Stainless Steel S32900 Cold Rolled Annealed
Finish state
UNS S32900 · AISI/SAE 329
Choose thin-gauge sheet in 2B/2D pickled finish for linings and thin-wall heat exchanger parts; cold rolled then annealed for 550 MPa yield and 25% elongation.
Values for the Cold Rolled Annealed condition
Other S32900 tempers and conditions
S32900 is listed in 4 conditions; see the grade overview at S32900.
- Hot Finished
- Annealed
- Cold Rolled Annealed
- Cold Drawn
Compare all 4 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Hot Finished, Annealed Bar (ASTM A276/A479) | Use for large-diameter bar, flanges and valve-body forgings; hot finishing plus anneal matches annealed plate at 520 MPa yield, with slightly lower toughness in heavy sections. | 520 | 700 | 25 | 22 HRC | 2.2 % IACS |
AnnealedDefault solution annealed and quenched plate/sheet (ASTM A240) | Standard stock condition: solution annealing near 1000 °C followed by water quench balances the two phases for best corrosion resistance and toughness at 540 MPa yield. | 540 | 720 | 27 | 23 HRC | 2.2 % IACS |
Cold Rolled AnnealedThis page Cold Rolled, Annealed and Pickled Sheet (2B/2D) | Choose thin-gauge sheet in 2B/2D pickled finish for linings and thin-wall heat exchanger parts; cold rolled then annealed for 550 MPa yield and 25% elongation. | 550 | 730 | 25 | 24 HRC | 2.2 % IACS |
annealed then cold drawn to size | Pick for small-diameter precision bar needing tight size and good surface; drawing after annealing raises yield to 690 MPa but cuts elongation to 18% and limits forming. | 690 | 830 | 18 | 28 HRC | 2.2 % IACS |
What is S32900 Cold Rolled Annealed?
S32900 Cold Rolled Annealed is S32900 supplied in the Cold Rolled Annealed condition — choose thin-gauge sheet in 2B/2D pickled finish for linings and thin-wall heat exchanger parts; cold rolled then annealed for 550 MPa yield and 25% elongation. S32900 Cold Rolled Annealed has a yield strength of 550 MPa (79.8 ksi) and a tensile strength of 730 MPa (106 ksi) — stronger than 83% of stainless steel grades. Elongation at break is 25% and the elastic modulus is 200 GPa (29 Msi). S32900 Cold Rolled Annealed has a density of 7.8 g/cm³ (0.282 lb/in³), heavier than 50% of stainless steel grades. It melts at 1,400°C (2,552 °F). Annealed is the default condition FabDigit quotes; Cold Rolled Annealed is available on request or by drawing note.
Advantages
- Good corrosion resistance — 78/100, better than 84% of stainless steel grades
- High strength — 550 MPa (79.8 ksi), better than 83% of stainless steel grades
Limitations
- Limited service temperature — 300°C (572 °F), worse than 90% of stainless steel grades
- High embodied carbon — 5.5 kg CO₂/kg, worse than 77% of stainless steel grades
S32900 Cold Rolled Annealed properties
Typical room-temperature values for S32900 Cold Rolled Annealed; 24 are specific to this condition. Other listed values are S32900 reference data and may not represent this condition. Bars are the position among stainless steel grades.
Physical3
S32900 Cold Rolled Annealed has a density of 7.8 g/cm³ (0.282 lb/in³), heavier than 50% of stainless steel grades. It melts at 1,400°C (2,552 °F).
Mechanical17
S32900 Cold Rolled Annealed has a yield strength of 550 MPa (79.8 ksi) and a tensile strength of 730 MPa (106 ksi) — stronger than 83% of stainless steel grades. Elongation at break is 25% and the elastic modulus is 200 GPa (29 Msi).
Thermal6
S32900 Cold Rolled Annealed is rated for continuous service to 300°C (572 °F). It conducts heat at 16 W/m·K (9.24 BTU/hr·ft·°F), better than 58% of stainless steel grades. Thermal expansion is 11 µm/m·K (6.11 µin/in·°F).
Electrical3
S32900 Cold Rolled Annealed conducts electricity at 2.2 % IACS, worse than 61% of stainless steel grades.
Chemical & Environmental3
Corrosion resistance is very good (78/100), better than 84% of stainless steel grades.
Sustainability4
Producing a kilogram of S32900 Cold Rolled Annealed takes about 55 MJ of energy and emits 5.5 kg of CO₂ — more than 50% of stainless steel grades. Typical recycled content is 60%.
Manufacturability7
S32900 Cold Rolled Annealed's machinability is poor (33/100, worse than 57% of stainless steel grades); weldability good (55/100); formability fair (45/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with S32900 Cold Rolled Annealed
Is S32900 easy to machine?
Work-hardens strongly and needs roughly 1.5 times the cutting force of 304. Use a rigid machine, low speed with heavy feed, sharp coated carbide tooling and flood coolant, and never allow the tool to dwell or rub.
Can S32900 be welded?
GTAW, GMAW and SMAW are all usable with over-alloyed 2209 / E2209-type filler and heat input controlled to 0.5–2.0 kJ/mm. Because the base metal carries no nitrogen, a post-weld solution treatment at 1010–1120 °C followed by water quench should be applied wherever possible to restore ferrite/austenite balance and toughness.
Can S32900 be formed, bent or molded?
Cold forming requires much higher force than austenitic stainless and generous springback compensation. Hot form at 950–1150 °C and follow with a full solution anneal and water quench; do not dwell or finish forming in the 650–950 °C range where sigma phase precipitates.
What surface finishes work on S32900?
Pickle and passivate (nitric/hydrofluoric) to restore the passive film after welding or hot work. The surface can be mechanically polished to a mirror finish; anodizing does not apply, and all weld heat tint must be removed to keep corrosion resistance.
S32900 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| CASTM A240 | ≤ 0.08 | 0.05 |
| Mn | ≤ 1 | 0.6 |
| Si | ≤ 0.75 | 0.5 |
| P | ≤ 0.04 | 0.03 |
| S | ≤ 0.03 | 0.01 |
| Cr | 23 – 28 | 26 |
| Ni | 2.5 – 5 | 4 |
| Mo | 1 – 2 | 1.5 |
| Nno N specified in base grade; A789/A790 use 0.10 max or none | ≈ 0.05 | 0.05 |
| Fe | balance | — |
S32900 Cold Rolled Annealed — frequently asked
What is S32900 Cold Rolled Annealed used for?
S32900 Cold Rolled Annealed is typically used for heat exchanger tubing, condensers and acid processing equipment. In short: first-generation duplex stainless; chloride SCC resistant; largely superseded by 2205.
What is the yield strength of S32900 Cold Rolled Annealed?
S32900 Cold Rolled Annealed has a typical yield strength of 550 MPa (79.8 ksi) and a tensile strength of 730 MPa (106 ksi) — stronger than 83% of stainless steel grades. Strength varies by condition: see the 4 listed tempers.
Is S32900 Cold Rolled Annealed easy to machine?
Not especially — machinability is rated poor (33/100, worse than 57% of stainless steel grades). Work-hardens strongly and needs roughly 1.5 times the cutting force of 304. Use a rigid machine, low speed with heavy feed, sharp coated carbide tooling and flood coolant, and never allow the tool to dwell or rub.
Can S32900 Cold Rolled Annealed be welded?
Yes — weldability is rated good (55/100). GTAW, GMAW and SMAW are all usable with over-alloyed 2209 / E2209-type filler and heat input controlled to 0.5–2.0 kJ/mm. Because the base metal carries no nitrogen, a post-weld solution treatment at 1010–1120 °C followed by water quench should be applied wherever possible to restore ferrite/austenite balance and toughness.
What surface finishes work on S32900 Cold Rolled Annealed?
Pickle and passivate (nitric/hydrofluoric) to restore the passive film after welding or hot work. The surface can be mechanically polished to a mirror finish; anodizing does not apply, and all weld heat tint must be removed to keep corrosion resistance.
Can S32900 Cold Rolled Annealed be formed, bent or molded?
Cold forming requires much higher force than austenitic stainless and generous springback compensation. Hot form at 950–1150 °C and follow with a full solution anneal and water quench; do not dwell or finish forming in the 650–950 °C range where sigma phase precipitates.
What is the maximum service temperature of S32900 Cold Rolled Annealed?
S32900 Cold Rolled Annealed is rated for continuous use to about 300°C (572 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- ASTM A240/A240M — Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip — ASTM International (2023)
- ASTM A789/A790 — Ferritic/Austenitic Stainless Steel Tubing and Pipe — ASTM International (2021)
- ASTM A276/A479 — Stainless Steel Bars and Shapes — ASTM International (2022)
- ASM Handbook Vol.1: Properties and Selection — Irons, Steels, and High-Performance Alloys — ASM International (1990)
- Duplex stainless steel data sheets (Type 329 / S32900) — Outokumpu / Sandvik (2020)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.