Titanium Ti-15-3
UNS R58153, R58150 · also 4914, 4913
Ti-15-3 (Ti-15V-3Cr-3Al-3Sn) is a metastable beta titanium alloy supplied as UNS R58150/R58153 to AMS 4914 and AMS 4913, and also listed as Grade 20.
Values for the O condition
Ti-15-3 tempers and conditions
Ti-15-3 is supplied in 4 conditions, soft to hard. O is the default FabDigit quotes; the values on this page are for it.
Compare all 4 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
ODefault Annealed | Solution treated at about 790–815 °C and air or water quenched, this soft single-phase beta state is the delivery condition for cold rolling, deep drawing, roll forming and welding, with ageing done afterwards. | 790 | 820 | 20 | 27 HRC | — |
Cold rolled | Order as-rolled, unaged strip and foil when 960 MPa yield is enough and the part must still take bends, then age it later to develop maximum strength. | 960 | 1,000 | 8 | 33 HRC | 1.2 % IACS |
Solution treated and aged | Age at 480–540 °C for 8–24 h once forming and welding are complete to reach 1240 MPa yield for fasteners, springs and load-bearing parts; elongation falls to 7% and machining gets harder. | 1,240 | 1,300 | 7 | 43 HRC | — |
Cold worked and aged | Combine cold rolling with a 480–540 °C age for the highest strength, 1380 MPa yield, in thin-section springs, washers and clamps; elongation is only 4% and further forming is not practical. | 1,380 | 1,450 | 4 | 46 HRC | — |
What is Ti-15-3?
Ti-15-3 (Ti-15V-3Cr-3Al-3Sn) is a metastable beta titanium alloy supplied as UNS R58150/R58153 to AMS 4914 and AMS 4913, and also listed as Grade 20. Engineers choose it because it cold forms in the solution-treated condition and can then be aged to high strength, so it is bought mainly as strip, foil, sheet and wire for springs, fasteners and formed sheet parts. Limits are a 260 °C service ceiling, an elastic modulus of only 82 GPa, and poor machinability (score 20) that makes metal removal slow; Ti-6Al-4V is the usual alternative when bar or plate sections are needed. Ti-15-3 has a density of 4.76 g/cm³ (0.172 lb/in³), heavier than 92% of titanium grades. It melts at 1,600°C (2,912 °F). Ti-15-3 has a yield strength of 790 MPa (115 ksi) and a tensile strength of 820 MPa (119 ksi) — stronger than 55% of titanium grades. Elongation at break is 20% and the elastic modulus is 82 GPa (11.9 Msi).
What is Ti-15-3 used for?
- Aerospace springs
- Fasteners
- Golf shafts
Advantages
- Tough — resists crack growth — 100 MPa·√m (91 ksi·√in), better than 100% of titanium grades
- Forms and bends easily — 80/100, better than 90% of titanium grades
Limitations
- Limited service temperature — 260°C (500 °F), worse than 97% of titanium grades
- Low stiffness — 82 GPa (11.9 Msi), worse than 96% of titanium grades
- High embodied carbon — 48 kg CO₂/kg, worse than 95% of titanium grades
Ti-15-3 properties
Typical room-temperature values for Ti-15-3-O; bars are the position among titanium grades.
Physical3
Ti-15-3 has a density of 4.76 g/cm³ (0.172 lb/in³), heavier than 92% of titanium grades. It melts at 1,600°C (2,912 °F).
Mechanical15
Ti-15-3 has a yield strength of 790 MPa (115 ksi) and a tensile strength of 820 MPa (119 ksi) — stronger than 55% of titanium grades. Elongation at break is 20% and the elastic modulus is 82 GPa (11.9 Msi).
Thermal6
Ti-15-3 is rated for continuous service to 260°C (500 °F). It conducts heat at 8.1 W/m·K (4.68 BTU/hr·ft·°F), better than 52% of titanium grades. Thermal expansion is 8.5 µm/m·K (4.72 µin/in·°F).
Electrical3
Ti-15-3 conducts electricity at 1.2 % IACS, worse than 55% of titanium grades.
Chemical & Environmental3
Corrosion resistance is excellent (88/100), worse than 77% of titanium grades.
Sustainability4
Producing a kilogram of Ti-15-3 takes about 750 MJ of energy and emits 48 kg of CO₂ — more than 95% of titanium grades. Typical recycled content is 20%.
Manufacturability7
Ti-15-3's machinability is poor (20/100, worse than 68% of titanium grades); weldability very good (70/100); formability very good (80/100).
Common Calculations5
Values are nominal handbook figures for design screening. Certified mill or lot data ships with every FabDigit order on request.
Strength versus weight in the titanium family
Yield strength against density for every titanium grade FabDigit runs. Ti-15-3 is highlighted; hover a dot for its name, or open the interactive family chart.
Working with Ti-15-3
Is Ti-15-3 easy to machine?
Machinability is poor: use low surface speed with heavy feed, rigid workholding, sharp carbide or coated carbide tooling and high-pressure flood coolant. The aged condition is harder still, so avoid dwelling in the cut, which work-hardens the surface and promotes built-up edge.
Can Ti-15-3 be welded?
Weld in the solution-treated condition by GTAW, plasma arc or electron beam under inert gas or vacuum, then solution treat or age the assembly to restore joint properties. Oil, grease and air contamination must be excluded completely.
Can Ti-15-3 be formed, bent or molded?
Cold formability is excellent in the solution-treated condition — room-temperature deep drawing, roll forming and cold rolling to foil are all practical. Age after forming; do not bend material that has already been aged.
Manufacturability
The process limits FabDigit's quote engine applies to Ti-15-3. Design inside these and the part quotes instantly; outside them it routes to an engineer.
CNC machining
| Machinability | Fair20 / 100 |
|---|---|
| ISO material group | S.3 |
| Cutting speed (rough / finish) | 60 / 75 m/min |
| Minimum wall | 1 mm |
| Minimum internal radius | 1.5 mm |
| Drill depth limit | 4× diameter |
| Best surface (machined / polished) | Ra 1.6 / — |
| Hardenable after machining | No |
Sheet metal
| Formability | Better80 / 100 |
|---|---|
| Weldability | Fair70 / 100 |
| Bendable | Yes |
Ti-15-3 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Vβ-stabilizing element | 14 – 16 | 15 |
| Cr | 2.5 – 3.5 | 3 |
| Alα-stabilizer, age-hardening | 2.5 – 3.5 | 3 |
| Sn | 2.5 – 3.5 | 3 |
| Fe | ≤ 0.25 | 0.1 |
| O | ≤ 0.13 | 0.1 |
| C | ≤ 0.05 | |
| N | ≤ 0.05 | |
| Hsheet/strip product | ≤ 0.02 | |
| Ti | balance |
What surface finishes work on Ti-15-3?
Shot peening, HNO3/HF pickling for descaling, colour anodizing and painting all work. Conventional electroplating is not suitable; for fretting wear use ion nitriding or solid-film lubricant coatings.
Surface treatments FabDigit runs on titanium parts — pick them in the quote configurator or call them out on the drawing. Each links to its datasheet in the surface-finish library (thickness, specs, call-out, material verdicts).
Passivation
Conversion Coating
Organic Coating
CVD Coating
Thermal Spray
Equivalent designations
Standards and trade names that resolve to Titanium Ti-15-3 in FabDigit's catalog. Equivalence is nominal — check the exact specification when certification matters.
- UNS
- R58153R58150
- Trade names
- 49144913
- Also called
- 15-3-3-3
- Similar grades
- Grade 20
How much does Ti-15-3 cost?
Ti-15-3 is a specialty-cost titanium ($$$$$), pricier than about 99% of the materials FabDigit quotes. Part price depends far more on geometry, tolerance and quantity than on the raw stock — upload a CAD file for a live quote.
Ti-15-3 — frequently asked
What is Ti-15-3 used for?
Ti-15-3 is typically used for aerospace springs, fasteners and golf shafts. In short: cold-formable β titanium.
What is the yield strength of Ti-15-3?
Ti-15-3 has a typical yield strength of 790 MPa (115 ksi) and a tensile strength of 820 MPa (119 ksi) — stronger than 55% of titanium grades. Strength varies by condition: see the 4 listed tempers.
Is Ti-15-3 easy to machine?
Not especially — machinability is rated poor (20/100, worse than 68% of titanium grades). Machinability is poor: use low surface speed with heavy feed, rigid workholding, sharp carbide or coated carbide tooling and high-pressure flood coolant. The aged condition is harder still, so avoid dwelling in the cut, which work-hardens the surface and promotes built-up edge.
Can Ti-15-3 be welded?
Yes — weldability is rated very good (70/100). Weld in the solution-treated condition by GTAW, plasma arc or electron beam under inert gas or vacuum, then solution treat or age the assembly to restore joint properties. Oil, grease and air contamination must be excluded completely.
What surface finishes work on Ti-15-3?
Shot peening, HNO3/HF pickling for descaling, colour anodizing and painting all work. Conventional electroplating is not suitable; for fretting wear use ion nitriding or solid-film lubricant coatings.
Can Ti-15-3 be formed, bent or molded?
Cold formability is excellent in the solution-treated condition — room-temperature deep drawing, roll forming and cold rolling to foil are all practical. Age after forming; do not bend material that has already been aged.
What is the maximum service temperature of Ti-15-3?
Ti-15-3 is rated for continuous use to about 260°C (500 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between Ti-15-3-O and Ti-15-3-CRA?
O is the default condition — solution treated at about 790–815 °C and air or water quenched, this soft single-phase beta state is the delivery condition for cold rolling, deep drawing, roll forming and welding, with ageing done afterwards. CRA: combine cold rolling with a 480–540 °C age for the highest strength, 1380 MPa yield, in thin-section springs, washers and clamps; elongation is only 4% and further forming is not practical. Yield strength is 790 MPa in O versus 1,380 MPa in CRA.
How much does Ti-15-3 cost?
Ti-15-3 is a specialty-cost titanium ($$$$$), pricier than about 99% of the materials FabDigit quotes. Part price depends far more on geometry, tolerance and quantity than on the raw stock — upload a CAD file for a live quote.
Can FabDigit make parts in Ti-15-3?
Yes — Ti-15-3 is available for CNC machining and sheet metal with instant online pricing. Upload a STEP file to get a price and a DFM check.
Sources
- AMS 4914 — Titanium Alloy Sheet, Strip and Plate 15V-3Cr-3Al-3Sn, Solution Heat Treated — SAE International (2018)
- Materials Properties Handbook: Titanium Alloys — ASM International (1994)
- ASM Handbook Vol.2 — Properties and Selection: Nonferrous Alloys — ASM International (1990)
- ASM Handbook Vol.13B — Corrosion: Materials — ASM International (2005)
Property data is compiled from published supplier and standards handbooks and normalised for comparison; hardness values on non-Brinell scales are converted approximately for charting only. Manufacturability limits are FabDigit quote-engine defaults and may be relaxed by engineering review. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.