ABS vs PEEK-ESD
Polymer · grade comparison
ABS and PEEK-ESD are both polymer grades. PEEK-ESD is the stronger of the two: yield strength 88 MPa (12.8 ksi) against 42 MPa (6.09 ksi) for ABS, about 110% more; tensile strength follows at 90 MPa (13.1 ksi) vs 43 MPa (6.24 ksi). In exchange, ABS is the more ductile: elongation 25% versus 6% for PEEK-ESD, and PEEK-ESD is harder (86 Shore D vs 78 Shore D). ABS is lighter (1.04 g/cm³ vs 1.42 g/cm³ for PEEK-ESD) and PEEK-ESD is stiffer (4.2 GPa vs 2.3 GPa). On the shop floor, ABS machines more easily (very good vs good), ABS welds better (very good vs fair), and ABS sits in a lower cost tier (budget, $) than PEEK-ESD (high, $$$$).
ABSChoose it when the part is bent, formed or impact-loaded, or when weight is the constraint.
PEEK-ESDChoose it when strength drives the design, or when the part sees heat.
ABS vs PEEK-ESD: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Compressive Strength
Compressive Modulus
Flexural Strength
Flexural Modulus
Shear Strength
Fracture Toughness (K_IC)
Izod Impact, Notched
Hardness, Shore D
Hardness, Rockwell R
Hardness, Rockwell M
Physical
Density and transition temperatures.
Density
Glass Transition (Tg)
Water Absorption (24 h)
Water Absorption (Saturation)
Melting Temperature (Tm)
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Heat Deflection Temp. @ 0.45 MPa
Heat Deflection Temp. @ 1.8 MPa
Vicat Softening Point (B50)
Limiting Oxygen Index
Max Service Temperature (short-term)
Electrical
Conductivity and insulation.
Electrical Resistivity
Dielectric Strength
Dielectric Constant (1 MHz)
Dissipation Factor (1 MHz)
Volume Resistivity
Surface Resistivity
Comparative Tracking Index (CTI)
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
UV / Weathering Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Polishability
Mold Shrinkage
Melt Flow Rate
Processing Melt Temperature (typ.)
Mold Temperature (typ.)
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 0
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | ABS | PEEK-ESD |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Injection molding | Yes | — |
| 3D printing | Yes | — |
| Default condition | Unfilled | — |
| Relative cost | $ Budget | $$$$ High |
| Min. machined wall | 0.5 mm | — |
| Best machined surface | Ra 0.8 µm | — |
| Chrome Plating (Plastic) | Yes | — |
| Conductive Coating | Yes | — |
| Dyeing (Nylon) | Yes | — |
| EMI Shielding Coating | Yes | — |
| Painting | Yes | — |
| Primer Coating | Yes | — |
| Soft Touch Coating | Yes | — |
| Spray Painting | Yes | — |
| Tinted Coating | Yes | — |
| UV Coating | Yes | — |
| Vacuum Metallization | Yes | — |
| Waterproof Coating | Yes | — |
ABS vs PEEK-ESD — frequently asked
Is PEEK-ESD stronger than ABS?
Yes. PEEK-ESD has a typical yield strength of 88 MPa (12.8 ksi) against 42 MPa (6.09 ksi) for ABS — about 110% more. Tensile strength is 90 MPa (13.1 ksi) vs 43 MPa (6.24 ksi).
Which is cheaper, ABS or PEEK-ESD?
ABS is the lower-cost material: it sits in the budget tier ($) while PEEK-ESD is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, ABS or PEEK-ESD?
ABS. Its machinability rates very good (80/100) against good (60/100) for PEEK-ESD; for welding the order is ABS first (very good, 78/100) then PEEK-ESD (fair, 40/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in ABS and PEEK-ESD side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.