Stainless Steel S32003-CD (Cold drawn)
Supply condition
UNS S32003
Pick for shafting, fasteners and machined parts needing higher yield strength and tight tolerance.
Values for the CD condition
Other S32003 tempers and conditions
S32003 is listed in 5 conditions; see the grade overview at S32003.
Compare all 5 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
As-welded deposit | Represents in-service welded joints; expect lower toughness and slightly reduced pitting resistance from ferrite-rich HAZ and nitrogen loss. | 510 | 720 | 22 | 23 HRC | 2.2 % IACS |
Forged + solution annealed (ASTM A182/A815 type flanges and fittings) | Pick for flanges, valve bodies and heavy fittings; requires post-forge solution anneal and quench to restore phase balance. | 520 | 710 | 30 | 24 HRC | 2.2 % IACS |
AnnealedDefault solution annealed and quenched (mill annealed, ~1000–1080 °C, water quench) | Standard mill-supplied condition for all wrought S32003 products; balanced 50/50 ferrite–austenite for best corrosion and toughness. | 530 | 730 | 32 | 25 HRC | — |
Cold Rolled 2B | Pick for thin sheet/coil (<6 mm) needing a smooth mill finish for forming and welded tube making. | 560 | 760 | 30 | 26 HRC | 2.2 % IACS |
CDThis page Cold drawn | Pick for shafting, fasteners and machined parts needing higher yield strength and tight tolerance. | 650 | 820 | 22 | 28 HRC | 2.2 % IACS |
What is S32003-CD?
S32003-CD is S32003 supplied in the CD condition — pick for shafting, fasteners and machined parts needing higher yield strength and tight tolerance. S32003-CD has a yield strength of 650 MPa (94.3 ksi) and a tensile strength of 820 MPa (119 ksi) — stronger than 90% of stainless steel grades. Elongation at break is 22% and the elastic modulus is 200 GPa (29 Msi). S32003-CD has a density of 7.8 g/cm³ (0.282 lb/in³), heavier than 50% of stainless steel grades. It melts at 1,385°C (2,525 °F). Annealed is the default condition FabDigit quotes; CD is available on request or by drawing note.
Advantages
- High strength — 650 MPa (94.3 ksi), better than 90% of stainless steel grades
Limitations
- Limited service temperature — 300°C (572 °F), worse than 90% of stainless steel grades
- Limited ductility — 22%, worse than 75% of stainless steel grades
S32003-CD properties
Typical room-temperature values for S32003-CD; 22 are specific to this condition. Other listed values are S32003 reference data and may not represent this condition. Bars are the position among stainless steel grades.
Physical3
S32003-CD has a density of 7.8 g/cm³ (0.282 lb/in³), heavier than 50% of stainless steel grades. It melts at 1,385°C (2,525 °F).
Mechanical17
S32003-CD has a yield strength of 650 MPa (94.3 ksi) and a tensile strength of 820 MPa (119 ksi) — stronger than 90% of stainless steel grades. Elongation at break is 22% and the elastic modulus is 200 GPa (29 Msi).
Thermal6
S32003-CD is rated for continuous service to 300°C (572 °F). It conducts heat at 15.5 W/m·K (8.96 BTU/hr·ft·°F), better than 53% of stainless steel grades. Thermal expansion is 13 µm/m·K (7.22 µin/in·°F).
Electrical3
S32003-CD conducts electricity at 2.2 % IACS, worse than 61% of stainless steel grades.
Chemical & Environmental3
Corrosion resistance is very good (71/100), better than 70% of stainless steel grades.
Sustainability4
Producing a kilogram of S32003-CD takes about 62 MJ of energy and emits 5.2 kg of CO₂ — more than 75% of stainless steel grades. Typical recycled content is 65%.
Manufacturability7
S32003-CD's machinability is poor (33/100, worse than 57% of stainless steel grades); weldability good (66/100); formability fair (35/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with S32003-CD
Is S32003 easy to machine?
Machine like 2205: rigid setups, positive-rake carbide, ~30–40% of 304 surface speed, heavy constant feed and flood coolant to avoid work hardening.
Can S32003 be welded?
Weld with 2209-type (or matching lean-duplex) filler, Ar+1–3%N₂ shielding, heat input ~0.5–2.0 kJ/mm and interpass <150 °C to keep 35–60% ferrite; avoid autogenous welds without filler or N₂ addition.
Can S32003 be formed, bent or molded?
Cold forms well but needs ~2× the press force and larger bend radii than 304 with high springback; hot work 950–1150 °C followed by full solution anneal and quench.
What surface finishes work on S32003?
Pickle and passivate (nitric or citric per ASTM A967) after welding/grinding; no anodizing — mechanical polish or electropolish for hygienic surfaces.
S32003 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| C | ≤ 0.03 | 0.02 |
| Si | ≤ 1 | 0.5 |
| Mn | ≤ 2 | 1.5 |
| P | ≤ 0.03 | — |
| S | ≤ 0.02 | — |
| Cr | 19.5 – 22.5 | 21 |
| Ni | 3 – 4 | 3.5 |
| Molean Mo vs 2205 | 1.5 – 2 | 1.75 |
| Naustenite stabiliser, raises PREN | 0.14 – 0.2 | 0.17 |
| Fe | balance | — |
S32003-CD — frequently asked
What is S32003-CD used for?
S32003-CD is typically used for pressure vessels, tank trailers and structural pipe. In short: lean duplex, 2205 strength; lower alloy cost; reduced molybdenum content.
What is the yield strength of S32003-CD?
S32003-CD has a typical yield strength of 650 MPa (94.3 ksi) and a tensile strength of 820 MPa (119 ksi) — stronger than 90% of stainless steel grades. Strength varies by condition: see the 5 listed tempers.
Is S32003-CD easy to machine?
Not especially — machinability is rated poor (33/100, worse than 57% of stainless steel grades). Machine like 2205: rigid setups, positive-rake carbide, ~30–40% of 304 surface speed, heavy constant feed and flood coolant to avoid work hardening.
Can S32003-CD be welded?
Yes — weldability is rated good (66/100). Weld with 2209-type (or matching lean-duplex) filler, Ar+1–3%N₂ shielding, heat input ~0.5–2.0 kJ/mm and interpass <150 °C to keep 35–60% ferrite; avoid autogenous welds without filler or N₂ addition.
What surface finishes work on S32003-CD?
Pickle and passivate (nitric or citric per ASTM A967) after welding/grinding; no anodizing — mechanical polish or electropolish for hygienic surfaces.
Can S32003-CD be formed, bent or molded?
Cold forms well but needs ~2× the press force and larger bend radii than 304 with high springback; hot work 950–1150 °C followed by full solution anneal and quench.
What is the maximum service temperature of S32003-CD?
S32003-CD is rated for continuous use to about 300°C (572 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between S32003 Annealed and S32003-CD?
Annealed is the default condition — standard mill-supplied condition for all wrought S32003 products; balanced 50/50 ferrite–austenite for best corrosion and toughness. CD: pick for shafting, fasteners and machined parts needing higher yield strength and tight tolerance. Yield strength is 530 MPa in Annealed versus 650 MPa in CD.
Sources
- ASTM A240/A240M — Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip (UNS S32003) — ASTM International (2023)
- ASTM A789/A790 — Seamless and Welded Ferritic/Austenitic Stainless Steel Tubing and Pipe — ASTM International (2021)
- ATI 2003 Lean Duplex Stainless Steel Technical Data Sheet — ATI (Allegheny Technologies) (2014)
- Practical Guidelines for the Fabrication of Duplex Stainless Steels, 3rd ed. — IMOA (2014)
- ASM Handbook Vol.1 — Properties and Selection: Irons, Steels, and High-Performance Alloys — ASM International (1990)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.