application needing maximum ductility. | 35 | 90 | 38 | 23 HB | 59 % IACS |
As fabricated | Mill-finish hot-rolled coil or plate with no guaranteed mechanical properties — feedstock for further rolling. | 45 | 95 | 30 | 25 HB | 59 % IACS |
Strain hardened and partially annealed, quarter hard | Same strength class as H12 but with better ductility and flatness from a partial anneal. | 85 | 110 | 16 | 28 HB | 58.5 % IACS |
Strain hardened, quarter hard | Light cold work for slightly higher strength while keeping good bending and forming. | 100 | 110 | 12 | 28 HB | 58.5 % IACS |
Strain hardened and partially annealed, half hard | Half-hard strip with extra bendability — common for stamped, formed and rolled foil products. | 100 | 125 | 12 | 32 HB | 58.5 % IACS |
Strain hardened, half hard | The usual general-purpose sheet temper: workable balance of strength, flatness and bending. | 115 | 125 | 9 | 32 HB | 58.5 % IACS |
Strain hardened and partially annealed, three-quarter hard | Three-quarter-hard strip with improved ductility over H16 for light forming. | 125 | 145 | 8 | 38 HB | 58 % IACS |
Strain hardened, three-quarter hard | Higher strength strip where only gentle forming or flat use is needed. | 140 | 145 | 6 | 38 HB | 58 % IACS |
Strain hardened, full hard | Maximum cold-worked strength; the standard temper for hard foil and capacitor/packaging foil stock. | 150 | 165 | 5 | 44 HB | 57 % IACS |
What is A1N00?
A1N00 is a JIS-only high-purity commercially pure aluminum of the 1000-series family, at roughly 99.9%+ Al and formulated for electrolytic capacitor foil where etching must be uniform. Engineers use it for foil and thin strip in O, F, H12 through H18 and H22 through H26, drawing on 98 formability, 222 W/m-K thermal conductivity and 59% IACS electrical conductivity. Mechanical strength is low at 35 MPa yield, 90 MPa tensile, 23 HB and 38% elongation, machinability is 22, and service is limited to about 200 C. Availability is tied to JIS foil supply; 1188 or 1085 are the nearest equivalents outside that system. A1N00 has a density of 2.71 g/cm³ (0.0979 lb/in³), heavier than 51% of aluminum grades. It melts at 643°C (1,189 °F). A1N00 has a yield strength of 35 MPa (5.08 ksi) and a tensile strength of 90 MPa (13.1 ksi) — weaker than 96% of aluminum grades. Elongation at break is 38% and the elastic modulus is 69 GPa (10 Msi).
What is A1N00 used for?
- Electrolytic capacitor foil
- High-purity electrical foil
- Etched anode and cathode foil stock
- Thin-gauge conductor strip
- Foil laminates and shielding
- Reflective foil sheet
Advantages
- Ductile — tolerates forming and impact — 38%, better than 98% of aluminum grades
- Forms and bends easily — 98/100, better than 98% of aluminum grades
- High electrical conductivity — 59 % IACS, better than 95% of aluminum grades
- Readily welded — 92/100, better than 95% of aluminum grades
- Conducts heat well — 222 W/m·K (128.3 BTU/hr·ft·°F), better than 94% of aluminum grades
Limitations
- Difficult to machine — 22/100, worse than 98% of aluminum grades
- Low strength — 35 MPa (5.08 ksi), worse than 96% of aluminum grades
A1N00 properties
Typical room-temperature values for A1N00-O; bars are the position among aluminum grades.
Physical3
A1N00 has a density of 2.71 g/cm³ (0.0979 lb/in³), heavier than 51% of aluminum grades. It melts at 643°C (1,189 °F).
Mechanical11
A1N00 has a yield strength of 35 MPa (5.08 ksi) and a tensile strength of 90 MPa (13.1 ksi) — weaker than 96% of aluminum grades. Elongation at break is 38% and the elastic modulus is 69 GPa (10 Msi).
Thermal6
A1N00 is rated for continuous service to 200°C (392 °F). It conducts heat at 222 W/m·K (128.3 BTU/hr·ft·°F), better than 94% of aluminum grades. Thermal expansion is 23.6 µm/m·K (13.1 µin/in·°F).
Electrical3
A1N00 conducts electricity at 59 % IACS, better than 95% of aluminum grades.
Chemical & Environmental3
Corrosion resistance is very good (72/100), better than 83% of aluminum grades.
Sustainability4
Producing a kilogram of A1N00 takes about 205 MJ of energy and emits 12.5 kg of CO₂ — more than 76% of aluminum grades. Typical recycled content is 20%.
Manufacturability7
A1N00's machinability is poor (22/100, worse than 98% of aluminum grades); weldability excellent (92/100); formability excellent (98/100).
Common Calculations5
Values are nominal handbook figures for design screening. Certified mill or lot data ships with every FabDigit order on request.
Strength versus weight in the aluminum family
Yield strength against density for every aluminum grade FabDigit runs. A1N00 is highlighted; hover a dot for its name, or open the interactive family chart.
Working with A1N00
Is A1N00 easy to machine?
Very soft and gummy — use polished high-rake carbide, high surface speed, sharp tools and generous lubricant to avoid built-up edge; hard tempers (H18) chip better than O.
Can A1N00 be welded?
Excellent with GTAW/GMAW using ER1100 or ER4043 filler; resistance welding and brazing are also routine, but the weld softens to near-O strength in the HAZ.
Can A1N00 be formed, bent or molded?
Outstanding cold formability in O/H22 — deep draws, spinning, and rolling to sub-10 µm foil; intermediate anneals restore ductility in hard tempers.
A1N00 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Si+Fecombined limit per JIS H 4000 | ≤ 1 | |
| Cu | 0.05 – 0.2 | 0.12 |
| Mn | ≤ 0.05 | |
| MgMg allowance is the main difference from 1100 | ≤ 0.1 | |
| Zn | ≤ 0.1 | |
| Others (each) | ≤ 0.05 | |
| Al99.00 % min by difference | ≥ 99 (balance) |
What surface finishes work on A1N00?
Takes clear/bright anodize, chemical conversion coating, lacquer and printing well; the anodic layer stays thin and soft, so use it for appearance and corrosion rather than wear.
Surface treatments FabDigit runs on aluminum parts — pick them in the quote configurator or call them out on the drawing. Each links to its datasheet in the surface-finish library (thickness, specs, call-out, material verdicts).
Organic Coating
How much does A1N00 cost?
A1N00 is a standard-cost aluminum ($$), cheaper than about 71% of the materials FabDigit quotes. Part price depends far more on geometry, tolerance and quantity than on the raw stock — upload a CAD file for a live quote.
A1N00 — frequently asked
What is A1N00 used for?
A1N00 is typically used for electrolytic capacitor foil, high-purity electrical foil, etched anode and cathode foil stock, thin-gauge conductor strip, foil laminates and shielding and reflective foil sheet. In short: JIS capacitor-foil purity grade; near-maximum 1000-series formability; uniform etching characteristics.
What is the yield strength of A1N00?
A1N00 has a typical yield strength of 35 MPa (5.08 ksi) and a tensile strength of 90 MPa (13.1 ksi) — weaker than 96% of aluminum grades. Strength varies by condition: see the 9 listed tempers.
Is A1N00 easy to machine?
Not especially — machinability is rated poor (22/100, worse than 98% of aluminum grades). Very soft and gummy — use polished high-rake carbide, high surface speed, sharp tools and generous lubricant to avoid built-up edge; hard tempers (H18) chip better than O.
Can A1N00 be welded?
Yes — weldability is rated excellent (92/100). Excellent with GTAW/GMAW using ER1100 or ER4043 filler; resistance welding and brazing are also routine, but the weld softens to near-O strength in the HAZ.
What surface finishes work on A1N00?
Takes clear/bright anodize, chemical conversion coating, lacquer and printing well; the anodic layer stays thin and soft, so use it for appearance and corrosion rather than wear.
Can A1N00 be formed, bent or molded?
Outstanding cold formability in O/H22 — deep draws, spinning, and rolling to sub-10 µm foil; intermediate anneals restore ductility in hard tempers.
What is the maximum service temperature of A1N00?
A1N00 is rated for continuous use to about 200°C (392 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between A1N00-O and A1N00-H18?
O is the default condition — softest, most formable condition — deep drawing, foil converting and any application needing maximum ductility. H18: maximum cold-worked strength; the standard temper for hard foil and capacitor/packaging foil stock. Yield strength is 35 MPa in O versus 150 MPa in H18.
How much does A1N00 cost?
A1N00 is a standard-cost aluminum ($$), cheaper than about 71% of the materials FabDigit quotes. Part price depends far more on geometry, tolerance and quantity than on the raw stock — upload a CAD file for a live quote.
Sources
- JIS H 4000 — Aluminium and aluminium alloy sheets, strips and plates — JSA (2014)
- JIS H 4160 — Aluminium and aluminium alloy foils — JSA (2020)
- ASM Handbook Vol.2 — Properties and Selection: Nonferrous Alloys (1100 data) — ASM International (1990)
- ASM Handbook Vol.13B — Corrosion: Materials (aluminium) — ASM International (2005)
- Aluminum Association Teal Sheets — International Alloy Designations — The Aluminum Association (2018)
Property data is compiled from published supplier and standards handbooks and normalised for comparison; hardness values on non-Brinell scales are converted approximately for charting only. Manufacturability limits are FabDigit quote-engine defaults and may be relaxed by engineering review. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.