PLLA GF30
Reinforced grade
GF30 = 30% glass-fiber reinforced PLLA
For structural biobased parts needing high stiffness and dimensional stability; must be moulded hot/annealed to exploit the heat resistance.
Values for the GF30 condition
Other PLLA grades and fills
PLLA is listed in 8 conditions; see the grade overview at PLLA.
Compare all 8 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
Foamed / expanded PLLA | Physically blown biobased foam for protective packaging and insulation where low density matters more than strength. | — | 0.6 | 8 | — |
Impact-modified / toughened PLLA | Core-shell or bio-elastomer toughened compound for drop-resistant housings and durable goods, at the cost of stiffness and clarity. | 42 | 45 | 120 | 72 Shore D |
Flame-retardant PLLA | Phosphorus/nitrogen FR compound for electronics housings and appliance parts that must meet UL 94 V-0. | 44 | 45 | 2.5 | 82 Shore D |
20% talc / mineral-filled PLLA | Cost-down, faster-crystallizing compound for rigid packaging and thermoformed trays with improved heat resistance. | 47 | 48 | 2.5 | 85 Shore D |
Nucleated fast-crystallizing PLLA | Pick for injection moulding with short cycles when a crystalline, heat-resistant part is needed straight out of the tool. | 58 | 60 | 3 | 84 Shore D |
Annealed / crystallized PLLA | Choose when the part must survive hot-fill, dishwasher or ~90–110 °C air service: crystallinity is developed by hot mold or post-mold annealing. | — | 68 | 3 | — |
Stereocomplex PLLA/PDLA blend | Blend with PDLA to form the stereocomplex crystal — melting point jumps to ~220–230 °C for the highest heat resistance available from PLA chemistry. | 68 | 70 | 5 | 85 Shore D |
GF30This page 30% glass-fiber reinforced PLLA | For structural biobased parts needing high stiffness and dimensional stability; must be moulded hot/annealed to exploit the heat resistance. | — | 100 | 2 | — |
What is PLLA GF30?
PLLA GF30 is PLLA in the GF30 grade — for structural biobased parts needing high stiffness and dimensional stability; must be moulded hot/annealed to exploit the heat resistance. PLLA GF30 has a yield strength of 60 MPa (8.7 ksi) and a tensile strength of 100 MPa (14.5 ksi) — stronger than 69% of polymer grades. Elongation at break is 2% and the elastic modulus is 9 GPa (1.31 Msi). PLLA GF30 has a density of 1.45 g/cm³ (0.0524 lb/in³), heavier than 86% of polymer grades. Its glass-transition temperature is 61°C (142 °F).
Advantages
- Low embodied carbon — 1.3 kg CO₂/kg, better than 100% of polymer grades
- Stiff — 9 GPa (1.31 Msi), better than 93% of polymer grades
- Low, predictable mold shrinkage — 0.25%, better than 93% of polymer grades
- Readily welded — 75/100, better than 82% of polymer grades
- Polishes to a fine finish — 70/100, better than 77% of polymer grades
Limitations
- Limited ductility — 2%, worse than 95% of polymer grades
- Needs corrosion protection — 55/100, worse than 94% of polymer grades
- Heavy — 1.45 g/cm³ (0.0524 lb/in³), worse than 86% of polymer grades
- Poor heat conductor — 0.16 W/m·K (0.0924 BTU/hr·ft·°F), worse than 78% of polymer grades
- Difficult to machine — 45/100, worse than 78% of polymer grades
PLLA GF30 properties
Typical room-temperature values for PLLA GF30; 13 are specific to this condition. Other listed values are PLLA reference data and may not represent this condition. Bars are the position among polymer grades.
Physical7
PLLA GF30 has a density of 1.45 g/cm³ (0.0524 lb/in³), heavier than 86% of polymer grades. Its glass-transition temperature is 61°C (142 °F).
Mechanical15
PLLA GF30 has a yield strength of 60 MPa (8.7 ksi) and a tensile strength of 100 MPa (14.5 ksi) — stronger than 69% of polymer grades. Elongation at break is 2% and the elastic modulus is 9 GPa (1.31 Msi).
Thermal11
PLLA GF30 is rated for continuous service to 110°C (230 °F). It conducts heat at 0.16 W/m·K (0.0924 BTU/hr·ft·°F), worse than 78% of polymer grades. Thermal expansion is 30 µm/m·K (16.7 µin/in·°F).
Electrical6
PLLA GF30 is an electrical insulator with a dielectric strength of 18 kV/mm (457.2 V/mil) and a resistivity of 1×10¹⁴ Ω·m.
Chemical & Environmental3
Corrosion resistance is good (55/100), worse than 94% of polymer grades. UV resistance is fair.
Sustainability3
Producing a kilogram of PLLA GF30 takes about 50 MJ of energy and emits 1.3 kg of CO₂ — less than 99% of polymer grades. Typical recycled content is 0%.
Manufacturability8
PLLA GF30's machinability is fair (45/100, worse than 78% of polymer grades); weldability very good (75/100); formability good (55/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with PLLA GF30
Is PLLA easy to machine?
Machines like acrylic with sharp, high-rake tools and air blast — keep speeds moderate and avoid coolant soak, since frictional heat above 60 °C softens the part and hot water accelerates hydrolysis.
Can PLLA be welded?
Ultrasonic, hot-plate, vibration and laser welding all work well; solvent bonding with chloroform/dichloromethane or cyanoacrylate gives strong joints on non-crystalline surfaces.
Can PLLA be formed, bent or molded?
Dry to <250 ppm (4 h at 80 °C, or 45 °C for high-IV medical resin) before processing to prevent hydrolytic molecular-weight loss; mould at 190–220 °C melt with a cold tool (20–30 °C) for clear amorphous parts or 100–110 °C plus nucleant for crystallized heat-resistant parts; thermoforming window is narrow just above Tg.
What surface finishes work on PLLA?
Takes printing, hot stamping and vacuum metallizing after corona/plasma treatment; can be vapour-smoothed or solvent-polished, but avoid alkaline cleaners and steam sterilization (use EO or e-beam/gamma with dose control).
PLLA chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| D-isomer (D-lactide) content<1–2 % for high-crystallinity / medical PLLA; higher D lowers Tm and crystallinity | 0 – 4 | 1 |
| residual lactide monomertypically <0.1 % in medical grades | 0 – 0.5 | 0.1 |
| Sn (tin octoate catalyst residue)limited to low ppm in implant grades | 0 – 0.02 | 0.01 |
| L-lactic acid repeat unit (poly L-lactidring-opening polymerisation of L-lactide from fermented plant sugar | ≥ 96 (balance) | — |
PLLA GF30 — frequently asked
What is PLLA GF30 used for?
PLLA GF30 is typically used for surgical sutures, bone fixation screws/pins, biodegradable textile fiber, rigid food packaging and high-heat 3D printing filament. In short: highest-heat PLA grade; medical resorbable standard; brittle, hydrolysis sensitive.
What is the yield strength of PLLA GF30?
PLLA GF30 has a typical yield strength of 60 MPa (8.7 ksi) and a tensile strength of 100 MPa (14.5 ksi) — stronger than 69% of polymer grades. Strength varies by condition: see the 8 listed tempers.
Is PLLA GF30 easy to machine?
Reasonably — machinability is rated fair (45/100, worse than 78% of polymer grades). Machines like acrylic with sharp, high-rake tools and air blast — keep speeds moderate and avoid coolant soak, since frictional heat above 60 °C softens the part and hot water accelerates hydrolysis.
Can PLLA GF30 be welded?
Yes — weldability is rated very good (75/100). Ultrasonic, hot-plate, vibration and laser welding all work well; solvent bonding with chloroform/dichloromethane or cyanoacrylate gives strong joints on non-crystalline surfaces.
What surface finishes work on PLLA GF30?
Takes printing, hot stamping and vacuum metallizing after corona/plasma treatment; can be vapour-smoothed or solvent-polished, but avoid alkaline cleaners and steam sterilization (use EO or e-beam/gamma with dose control).
Can PLLA GF30 be formed, bent or molded?
Dry to <250 ppm (4 h at 80 °C, or 45 °C for high-IV medical resin) before processing to prevent hydrolytic molecular-weight loss; mould at 190–220 °C melt with a cold tool (20–30 °C) for clear amorphous parts or 100–110 °C plus nucleant for crystallized heat-resistant parts; thermoforming window is narrow just above Tg.
What is the maximum service temperature of PLLA GF30?
PLLA GF30 is rated for continuous use to about 110°C (230 °F), and briefly to 80°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- Luminy L-series high heat PLA resin data sheets — TotalEnergies Corbion (2023)
- Purasorb PL / PLLA bioresorbable polymer data sheets — Corbion (2022)
- RESOMER L series (poly L-lactide) product information — Evonik (2022)
- Ingeo Biopolymer technical data sheets and processing guides — NatureWorks (2023)
- ISO 527-2 / ISO 178 / ISO 75 / ISO 306 plastics test methods — ISO (2019)
- ASTM F1925 Standard Specification for Semi-Crystalline Poly(lactide) Polymer and Copolymer Resins for Surgical Implants — ASTM (2022)
- Poly(lactic acid): Synthesis, Structures, Properties, Processing and Applications — Wiley (2010)
- CAMPUS / typical PLA compound datasheets — CWFG (2023)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.