PMMA UV Resistant
Grade
also Acrylite, Perspex
For long-life outdoor glazing, signage faces and automotive lenses, or to shield UV-sensitive contents behind the sheet.
Values for the UV Resistant condition
Other PMMA grades and fills
PMMA is listed in 8 conditions; see the grade overview at PMMA.
- Impact Modified
- FR
- UV Resistant
- Extruded
- INJ
- Optical Grade
- Cast
- HH
Compare all 8 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
rubber-toughened acrylic (HI-PMMA / acrylic-impact blends) | Use where clarity is still needed but breakage or notch sensitivity is the failure mode — machine guards, signage, POP displays. | 47 | 50 | 35 | 60 HRM |
FR V-0 | For lighting diffusers, transit glazing and electrical enclosures needing UL 94 V-0 or low smoke; expect some loss of clarity and toughness. | 56 | 58 | 3 | 87 Shore D |
UV ResistantThis page UV-absorber stabilised outdoor grade | For long-life outdoor glazing, signage faces and automotive lenses, or to shield UV-sensitive contents behind the sheet. | 68 | 70 | 4.5 | 89 Shore D |
ExtrudedDefault standard extruded sheet / general purpose grade | Lowest-cost transparent acrylic sheet with tight thickness tolerance; best for thermoforming, laser cutting and signage. | — | 70 | 4.5 | 92 HRM |
General-purpose injection-molding pellet grade | Free-flowing pellet grade for thin-wall transparent moldings; dry 4 h at 80 °C before molding. | 70 | 72 | 4 | 90 Shore D |
low-birefringence, high-purity molding/sheet grade | Pick for lenses, light guides, LED optics and display covers where transmission, low haze and low birefringence matter. | — | 72 | 4 | — |
As cast | Choose for machined and polished parts, thick sheet, chemical exposure and laser-engraved work — higher MW gives better crazing and thermal resistance. | — | 76 | 4 | 100 HRM |
Heat-resistant / high-Tg acrylic copolymer | Pick when clarity must survive lamp housings, headlight lenses or autoclave-adjacent temperatures above 100 °C. | — | 76 | 3.5 | — |
What is PMMA UV Resistant?
PMMA UV Resistant is PMMA in the UV Resistant grade — for long-life outdoor glazing, signage faces and automotive lenses, or to shield UV-sensitive contents behind the sheet. PMMA UV Resistant has a yield strength of 68 MPa (9.86 ksi) and a tensile strength of 70 MPa (10.2 ksi) — stronger than 77% of polymer grades. Elongation at break is 4.5% and the elastic modulus is 3.2 GPa (0.464 Msi). PMMA UV Resistant has a density of 1.19 g/cm³ (0.043 lb/in³), heavier than 53% of polymer grades. Its glass-transition temperature is 105°C (221 °F). Extruded is the default condition FabDigit quotes; UV Resistant is available on request or by drawing note.
Advantages
- Good UV / weathering resistance — 98/100, better than 99% of polymer grades
- Polishes to a fine finish — 96/100, better than 99% of polymer grades
- High strength — 68 MPa (9.86 ksi), better than 77% of polymer grades
- Stiff — 3.2 GPa (0.464 Msi), better than 77% of polymer grades
Limitations
- Low fracture toughness — 1.2 MPa·√m (1.09 ksi·√in), worse than 77% of polymer grades
- Limited ductility — 4.5%, worse than 75% of polymer grades
PMMA UV Resistant properties
Typical room-temperature values for PMMA UV Resistant; 28 are specific to this condition. Other listed values are PMMA reference data and may not represent this condition. Bars are the position among polymer grades.
Physical6
PMMA UV Resistant has a density of 1.19 g/cm³ (0.043 lb/in³), heavier than 53% of polymer grades. Its glass-transition temperature is 105°C (221 °F).
Mechanical16
PMMA UV Resistant has a yield strength of 68 MPa (9.86 ksi) and a tensile strength of 70 MPa (10.2 ksi) — stronger than 77% of polymer grades. Elongation at break is 4.5% and the elastic modulus is 3.2 GPa (0.464 Msi).
Thermal11
PMMA UV Resistant is rated for continuous service to 75°C (167 °F). It conducts heat at 0.19 W/m·K (0.11 BTU/hr·ft·°F), worse than 68% of polymer grades. Thermal expansion is 70 µm/m·K (38.9 µin/in·°F).
Electrical7
PMMA UV Resistant is an electrical insulator with a dielectric strength of 25 kV/mm (635 V/mil) and a resistivity of 1×10¹³ Ω·m.
Chemical & Environmental3
Corrosion resistance is very good (80/100), worse than 52% of polymer grades. UV resistance is excellent.
Sustainability4
Producing a kilogram of PMMA UV Resistant takes about 101 MJ of energy and emits 6.4 kg of CO₂ — less than 56% of polymer grades. Typical recycled content is 2%.
Manufacturability8
PMMA UV Resistant's machinability is very good (70/100, better than 74% of polymer grades); weldability poor (30/100); formability fair (40/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with PMMA UV Resistant
Is PMMA easy to machine?
Machines cleanly with sharp, polished, high-rake carbide tools and high spindle speed / low feed; use 0° rake or step drills to avoid chipping, and anneal (80 °C, 1 h per 3 mm) before and after cutting to prevent crazing.
Can PMMA be welded?
Not conventionally weldable — join with methylene-chloride or MMA cement (solvent/polymerisable), UV-cure acrylic adhesive, or ultrasonic welding for molded parts; hot-gas/hot-plate welding is possible but leaves visible seams.
Can PMMA be formed, bent or molded?
Thermoform at 150–175 °C from dried sheet; injection mold at 220–265 °C melt / 50–90 °C mold after drying 3–4 h at 80 °C, and hold back pressure to avoid silver streaking.
What surface finishes work on PMMA?
Flame, diamond or buff polish gives optical edges; hard-coat lacquers improve scratch and chemical resistance; paints and inks must be acrylic/urethane-based — solvent-rich systems craze the surface.
PMMA chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| methyl acrylate / ethyl acrylate comonomadded in extrusion/injection grades for thermal-processing stability | 0 – 8 | 2 |
| acrylic impact modifier (core-shell rubbonly in impact-modified grades | 0 – 25 | 0 |
| UV absorber (benzotriazole/benzophenone)UV-resistant grades | 0 – 1 | 0 |
| processing aids / release agent / antiox | 0 – 1 | 0.3 |
| methyl methacrylate (MMA)polymerised MMA backbone; homopolymer for cast sheet | ≥ 92 (balance) | — |
PMMA UV Resistant — frequently asked
What is PMMA UV Resistant used for?
PMMA UV Resistant is typically used for automotive taillight lenses, illuminated signage and lettering, machine guards and viewing windows, light pipes and optical lenses, display cases and retail fixtures and skylights and architectural glazing. In short: crystal clear; weatherproof.
What is the yield strength of PMMA UV Resistant?
PMMA UV Resistant has a typical yield strength of 68 MPa (9.86 ksi) and a tensile strength of 70 MPa (10.2 ksi) — stronger than 77% of polymer grades. Strength varies by condition: see the 8 listed tempers.
Is PMMA UV Resistant easy to machine?
Yes — machinability is rated very good (70/100, better than 74% of polymer grades). Machines cleanly with sharp, polished, high-rake carbide tools and high spindle speed / low feed; use 0° rake or step drills to avoid chipping, and anneal (80 °C, 1 h per 3 mm) before and after cutting to prevent crazing.
Can PMMA UV Resistant be welded?
Not readily — weldability is rated poor (30/100). Not conventionally weldable — join with methylene-chloride or MMA cement (solvent/polymerisable), UV-cure acrylic adhesive, or ultrasonic welding for molded parts; hot-gas/hot-plate welding is possible but leaves visible seams.
What surface finishes work on PMMA UV Resistant?
Flame, diamond or buff polish gives optical edges; hard-coat lacquers improve scratch and chemical resistance; paints and inks must be acrylic/urethane-based — solvent-rich systems craze the surface.
Can PMMA UV Resistant be formed, bent or molded?
Thermoform at 150–175 °C from dried sheet; injection mold at 220–265 °C melt / 50–90 °C mold after drying 3–4 h at 80 °C, and hold back pressure to avoid silver streaking.
What is the maximum service temperature of PMMA UV Resistant?
PMMA UV Resistant is rated for continuous use to about 75°C (167 °F), and briefly to 95°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between PMMA Extruded and PMMA FR?
Extruded is the default condition — lowest-cost transparent acrylic sheet with tight thickness tolerance; best for thermoforming, laser cutting and signage. FR: for lighting diffusers, transit glazing and electrical enclosures needing UL 94 V-0 or low smoke; expect some loss of clarity and toughness. Yield strength is 68 MPa in Extruded versus 56 MPa in FR.
Can FabDigit make parts in PMMA UV Resistant?
Yes — PMMA UV Resistant is available for CNC machining, sheet metal and injection molding with instant online pricing. Upload a STEP file to get a price and a DFM check.
Sources
- ISO 7823-1/-2 (Poly(methyl methacrylate) sheets — cast and extruded) — ISO (2003)
- ASTM D788 Standard Classification for Poly(Methyl Methacrylate) Molding and Extrusion Compounds — ASTM (2018)
- PLEXIGLAS GS/XT and molding compound datasheets — Röhm GmbH (2023)
- ACRYLITE cast and extruded sheet technical data — Röhm America / Trinseo (2022)
- ACRYPET molding grade technical brochure — Mitsubishi Chemical (2021)
- CAMPUS plastics database — PMMA property profiles (ISO 10350) — CWFG (2024)
- Engineered Materials Handbook Vol. 2: Engineering Plastics — ASM International (1988)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.