Temper
AA 5082 · EN AW-5082, AW 5082
H19 = strain hardened, extra hard
Very heavily cold-rolled thin strip for beverage can ends and tabs.
Values for the H19 condition
Other 5082 tempers and conditions
5082 is listed in 18 conditions; see the grade overview at 5082.
Compare all 18 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Annealed | Pick for maximum formability in deep drawing and severe stretch forming. | 125 | 265 | 24 | 62 HB | 29.5 % IACS |
Strain hardened from hot working only | Hot-rolled thicker plate where only minimum properties, not a defined cold-work level, are required. | 135 | 275 | 16 | 65 HB | 29 % IACS |
Slightly strain hardened | Most commonly stocked plate/sheet condition: near-annealed formability with straight, flat product. | 140 | 275 | 20 | 66 HB | 29 % IACS |
Strain hardened and partially annealed, quarter hard | Quarter-hard strength with better ductility than H12 for formed parts. | 210 | 300 | 14 | 74 HB | 29 % IACS |
Strain hardened, quarter hard | Light cold work for modest strength gain with retained bending ability. | 215 | 300 | 12 | 75 HB | 29 % IACS |
Strain hardened and stabilized, quarter hard | Stabilized quarter-hard sheet — the standard choice when age-softening must be avoided. | 215 | 305 | 12 | 76 HB | 29 % IACS |
Strain hardened, corrosion-resistant marine temper | Choose for marine hull and superstructure plate requiring ASTM G66/G67 exfoliation performance. | 215 | 305 | 12 | 78 HB | 29 % IACS |
Strain hardened and stabilized, marine temper | Standard structural plate temper for tanks, marine and pressure applications needing stable properties and good IGC resistance. | 230 | 320 | 12 | 80 HB | 29 % IACS |
Strain hardened and partially annealed, half hard | Half-hard with recovered ductility for roll-formed and moderately drawn parts. | 250 | 330 | 10 | 84 HB | 29 % IACS |
Strain hardened and stabilized, half hard | Stabilized half-hard sheet for tank walls and panels needing higher strength than H32. | 255 | 335 | 9 | 86 HB | 29 % IACS |
Strain hardened, half hard | Half-hard strip for flat or lightly formed parts needing higher yield strength. | 260 | 330 | 9 | 85 HB | 29 % IACS |
Strain hardened and partially annealed, three-quarter hard | Three-quarter hard with slightly improved bendability over H16. | 285 | 355 | 7 | 91 HB | 29 % IACS |
Strain hardened, three-quarter hard | High-strength strip where forming is limited to gentle bends. | 290 | 360 | 6 | 92 HB | 29 % IACS |
Strain hardened and stabilized, three-quarter hard | Stabilized three-quarter hard for high-strength thin sheet/strip. | 290 | 360 | 6 | 93 HB | 29 % IACS |
Strain hardened, full hard | Fully cold-worked strip for maximum strength in flat blanks. | 340 | 390 | 4 | 100 HB | 29 % IACS |
Strain hardened and stabilized, full hard | Stabilized full-hard sheet where the highest non-heat-treatable strength is needed. | 345 | 395 | 4 | 102 HB | 29 % IACS |
Strain hardened, stabilized, extra hard | Extra-hard cold-rolled and low-temperature stabilized condition of Al-4.5Mg 5082, giving the highest strength of the H3x series with very limited ductility; typical of thin can-end / closure stock. | 370 | 400 | 4 | 108 HB | 29 % IACS |
H19This page Strain hardened, extra hard | Very heavily cold-rolled thin strip for beverage can ends and tabs. | 375 | 415 | 3 | 108 HB | 29 % IACS |
What is 5082-H19?
5082-H19 is 5082 in the H19 temper — very heavily cold-rolled thin strip for beverage can ends and tabs. 5082-H19 has a yield strength of 375 MPa (54.4 ksi) and a tensile strength of 415 MPa (60.2 ksi) — stronger than 86% of aluminum grades. Elongation at break is 3% and the elastic modulus is 70 GPa (10.2 Msi). 5082-H19 has a density of 2.65 g/cm³ (0.0957 lb/in³), lighter than 90% of aluminum grades. It melts at 577°C (1,071 °F).
Advantages
- High strength — 375 MPa (54.4 ksi), better than 86% of aluminum grades
Limitations
- Limited service temperature — 65°C (149 °F), worse than 97% of aluminum grades
- Poor heat conductor — 120 W/m·K (69.3 BTU/hr·ft·°F), worse than 80% of aluminum grades
- Limited ductility — 3%, worse than 79% of aluminum grades
- Low electrical conductivity — 29 % IACS, worse than 78% of aluminum grades
5082-H19 properties
Typical room-temperature values for 5082-H19; 21 are specific to this condition. Other listed values are 5082 reference data and may not represent this condition. Bars are the position among aluminum grades.
Physical3
5082-H19 has a density of 2.65 g/cm³ (0.0957 lb/in³), lighter than 90% of aluminum grades. It melts at 577°C (1,071 °F).
Mechanical11
5082-H19 has a yield strength of 375 MPa (54.4 ksi) and a tensile strength of 415 MPa (60.2 ksi) — stronger than 86% of aluminum grades. Elongation at break is 3% and the elastic modulus is 70 GPa (10.2 Msi).
Thermal6
5082-H19 is rated for continuous service to 65°C (149 °F). It conducts heat at 120 W/m·K (69.3 BTU/hr·ft·°F), worse than 80% of aluminum grades. Thermal expansion is 24.2 µm/m·K (13.4 µin/in·°F).
Electrical3
5082-H19 conducts electricity at 29 % IACS, worse than 78% of aluminum grades.
Chemical & Environmental3
Corrosion resistance is good (62/100), better than 67% of aluminum grades.
Sustainability4
Producing a kilogram of 5082-H19 takes about 200 MJ of energy and emits 12.5 kg of CO₂ — less than 60% of aluminum grades. Typical recycled content is 35%.
Manufacturability7
5082-H19's machinability is good (58/100, worse than 54% of aluminum grades); weldability very good (80/100); formability poor (25/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with 5082-H19
Is 5082 easy to machine?
Gummy, long-chipping alloy — use sharp polished-flute carbide tools, high rake, high speed and flood coolant or MQL to prevent built-up edge; harder H3x tempers cut cleaner.
Can 5082 be welded?
Readily GMAW/GTAW welded with 5183 or 5356 filler; do not use 4000 series Si fillers (brittle Mg2Si), and keep interpass temperature low to limit sensitization.
Can 5082 be formed, bent or molded?
Excellent deep-drawing and stretch forming in O/H111; watch for Lüders (stretcher-strain) markings on annealed sheet — use temper-rolled or stabilized H2x/H3x for visible surfaces.
What surface finishes work on 5082?
Anodizes clear and bright and takes marine-grade sulphuric anodize well; brushed and painted finishes are common, flux brazing is not recommended due to the high Mg content.
5082 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Si | ≤ 0.2 | 0.1 |
| Fe | ≤ 0.35 | 0.2 |
| Cu | ≤ 0.15 | 0.05 |
| Mnlower than 5182 | ≤ 0.15 | 0.08 |
| Mgprincipal strengthening element | 4 – 5 | 4.5 |
| Cr | ≤ 0.15 | 0.05 |
| Zn | ≤ 0.25 | 0.05 |
| Ti | ≤ 0.1 | 0.02 |
| Others (each) | ≤ 0.05 | — |
| Others (total) | ≤ 0.15 | — |
| Al | balance | — |
5082-H19 — frequently asked
What is 5082-H19 used for?
5082-H19 is typically used for deep-drawn can ends, tank trucks, pressure vessels, automotive body panels, storage tanks and marine hull and deck structures. In short: marine-grade plate alloy.
What is the yield strength of 5082-H19?
5082-H19 has a typical yield strength of 375 MPa (54.4 ksi) and a tensile strength of 415 MPa (60.2 ksi) — stronger than 86% of aluminum grades. Strength varies by condition: see the 18 listed tempers.
Is 5082-H19 easy to machine?
Reasonably — machinability is rated good (58/100, worse than 54% of aluminum grades). Gummy, long-chipping alloy — use sharp polished-flute carbide tools, high rake, high speed and flood coolant or MQL to prevent built-up edge; harder H3x tempers cut cleaner.
Can 5082-H19 be welded?
Yes — weldability is rated very good (80/100). Readily GMAW/GTAW welded with 5183 or 5356 filler; do not use 4000 series Si fillers (brittle Mg2Si), and keep interpass temperature low to limit sensitization.
What surface finishes work on 5082-H19?
Anodizes clear and bright and takes marine-grade sulphuric anodize well; brushed and painted finishes are common, flux brazing is not recommended due to the high Mg content.
Can 5082-H19 be formed, bent or molded?
Excellent deep-drawing and stretch forming in O/H111; watch for Lüders (stretcher-strain) markings on annealed sheet — use temper-rolled or stabilized H2x/H3x for visible surfaces.
What is the maximum service temperature of 5082-H19?
5082-H19 is rated for continuous use to about 65°C (149 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Can FabDigit make parts in 5082-H19?
Yes — 5082-H19 is available for CNC machining and sheet metal; every part is priced by an engineer rather than instantly. Upload a STEP file to get a price and a DFM check.
Sources
- International Alloy Designations and Chemical Composition Limits for Wrought Aluminum (Teal Sheets) — The Aluminum Association (2018)
- EN 573-3 Aluminium and aluminium alloys — Chemical composition — CEN (2019)
- EN 485-2 Aluminium and aluminium alloys — Sheet, strip and plate — Mechanical properties — CEN (2016)
- ASM Handbook Vol. 2: Properties and Selection — Nonferrous Alloys — ASM International (1990)
- ASM Handbook Vol. 13B: Corrosion — Materials (aluminium alloys) — ASM International (2005)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.