Aluminum 5754 · temper
Aluminum 5754-H22
Properties of the H22 condition, compared with the other 5754 tempers.
Stabilised quarter-hard sheet: better ductility and shape stability than H12 at the same strength class.
What is 5754-H22?
5754-H22 is 5754 in the H22 temper — stabilised quarter-hard sheet: better ductility and shape stability than H12 at the same strength class. 5754-H22 has a yield strength of 150 MPa (21.8 ksi) and a tensile strength of 245 MPa (35.5 ksi) — weaker than 66% of aluminum grades. Elongation at break is 14% and the elastic modulus is 70 GPa (10.2 Msi). 5754-H22 has a density of 2.67 g/cm³ (0.0965 lb/in³), lighter than 78% of aluminum grades. It melts at 600°C (1,112 °F).
Advantages
- Readily welded — 92/100, better than 95% of aluminum grades
- Good corrosion resistance — 76/100, better than 90% of aluminum grades
- Forms and bends easily — 74/100, better than 86% of aluminum grades
- Ductile — tolerates forming and impact — 14%, better than 81% of aluminum grades
Limitations
- Limited service temperature — 65°C (149 °F), worse than 97% of aluminum grades
5754-H22 properties
Typical room-temperature values for 5754-H22 — 8 properties are specific to this condition; the rest are grade-level values shared by every 5754 temper. Each bar shows where the value sits among the aluminum grades in FabDigit's library — further right is higher.
Physical3
5754-H22 has a density of 2.67 g/cm³ (0.0965 lb/in³), lighter than 78% of aluminum grades. It melts at 600°C (1,112 °F).
Mechanical10
5754-H22 has a yield strength of 150 MPa (21.8 ksi) and a tensile strength of 245 MPa (35.5 ksi) — weaker than 66% of aluminum grades. Elongation at break is 14% and the elastic modulus is 70 GPa (10.2 Msi).
Thermal6
5754-H22 is rated for continuous service to 65°C (149 °F). It conducts heat at 147 W/m·K (84.9 BTU/hr·ft·°F), better than 55% of aluminum grades. Thermal expansion is 23.7 µm/m·K (13.2 µin/in·°F).
Electrical3
5754-H22 conducts electricity at 35 % IACS, better than 52% of aluminum grades.
Chemical & Environmental3
Corrosion resistance is very good (76/100), better than 90% of aluminum grades.
Sustainability4
Producing a kilogram of 5754-H22 takes about 200 MJ of energy and emits 12.5 kg of CO₂ — less than 60% of aluminum grades. Typical recycled content is 50%.
Manufacturability7
5754-H22's machinability is fair (45/100, worse than 72% of aluminum grades); weldability excellent (92/100); formability very good (74/100).
Values are nominal handbook figures for design screening. Certified mill or lot data ships with every FabDigit order on request.
Other 5754 tempers and conditions
5754 is also supplied in 15 other conditions. The full side-by-side table is on the 5754 overview.
- H24Common half-hard temper for tread plate, vehicle panels and brackets needing strength plus some bendability.180 MPa yield · 72 HB
- H34Stabilised half-hard sheet/plate for welded structures and marine parts requiring property retention.180 MPa yield · 73 HB
- H32Thermally stabilised quarter-hard temper for 5xxx sheet/plate that must keep properties and avoid age softening.150 MPa yield · 66 HB
- H22Stabilised quarter-hard sheet: better ductility and shape stability than H12 at the same strength class.150 MPa yield · 65 HB
- H111The standard European stock condition for 5754 sheet/plate: near-O formability with flatter, handling-hardened material.110 MPa yield · 55 HB
- OPick for maximum drawability/bendability in deep-drawn or severely formed parts.100 MPa yield · 50 HB
Working with 5754-H22
Is 5754 easy to machine?
Machines like soft 5xxx: use sharp polished-flute carbide, high rake, high speed and flood coolant or mist to stop built-up edge; harder H24–H38 tempers chip much cleaner than O.
Can 5754 be welded?
Excellent for MIG/TIG, FSW, resistance and laser welding with 5356 or 5183 filler (never 4043-type Al-Si with high-Mg base); as-welded joint strength approaches O-temper base metal.
Can 5754 be formed, bent or molded?
Very good cold formability in O/H111 (deep drawing, hemming, stretch forming); keep bend radii larger and expect springback in H24 and above, and watch for Lüders/stretcher-strain marks on visible O-temper panels.
What surface finishes work on 5754?
Takes clear and hard anodizing well and is a good base for chemical conversion, e-coat and paint; brushed/etched finishes are excellent, bright decorative anodizing can appear slightly grey.
5754 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Mg | 2.6 – 3.6 | 3.1 |
| MnMn+Cr must be 0.10–0.6 | ≤ 0.5 | 0.2 |
| CrMn+Cr must be 0.10–0.6 | ≤ 0.3 | 0.05 |
| Fe | ≤ 0.4 | 0.25 |
| Si | ≤ 0.4 | 0.2 |
| Cu | ≤ 0.1 | 0.03 |
| Zn | ≤ 0.2 | 0.05 |
| Ti | ≤ 0.15 | 0.02 |
| Others (each)total others max 0.15 | ≤ 0.05 | — |
| Alremainder, ~95.5–96.5% | balance | — |
5754-H22 — frequently asked
What is 5754-H22 used for?
5754-H22 is typically used for automotive inner body panels, floor and tread plate, marine and vehicle sheet panels, welded pressure vessel shells, truck and trailer body panels and riveted sheet-metal enclosures. In short: auto body / structural sheet.
What is the yield strength of 5754-H22?
5754-H22 has a typical yield strength of 150 MPa (21.8 ksi) and a tensile strength of 245 MPa (35.5 ksi) — weaker than 66% of aluminum grades. Strength varies by condition: see the 16 listed tempers.
Is 5754-H22 easy to machine?
Reasonably — machinability is rated fair (45/100, worse than 72% of aluminum grades). Machines like soft 5xxx: use sharp polished-flute carbide, high rake, high speed and flood coolant or mist to stop built-up edge; harder H24–H38 tempers chip much cleaner than O.
Can 5754-H22 be welded?
Yes — weldability is rated excellent (92/100). Excellent for MIG/TIG, FSW, resistance and laser welding with 5356 or 5183 filler (never 4043-type Al-Si with high-Mg base); as-welded joint strength approaches O-temper base metal.
What surface finishes work on 5754-H22?
Takes clear and hard anodizing well and is a good base for chemical conversion, e-coat and paint; brushed/etched finishes are excellent, bright decorative anodizing can appear slightly grey.
Can 5754-H22 be formed, bent or molded?
Very good cold formability in O/H111 (deep drawing, hemming, stretch forming); keep bend radii larger and expect springback in H24 and above, and watch for Lüders/stretcher-strain marks on visible O-temper panels.
What is the maximum service temperature of 5754-H22?
5754-H22 is rated for continuous use to about 65°C (149 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Can FabDigit make parts in 5754-H22?
Yes — 5754-H22 is available for CNC machining and sheet metal with instant online pricing. Upload a STEP file to get a price and a DFM check.
Sources
- EN 573-3 — Aluminium and aluminium alloys, chemical composition of wrought products — CEN (2019)
- EN 485-2 — Aluminium sheet, strip and plate: mechanical properties — CEN (2021)
- International Alloy Designations and Chemical Composition Limits (Teal Sheets) — The Aluminum Association (2018)
- ASM Handbook Vol. 2 — Properties and Selection: Nonferrous Alloys — ASM International (1990)
- ASM Handbook Vol. 13B — Corrosion: Materials — ASM International (2005)
- EN AW-5754 (AlMg3) rolled products datasheet — Constellium / Aleris rolled products (2021)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.