PLLA SC
Finish state
SC = stereocomplex PLLA/PDLA blend
Blend with PDLA to form the stereocomplex crystal — melting point jumps to ~220–230 °C for the highest heat resistance available from PLA chemistry.
Values for the SC condition
Other PLLA grades and fills
PLLA is listed in 8 conditions; see the grade overview at PLLA.
Compare all 8 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
Foamed / expanded PLLA | Physically blown biobased foam for protective packaging and insulation where low density matters more than strength. | — | 0.6 | 8 | — |
Impact-modified / toughened PLLA | Core-shell or bio-elastomer toughened compound for drop-resistant housings and durable goods, at the cost of stiffness and clarity. | 42 | 45 | 120 | 72 Shore D |
Flame-retardant PLLA | Phosphorus/nitrogen FR compound for electronics housings and appliance parts that must meet UL 94 V-0. | 44 | 45 | 2.5 | 82 Shore D |
20% talc / mineral-filled PLLA | Cost-down, faster-crystallizing compound for rigid packaging and thermoformed trays with improved heat resistance. | 47 | 48 | 2.5 | 85 Shore D |
Nucleated fast-crystallizing PLLA | Pick for injection moulding with short cycles when a crystalline, heat-resistant part is needed straight out of the tool. | 58 | 60 | 3 | 84 Shore D |
Annealed / crystallized PLLA | Choose when the part must survive hot-fill, dishwasher or ~90–110 °C air service: crystallinity is developed by hot mold or post-mold annealing. | — | 68 | 3 | — |
SCThis page Stereocomplex PLLA/PDLA blend | Blend with PDLA to form the stereocomplex crystal — melting point jumps to ~220–230 °C for the highest heat resistance available from PLA chemistry. | 68 | 70 | 5 | 85 Shore D |
30% glass-fiber reinforced PLLA | For structural biobased parts needing high stiffness and dimensional stability; must be moulded hot/annealed to exploit the heat resistance. | — | 100 | 2 | — |
What is PLLA SC?
PLLA SC is PLLA supplied in the SC condition — blend with PDLA to form the stereocomplex crystal — melting point jumps to ~220–230 °C for the highest heat resistance available from PLA chemistry. PLLA SC has a yield strength of 68 MPa (9.86 ksi) and a tensile strength of 70 MPa (10.2 ksi) — stronger than 77% of polymer grades. Elongation at break is 5% and the elastic modulus is 4 GPa (0.58 Msi). PLLA SC has a density of 1.26 g/cm³ (0.0455 lb/in³), heavier than 66% of polymer grades. Its glass-transition temperature is 65°C (149 °F).
Advantages
- Low embodied carbon — 1.3 kg CO₂/kg, better than 100% of polymer grades
- Stiff — 4 GPa (0.58 Msi), better than 86% of polymer grades
- High strength — 68 MPa (9.86 ksi), better than 77% of polymer grades
- Polishes to a fine finish — 70/100, better than 77% of polymer grades
Limitations
- Needs corrosion protection — 58/100, worse than 92% of polymer grades
PLLA SC properties
Typical room-temperature values for PLLA SC; 28 are specific to this condition. Other listed values are PLLA reference data and may not represent this condition. Bars are the position among polymer grades.
Physical7
PLLA SC has a density of 1.26 g/cm³ (0.0455 lb/in³), heavier than 66% of polymer grades. Its glass-transition temperature is 65°C (149 °F).
Mechanical15
PLLA SC has a yield strength of 68 MPa (9.86 ksi) and a tensile strength of 70 MPa (10.2 ksi) — stronger than 77% of polymer grades. Elongation at break is 5% and the elastic modulus is 4 GPa (0.58 Msi).
Thermal11
PLLA SC is rated for continuous service to 120°C (248 °F). It conducts heat at 0.18 W/m·K (0.104 BTU/hr·ft·°F), worse than 73% of polymer grades. Thermal expansion is 75 µm/m·K (41.7 µin/in·°F).
Electrical6
PLLA SC is an electrical insulator with a dielectric strength of 18 kV/mm (457.2 V/mil) and a resistivity of 1×10¹⁴ Ω·m.
Chemical & Environmental3
Corrosion resistance is good (58/100), worse than 92% of polymer grades. UV resistance is fair.
Sustainability3
Producing a kilogram of PLLA SC takes about 50 MJ of energy and emits 1.3 kg of CO₂ — less than 99% of polymer grades. Typical recycled content is 0%.
Manufacturability8
PLLA SC's machinability is good (58/100, worse than 55% of polymer grades); weldability good (60/100); formability poor (22/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with PLLA SC
Is PLLA easy to machine?
Machines like acrylic with sharp, high-rake tools and air blast — keep speeds moderate and avoid coolant soak, since frictional heat above 60 °C softens the part and hot water accelerates hydrolysis.
Can PLLA be welded?
Ultrasonic, hot-plate, vibration and laser welding all work well; solvent bonding with chloroform/dichloromethane or cyanoacrylate gives strong joints on non-crystalline surfaces.
Can PLLA be formed, bent or molded?
Dry to <250 ppm (4 h at 80 °C, or 45 °C for high-IV medical resin) before processing to prevent hydrolytic molecular-weight loss; mould at 190–220 °C melt with a cold tool (20–30 °C) for clear amorphous parts or 100–110 °C plus nucleant for crystallized heat-resistant parts; thermoforming window is narrow just above Tg.
What surface finishes work on PLLA?
Takes printing, hot stamping and vacuum metallizing after corona/plasma treatment; can be vapour-smoothed or solvent-polished, but avoid alkaline cleaners and steam sterilization (use EO or e-beam/gamma with dose control).
PLLA chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| D-isomer (D-lactide) content<1–2 % for high-crystallinity / medical PLLA; higher D lowers Tm and crystallinity | 0 – 4 | 1 |
| residual lactide monomertypically <0.1 % in medical grades | 0 – 0.5 | 0.1 |
| Sn (tin octoate catalyst residue)limited to low ppm in implant grades | 0 – 0.02 | 0.01 |
| L-lactic acid repeat unit (poly L-lactidring-opening polymerisation of L-lactide from fermented plant sugar | ≥ 96 (balance) | — |
PLLA SC — frequently asked
What is PLLA SC used for?
PLLA SC is typically used for surgical sutures, bone fixation screws/pins, biodegradable textile fiber, rigid food packaging and high-heat 3D printing filament. In short: highest-heat PLA grade; medical resorbable standard; brittle, hydrolysis sensitive.
What is the yield strength of PLLA SC?
PLLA SC has a typical yield strength of 68 MPa (9.86 ksi) and a tensile strength of 70 MPa (10.2 ksi) — stronger than 77% of polymer grades. Strength varies by condition: see the 8 listed tempers.
Is PLLA SC easy to machine?
Reasonably — machinability is rated good (58/100, worse than 55% of polymer grades). Machines like acrylic with sharp, high-rake tools and air blast — keep speeds moderate and avoid coolant soak, since frictional heat above 60 °C softens the part and hot water accelerates hydrolysis.
Can PLLA SC be welded?
Yes — weldability is rated good (60/100). Ultrasonic, hot-plate, vibration and laser welding all work well; solvent bonding with chloroform/dichloromethane or cyanoacrylate gives strong joints on non-crystalline surfaces.
What surface finishes work on PLLA SC?
Takes printing, hot stamping and vacuum metallizing after corona/plasma treatment; can be vapour-smoothed or solvent-polished, but avoid alkaline cleaners and steam sterilization (use EO or e-beam/gamma with dose control).
Can PLLA SC be formed, bent or molded?
Dry to <250 ppm (4 h at 80 °C, or 45 °C for high-IV medical resin) before processing to prevent hydrolytic molecular-weight loss; mould at 190–220 °C melt with a cold tool (20–30 °C) for clear amorphous parts or 100–110 °C plus nucleant for crystallized heat-resistant parts; thermoforming window is narrow just above Tg.
What is the maximum service temperature of PLLA SC?
PLLA SC is rated for continuous use to about 120°C (248 °F), and briefly to 80°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- Luminy L-series high heat PLA resin data sheets — TotalEnergies Corbion (2023)
- Purasorb PL / PLLA bioresorbable polymer data sheets — Corbion (2022)
- RESOMER L series (poly L-lactide) product information — Evonik (2022)
- Ingeo Biopolymer technical data sheets and processing guides — NatureWorks (2023)
- ISO 527-2 / ISO 178 / ISO 75 / ISO 306 plastics test methods — ISO (2019)
- ASTM F1925 Standard Specification for Semi-Crystalline Poly(lactide) Polymer and Copolymer Resins for Surgical Implants — ASTM (2022)
- Poly(lactic acid): Synthesis, Structures, Properties, Processing and Applications — Wiley (2010)
- CAMPUS / typical PLA compound datasheets — CWFG (2023)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.