Aluminum 5754-H36
Temper
AA 5754 · UNS A95754 · EN AlMg3, AW-5754
H36 = strain hardened and stabilized, three-quarter hard
Stabilised three-quarter hard sheet for coil-formed and roll-formed profiles.
Values for the H36 condition
Other 5754 tempers and conditions
5754 is listed in 16 conditions; see the grade overview at 5754.
Compare all 16 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
As fabricated | Cheapest hot-rolled plate or extrusion where no guaranteed mechanicals are needed. | 95 | 200 | 18 | 52 HB | 35.5 % IACS |
Strain hardened from hot working only | Thick hot-rolled plate and extrusions where guaranteed minimum strength is needed without cold rolling. | 95 | 200 | 16 | 52 HB | 35.5 % IACS |
Annealed | Pick for maximum drawability/bendability in deep-drawn or severely formed parts. | 100 | 210 | 22 | 50 HB | 36 % IACS |
Slightly strain hardened | The standard European stock condition for 5754 sheet/plate: near-O formability with flatter, handling-hardened material. | 110 | 215 | 20 | 55 HB | 35 % IACS |
Strain hardened and stabilized, quarter hard | Thermally stabilised quarter-hard temper for 5000-series sheet/plate that must keep properties and avoid age softening. | 150 | 245 | 13 | 66 HB | 35 % IACS |
Strain hardened and partially annealed, quarter hard | Stabilised quarter-hard sheet: better ductility and shape stability than H12 at the same strength class. | 150 | 245 | 14 | 65 HB | 35 % IACS |
Strain hardened and partially annealed, half hard | Common half-hard temper for tread plate, vehicle panels and brackets needing strength plus some bendability. | 180 | 260 | 10 | 72 HB | 34.5 % IACS |
Strain hardened, quarter hard | Cold-rolled quarter-hard sheet for moderate strength with fair bending. | 180 | 240 | 10 | 66 HB | 35 % IACS |
Strain hardened and stabilized, half hard | Stabilised half-hard sheet/plate for welded structures and marine parts requiring property retention. | 180 | 260 | 9 | 73 HB | 34.5 % IACS |
Strain hardened, half hard | Half-hard cold-rolled sheet for flat panels and light structures with limited bending. | 205 | 260 | 7 | 72 HB | 34.5 % IACS |
Strain hardened and partially annealed, three-quarter hard | Higher-strength stabilised strip where a modest bend radius is still required. | 210 | 270 | 7 | 76 HB | 34 % IACS |
H36This page Strain hardened and stabilized, three-quarter hard | Stabilised three-quarter hard sheet for coil-formed and roll-formed profiles. | 210 | 270 | 6 | 77 HB | 34 % IACS |
Strain hardened, three-quarter hard | Three-quarter hard strip for flat, higher-strength parts with minimal forming. | 235 | 275 | 5 | 78 HB | 34 % IACS |
Strain hardened and partially annealed, full hard | Full-hard stabilised strip for high-strength flat blanks and shims. | 235 | 290 | 5 | 82 HB | 34 % IACS |
Strain hardened and stabilized, full hard | Highest-strength stabilised 5754 temper; used where stiffness/strength of thin gauge matters more than bendability. | 235 | 290 | 4 | 83 HB | 34 % IACS |
Strain hardened, full hard | Fully cold-worked strip for maximum strength; essentially no forming capability. | 265 | 300 | 3 | 85 HB | 34 % IACS |
What is 5754-H36?
5754-H36 is 5754 in the H36 temper — stabilised three-quarter hard sheet for coil-formed and roll-formed profiles. 5754-H36 has a yield strength of 210 MPa (30.5 ksi) and a tensile strength of 270 MPa (39.2 ksi) — stronger than 56% of aluminum grades. Elongation at break is 6% and the elastic modulus is 70 GPa (10.2 Msi). 5754-H36 has a density of 2.67 g/cm³ (0.0965 lb/in³), lighter than 78% of aluminum grades. It melts at 600°C (1,112 °F).
Advantages
- Good corrosion resistance — 74/100, better than 87% of aluminum grades
- Readily welded — 87/100, better than 82% of aluminum grades
Limitations
- Limited service temperature — 65°C (149 °F), worse than 97% of aluminum grades
5754-H36 properties
Typical room-temperature values for 5754-H36; 19 are specific to this condition. Other listed values are 5754 reference data and may not represent this condition. Bars are the position among aluminum grades.
Physical3
5754-H36 has a density of 2.67 g/cm³ (0.0965 lb/in³), lighter than 78% of aluminum grades. It melts at 600°C (1,112 °F).
Mechanical10
5754-H36 has a yield strength of 210 MPa (30.5 ksi) and a tensile strength of 270 MPa (39.2 ksi) — stronger than 56% of aluminum grades. Elongation at break is 6% and the elastic modulus is 70 GPa (10.2 Msi).
Thermal6
5754-H36 is rated for continuous service to 65°C (149 °F). It conducts heat at 147 W/m·K (84.9 BTU/hr·ft·°F), better than 55% of aluminum grades. Thermal expansion is 23.7 µm/m·K (13.2 µin/in·°F).
Electrical3
5754-H36 conducts electricity at 34 % IACS, worse than 52% of aluminum grades.
Chemical & Environmental3
Corrosion resistance is very good (74/100), better than 87% of aluminum grades.
Sustainability4
Producing a kilogram of 5754-H36 takes about 200 MJ of energy and emits 12.5 kg of CO₂ — less than 60% of aluminum grades. Typical recycled content is 50%.
Manufacturability7
5754-H36's machinability is fair (53/100, worse than 62% of aluminum grades); weldability excellent (87/100); formability fair (50/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with 5754-H36
Is 5754 easy to machine?
Machines like soft 5000 series: use sharp polished-flute carbide, high rake, high speed and flood coolant or mist to stop built-up edge; harder H24–H38 tempers chip much cleaner than O.
Can 5754 be welded?
Excellent for MIG/TIG, FSW, resistance and laser welding with 5356 or 5183 filler (never 4043-type Al-Si with high-Mg base); as-welded joint strength approaches O-temper base metal.
Can 5754 be formed, bent or molded?
Very good cold formability in O/H111 (deep drawing, hemming, stretch forming); keep bend radii larger and expect springback in H24 and above, and watch for Lüders/stretcher-strain marks on visible O-temper panels.
What surface finishes work on 5754?
Takes clear and hard anodizing well and is a good base for chemical conversion, e-coat and paint; brushed/etched finishes are excellent, bright decorative anodizing can appear slightly grey.
5754 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Mg | 2.6 – 3.6 | 3.1 |
| MnMn+Cr must be 0.10–0.6 | ≤ 0.5 | 0.2 |
| CrMn+Cr must be 0.10–0.6 | ≤ 0.3 | 0.05 |
| Fe | ≤ 0.4 | 0.25 |
| Si | ≤ 0.4 | 0.2 |
| Cu | ≤ 0.1 | 0.03 |
| Zn | ≤ 0.2 | 0.05 |
| Ti | ≤ 0.15 | 0.02 |
| Others (each)total others max 0.15 | ≤ 0.05 | — |
| Alremainder, ~95.5–96.5% | balance | — |
5754-H36 — frequently asked
What is 5754-H36 used for?
5754-H36 is typically used for automotive inner body panels, floor and tread plate, marine and vehicle sheet panels, welded pressure vessel shells, truck and trailer body panels and riveted sheet-metal enclosures. In short: auto body / structural sheet.
What is the yield strength of 5754-H36?
5754-H36 has a typical yield strength of 210 MPa (30.5 ksi) and a tensile strength of 270 MPa (39.2 ksi) — stronger than 56% of aluminum grades. Strength varies by condition: see the 16 listed tempers.
Is 5754-H36 easy to machine?
Reasonably — machinability is rated fair (53/100, worse than 62% of aluminum grades). Machines like soft 5000 series: use sharp polished-flute carbide, high rake, high speed and flood coolant or mist to stop built-up edge; harder H24–H38 tempers chip much cleaner than O.
Can 5754-H36 be welded?
Yes — weldability is rated excellent (87/100). Excellent for MIG/TIG, FSW, resistance and laser welding with 5356 or 5183 filler (never 4043-type Al-Si with high-Mg base); as-welded joint strength approaches O-temper base metal.
What surface finishes work on 5754-H36?
Takes clear and hard anodizing well and is a good base for chemical conversion, e-coat and paint; brushed/etched finishes are excellent, bright decorative anodizing can appear slightly grey.
Can 5754-H36 be formed, bent or molded?
Very good cold formability in O/H111 (deep drawing, hemming, stretch forming); keep bend radii larger and expect springback in H24 and above, and watch for Lüders/stretcher-strain marks on visible O-temper panels.
What is the maximum service temperature of 5754-H36?
5754-H36 is rated for continuous use to about 65°C (149 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Can FabDigit make parts in 5754-H36?
Yes — 5754-H36 is available for CNC machining and sheet metal with instant online pricing. Upload a STEP file to get a price and a DFM check.
Sources
- EN 573-3 — Aluminium and aluminium alloys, chemical composition of wrought products — CEN (2019)
- EN 485-2 — Aluminium sheet, strip and plate: mechanical properties — CEN (2021)
- International Alloy Designations and Chemical Composition Limits (Teal Sheets) — The Aluminum Association (2018)
- ASM Handbook Vol. 2 — Properties and Selection: Nonferrous Alloys — ASM International (1990)
- ASM Handbook Vol. 13B — Corrosion: Materials — ASM International (2005)
- EN AW-5754 (AlMg3) rolled products datasheet — Constellium / Aleris rolled products (2021)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.