Stainless Steel 1.4482 CW-1/4H
Supply condition
EN 1.4482 · UNS S82011, S32001
CW-1/4H = cold worked, quarter hard temper rolled strip
Temper-rolled strip for spring-back-tolerant formed parts and weight-critical structures needing extra proof strength.
Values for the CW-1/4H condition
Other 1.4482 tempers and conditions
1.4482 is listed in 4 conditions; see the grade overview at 1.4482.
Compare all 4 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
As-welded deposit | Reference condition for design of welded fabrications; ferrite balance and heat input govern toughness and corrosion. | 520 | 700 | 22 | 24 HRC | 2.2 % IACS |
Hot Rolled, solution annealed and pickled | Choose for plate and heavy strip (roughly 3–25 mm) for tanks, structures and weldments where surface finish is secondary. | 530 | 720 | 32 | 21 HRC | — |
CR-2BDefault Cold Rolled, solution annealed and pickled | Standard stocked condition for sheet and thin strip up to about 6 mm; best surface and tightest thickness tolerance. | 560 | 740 | 28 | 22 HRC | — |
CW-1/4HThis page Cold worked, quarter hard temper rolled strip | Temper-rolled strip for spring-back-tolerant formed parts and weight-critical structures needing extra proof strength. | 750 | 900 | 15 | 31 HRC | 2.2 % IACS |
What is 1.4482 CW-1/4H?
1.4482 CW-1/4H is 1.4482 supplied in the CW-1/4H condition — temper-rolled strip for spring-back-tolerant formed parts and weight-critical structures needing extra proof strength. 1.4482 CW-1/4H has a yield strength of 750 MPa (109 ksi) and a tensile strength of 900 MPa (131 ksi) — stronger than 93% of stainless steel grades. Elongation at break is 15% and the elastic modulus is 200 GPa (29 Msi). 1.4482 CW-1/4H has a density of 7.75 g/cm³ (0.28 lb/in³), lighter than 65% of stainless steel grades. It melts at 1,420°C (2,588 °F). CR-2B is the default condition FabDigit quotes; CW-1/4H is available on request or by drawing note.
Advantages
- High strength — 750 MPa (109 ksi), better than 93% of stainless steel grades
- Low embodied carbon — 3.6 kg CO₂/kg, better than 83% of stainless steel grades
Limitations
- Limited service temperature — 200°C (392 °F), worse than 100% of stainless steel grades
- Limited ductility — 15%, worse than 89% of stainless steel grades
- Low fracture toughness — 80 MPa·√m (72.8 ksi·√in), worse than 79% of stainless steel grades
1.4482 CW-1/4H properties
Typical room-temperature values for 1.4482 CW-1/4H; 23 are specific to this condition. Other listed values are 1.4482 reference data and may not represent this condition. Bars are the position among stainless steel grades.
Physical3
1.4482 CW-1/4H has a density of 7.75 g/cm³ (0.28 lb/in³), lighter than 65% of stainless steel grades. It melts at 1,420°C (2,588 °F).
Mechanical17
1.4482 CW-1/4H has a yield strength of 750 MPa (109 ksi) and a tensile strength of 900 MPa (131 ksi) — stronger than 93% of stainless steel grades. Elongation at break is 15% and the elastic modulus is 200 GPa (29 Msi).
Thermal6
1.4482 CW-1/4H is rated for continuous service to 200°C (392 °F). It conducts heat at 15 W/m·K (8.67 BTU/hr·ft·°F), worse than 59% of stainless steel grades. Thermal expansion is 13 µm/m·K (7.22 µin/in·°F).
Electrical3
1.4482 CW-1/4H conducts electricity at 2.2 % IACS, worse than 61% of stainless steel grades.
Chemical & Environmental3
Corrosion resistance is good (60/100), worse than 58% of stainless steel grades.
Sustainability4
Producing a kilogram of 1.4482 CW-1/4H takes about 52 MJ of energy and emits 3.6 kg of CO₂ — less than 76% of stainless steel grades. Typical recycled content is 70%.
Manufacturability8
1.4482 CW-1/4H's machinability is poor (33/100, worse than 57% of stainless steel grades); weldability good (60/100); formability fair (35/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with 1.4482 CW-1/4H
Is 1.4482 easy to machine?
Machines like other duplex grades: high cutting forces and work hardening — use rigid setups, sharp coated carbide, positive rake, generous feed and flood coolant; avoid dwelling.
Can 1.4482 be welded?
Weld with GTAW/GMAW/SMAW using 2209-type or matching lean-duplex filler, no preheat, interpass below ~150 °C and controlled heat input (roughly 0.5–2.0 kJ/mm) to keep ferrite near 35–60 %; do not autogenously weld thick sections.
Can 1.4482 be formed, bent or molded?
Cold forms well but needs 1.5–2× the press force and larger bend radii/overbend than 304; hot working 1000–1150 °C followed by full solution anneal 1000–1080 °C and rapid water quench.
What surface finishes work on 1.4482?
Pickle and passivate after hot work or welding to restore the passive film; electropolishing or mechanical polishing to No.4/mirror is straightforward, but never anodize.
1.4482 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Clow carbon for weldability | ≤ 0.03 | 0.02 |
| Si | ≤ 1 | 0.5 |
| Mnaustenite stabiliser replacing Ni | 4 – 6 | 5 |
| P | ≤ 0.04 | 0.03 |
| S | ≤ 0.03 | 0 |
| Cr | 19.5 – 21.5 | 20.5 |
| Nilean nickel content | 1.5 – 3.5 | 2.2 |
| Moraises PREN vs 1.4162 | 0.1 – 0.6 | 0.3 |
| Nstrengthens and stabilises austenite | 0.05 – 0.2 | 0.15 |
| Fe | balance | — |
1.4482 CW-1/4H — frequently asked
What is 1.4482 CW-1/4H used for?
1.4482 CW-1/4H is typically used for structural tanks, transportation equipment and water treatment structures. In short: lean duplex, low nickel; best-forming duplex grade; lower corrosion than 2205.
What is the yield strength of 1.4482 CW-1/4H?
1.4482 CW-1/4H has a typical yield strength of 750 MPa (109 ksi) and a tensile strength of 900 MPa (131 ksi) — stronger than 93% of stainless steel grades. Strength varies by condition: see the 4 listed tempers.
Is 1.4482 CW-1/4H easy to machine?
Not especially — machinability is rated poor (33/100, worse than 57% of stainless steel grades). Machines like other duplex grades: high cutting forces and work hardening — use rigid setups, sharp coated carbide, positive rake, generous feed and flood coolant; avoid dwelling.
Can 1.4482 CW-1/4H be welded?
Yes — weldability is rated good (60/100). Weld with GTAW/GMAW/SMAW using 2209-type or matching lean-duplex filler, no preheat, interpass below ~150 °C and controlled heat input (roughly 0.5–2.0 kJ/mm) to keep ferrite near 35–60 %; do not autogenously weld thick sections.
What surface finishes work on 1.4482 CW-1/4H?
Pickle and passivate after hot work or welding to restore the passive film; electropolishing or mechanical polishing to No.4/mirror is straightforward, but never anodize.
Can 1.4482 CW-1/4H be formed, bent or molded?
Cold forms well but needs 1.5–2× the press force and larger bend radii/overbend than 304; hot working 1000–1150 °C followed by full solution anneal 1000–1080 °C and rapid water quench.
What is the maximum service temperature of 1.4482 CW-1/4H?
1.4482 CW-1/4H is rated for continuous use to about 200°C (392 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between 1.4482 CR-2B and 1.4482-AW?
CR-2B is the default condition — standard stocked condition for sheet and thin strip up to about 6 mm; best surface and tightest thickness tolerance. AW: reference condition for design of welded fabrications; ferrite balance and heat input govern toughness and corrosion. Yield strength is 560 MPa in CR-2B versus 520 MPa in AW.
Sources
- EN 10088-1/-2 Stainless steels — list of grades and technical delivery conditions for sheet/plate/strip — CEN (2014)
- EN 10028-7 Flat products of steels for pressure purposes — stainless steels — CEN (2016)
- ASTM A240/A240M (UNS S82011 lean duplex) — ASTM International (2022)
- ASM Handbook Vol.1 — Properties and Selection: Irons, Steels and High-Performance Alloys — ASM International (1990)
- Lean duplex stainless steel product datasheets — Outokumpu / Aperam (2023)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.