PEEK-ESD ESD-COND
Additive grade
Use where true grounding/charge bleed-off in the conductive range is required rather than dissipative decay.
Values for the ESD-COND condition
Other PEEK-ESD grades and fills
PEEK-ESD is listed in 6 conditions; see the grade overview at PEEK-ESD.
Compare all 6 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
ESD-CONDThis page high-loading carbon black, conductive (10²–10⁴ Ω/sq) | Use where true grounding/charge bleed-off in the conductive range is required rather than dissipative decay. | — | 72 | 3 | — |
dissipative bearing grade (carbon + PTFE/graphite) | For ESD-safe sliding surfaces, guide rails and bushings where low friction and low wear debris matter more than strength. | — | 80 | 3 | — |
ESD-CBDefault Carbon-black filled, static dissipative | General-purpose static-dissipative PEEK stock shape or molding compound for ESD-safe fixtures, guides and handling parts. | 88 | 90 | 6 | 86 Shore D |
semiconductor-clean stock shape (low ionic/metal extractables) | Specify when the part contacts wafers or wet-process chemistry and extractable-ion/metal certificates plus tight resistivity control are required. | 92 | 95 | 8 | 85 Shore D |
Carbon-nanotube modified, low-contamination dissipative | Pick when a tight, stable 10⁶–10⁹ Ω/sq window plus high ductility and minimal particle shedding is needed for wafer/panel contact parts. | — | 98 | 15 | — |
30 % carbon fibre reinforced, conductive and stiff | Choose for stiff, dimensionally stable ESD structural parts — end effectors, arms, test fixtures — where 10³–10⁵ Ω/sq is acceptable. | 180 | 185 | 2 | 105 HRM |
What is PEEK-ESD ESD-COND?
PEEK-ESD ESD-COND is PEEK-ESD in the ESD-COND grade — use where true grounding/charge bleed-off in the conductive range is required rather than dissipative decay. PEEK-ESD ESD-COND has a yield strength of 88 MPa (12.8 ksi) and a tensile strength of 72 MPa (10.4 ksi) — stronger than 90% of polymer grades. Elongation at break is 3% and the elastic modulus is 5 GPa (0.725 Msi). PEEK-ESD ESD-COND has a density of 1.44 g/cm³ (0.052 lb/in³), heavier than 85% of polymer grades. Its glass-transition temperature is 143°C (289 °F). ESD-CB is the default condition FabDigit quotes; ESD-COND is available on request or by drawing note.
Advantages
- Conducts heat well — 0.55 W/m·K (0.318 BTU/hr·ft·°F), better than 99% of polymer grades
- High service temperature — 250°C (482 °F), better than 94% of polymer grades
- Tough — resists crack growth — 4 MPa·√m (3.64 ksi·√in), better than 92% of polymer grades
- Good corrosion resistance — 92/100, better than 91% of polymer grades
- High strength — 88 MPa (12.8 ksi), better than 90% of polymer grades
Limitations
- High embodied carbon — 13 kg CO₂/kg, worse than 93% of polymer grades
- Heavy — 1.44 g/cm³ (0.052 lb/in³), worse than 85% of polymer grades
- Limited ductility — 3%, worse than 83% of polymer grades
PEEK-ESD ESD-COND properties
Typical room-temperature values for PEEK-ESD ESD-COND; 12 are specific to this condition. Other listed values are PEEK-ESD reference data and may not represent this condition. Bars are the position among polymer grades.
Physical5
PEEK-ESD ESD-COND has a density of 1.44 g/cm³ (0.052 lb/in³), heavier than 85% of polymer grades. Its glass-transition temperature is 143°C (289 °F).
Mechanical16
PEEK-ESD ESD-COND has a yield strength of 88 MPa (12.8 ksi) and a tensile strength of 72 MPa (10.4 ksi) — stronger than 90% of polymer grades. Elongation at break is 3% and the elastic modulus is 5 GPa (0.725 Msi).
Thermal11
PEEK-ESD ESD-COND is rated for continuous service to 250°C (482 °F). It conducts heat at 0.55 W/m·K (0.318 BTU/hr·ft·°F), better than 99% of polymer grades. Thermal expansion is 45 µm/m·K (25 µin/in·°F).
Electrical3
PEEK-ESD ESD-COND has an electrical resistivity of 1 Ω·m.
Chemical & Environmental3
Corrosion resistance is excellent (92/100), better than 91% of polymer grades. UV resistance is very good.
Sustainability4
Producing a kilogram of PEEK-ESD ESD-COND takes about 300 MJ of energy and emits 13 kg of CO₂ — more than 97% of polymer grades. Typical recycled content is 0%.
Manufacturability8
PEEK-ESD ESD-COND's machinability is good (55/100, worse than 64% of polymer grades); weldability fair (40/100); formability poor (20/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with PEEK-ESD ESD-COND
Is PEEK-ESD easy to machine?
Machines like unfilled PEEK but the carbon filler is abrasive — use polished-flute carbide or PCD tooling, sharp positive rake, high speed/low feed, air or clean coolant, and stress-relieve thick stock before finish cuts.
Can PEEK-ESD be welded?
Hot-plate, ultrasonic, IR and spin welding work with reduced joint strength; laser transmission welding is impossible because the part is opaque black — mechanical fastening or adhesive bonding after plasma treatment is common.
Can PEEK-ESD be formed, bent or molded?
Inject at 370–400 °C melt with 180–200 °C mold and slow decompression to keep the conductive network intact; hot runners and high shear can break carbon-black/CNT chains and raise resistivity, so gate and screw design are checked against target Ω/sq.
What surface finishes work on PEEK-ESD?
Cannot be plated or painted usefully in ESD service; specify machined or bead-blasted matte surfaces, deburr carefully to avoid loose carbon particles, and verify surface resistivity per ANSI/ESD STM11.11 after any surface treatment.
PEEK-ESD chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| conductive carbon blackprimary conductive network in the default ESD grade | 4 – 15 | 8 |
| carbon nanotube (MWCNT)used instead of carbon black in low-particulation ESD-CNT grades | 1 – 5 | 3 |
| carbon fiber30 % in CF30-ESD structural conductive grade | 0 – 30 | 0 |
| PTFE / graphite lubricantonly in ESD-TRIBO bearing grades | 0 – 10 | 0 |
| polyetheretherketone (PEEK) resinhigh-viscosity injection/extrusion grade base polymer | ≥ 85 (balance) | — |
PEEK-ESD ESD-COND — frequently asked
What is PEEK-ESD ESD-COND used for?
PEEK-ESD ESD-COND is typically used for wafer handling components, electronics fixtures, ESD-safe tooling and cleanroom parts. In short: controlled surface resistivity; cleanroom-compatible PEEK; opaque black only.
What is the yield strength of PEEK-ESD ESD-COND?
PEEK-ESD ESD-COND has a typical yield strength of 88 MPa (12.8 ksi) and a tensile strength of 72 MPa (10.4 ksi) — stronger than 90% of polymer grades. Strength varies by condition: see the 6 listed tempers.
Is PEEK-ESD ESD-COND easy to machine?
Reasonably — machinability is rated good (55/100, worse than 64% of polymer grades). Machines like unfilled PEEK but the carbon filler is abrasive — use polished-flute carbide or PCD tooling, sharp positive rake, high speed/low feed, air or clean coolant, and stress-relieve thick stock before finish cuts.
Can PEEK-ESD ESD-COND be welded?
With care — weldability is rated fair (40/100). Hot-plate, ultrasonic, IR and spin welding work with reduced joint strength; laser transmission welding is impossible because the part is opaque black — mechanical fastening or adhesive bonding after plasma treatment is common.
What surface finishes work on PEEK-ESD ESD-COND?
Cannot be plated or painted usefully in ESD service; specify machined or bead-blasted matte surfaces, deburr carefully to avoid loose carbon particles, and verify surface resistivity per ANSI/ESD STM11.11 after any surface treatment.
Can PEEK-ESD ESD-COND be formed, bent or molded?
Inject at 370–400 °C melt with 180–200 °C mold and slow decompression to keep the conductive network intact; hot runners and high shear can break carbon-black/CNT chains and raise resistivity, so gate and screw design are checked against target Ω/sq.
What is the maximum service temperature of PEEK-ESD ESD-COND?
PEEK-ESD ESD-COND is rated for continuous use to about 250°C (482 °F), and briefly to 310°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- Victrex PEEK polymer properties and processing guide — Victrex plc (2023)
- TECAPEEK ELS / ELS nano / CF30 stock shape data — Ensinger GmbH (2023)
- Ketron PEEK and Semitron ESd stock shape data sheets — Mitsubishi Chemical Advanced Materials (2023)
- ANSI/ESD STM11.11 — Surface Resistance Measurement of Static Dissipative Planar Materials — ESD Association (2015)
- ASTM D257 — DC Resistance or Conductance of Insulating Materials — ASTM (2021)
- CAMPUS / UL Prospector PAEK compound property records — CAMPUS Consortium (2024)
- ASM Engineered Materials Handbook Vol. 2 — Engineering Plastics — ASM International (1988)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.