TPO Foam D25
Grade
D25 = 25 kg/m³
Pick for light cushion packaging and void-fill where softness matters more than load bearing.
Values for the D25 condition
Other TPO Foam grades and fills
TPO Foam is listed in 10 conditions; see the grade overview at TPO Foam.
Compare all 10 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
33 kg/m³ | Common roll-goods density for interior trim backing and soft gasketing. | 0.13 | 0.28 | 140 | 16 Shore A |
D25This page 25 kg/m³ | Pick for light cushion packaging and void-fill where softness matters more than load bearing. | — | 0.2 | 120 | 12 Shore A |
60 kg/m³ | Use when the part must resist thermoforming stretch and carry higher gasket sealing loads. | 0.24 | 0.5 | 170 | 25 Shore A |
Non-crosslinked extruded foam | Lowest-cost route for packaging and protective sheet; coarser cells, higher set, fully re-extrudable scrap. | — | 0.28 | 130 | 18 Shore A |
Flame-retardant grade | Choose where interior/rail/electrical burn tests (FMVSS 302, UL 94 HF-1) must be passed. | — | 0.3 | 120 | 24 Shore A |
80 kg/m³ | Choose for repeated-impact pads, deep-draw thermoformed laminates and structural gaskets. | 0.34 | 0.7 | 180 | 30 Shore A |
D45Default 45 kg/m³ | Default all-round density: soft touch with usable load bearing for IP/door-trim laminates and sealing. | — | 0.35 | 150 | 20 Shore A |
Chemically/electron-beam crosslinked sheet | Specify crosslinked TPO foam when fine uniform cells, good thermoformability and low compression set are needed. | — | 0.4 | 170 | 22 Shore A |
100 kg/m³ | Pick for load-bearing spacers, anti-squeak/rattle pads and NVH parts needing firm resilience. | 0.45 | 0.9 | 190 | 35 Shore A |
Moldable expanded TPO bead foam | Use steam-chest molded bead foam for 3D energy-absorbing parts softer and more elastic than EPP. | — | 0.45 | 60 | 28 Shore A |
What is TPO Foam D25?
TPO Foam D25 is TPO Foam in the D25 grade — pick for light cushion packaging and void-fill where softness matters more than load bearing. TPO Foam D25 has a tensile strength of 0.2 MPa (0.029 ksi), weaker than 96% of polymer grades. Elongation at break is 120% and the elastic modulus is 5×10⁻⁴ GPa (7.25×10⁻⁵ Msi). TPO Foam D25 has a density of 0.03 g/cm³ (9.03×10⁻⁴ lb/in³), lighter than 96% of polymer grades. Its glass-transition temperature is -50°C (-58 °F). D45 is the default condition FabDigit quotes; D25 is available on request or by drawing note.
Advantages
- Lightweight — 0.03 g/cm³ (9.03×10⁻⁴ lb/in³), better than 96% of polymer grades
- Forms and bends easily — 85/100, better than 81% of polymer grades
Limitations
- Low stiffness — 5×10⁻⁴ GPa (7.25×10⁻⁵ Msi), worse than 98% of polymer grades
- Poor heat conductor — 0.04 W/m·K (0.0202 BTU/hr·ft·°F), worse than 93% of polymer grades
TPO Foam D25 properties
Typical room-temperature values for TPO Foam D25; 10 are specific to this condition. Other listed values are TPO Foam reference data and may not represent this condition. Bars are the position among polymer grades.
Physical4
TPO Foam D25 has a density of 0.03 g/cm³ (9.03×10⁻⁴ lb/in³), lighter than 96% of polymer grades. Its glass-transition temperature is -50°C (-58 °F).
Mechanical9
TPO Foam D25 has a tensile strength of 0.2 MPa (0.029 ksi), weaker than 96% of polymer grades. Elongation at break is 120% and the elastic modulus is 5×10⁻⁴ GPa (7.25×10⁻⁵ Msi).
Thermal8
TPO Foam D25 is rated for continuous service to 90°C (194 °F). It conducts heat at 0.04 W/m·K (0.0202 BTU/hr·ft·°F), worse than 93% of polymer grades. Thermal expansion is 150 µm/m·K (83.3 µin/in·°F).
Electrical4
TPO Foam D25 has an electrical resistivity of 1×10¹³ Ω·m.
Chemical & Environmental3
Corrosion resistance is excellent (88/100), better than 74% of polymer grades. UV resistance is fair.
Sustainability4
Producing a kilogram of TPO Foam D25 takes about 95 MJ of energy and emits 3.6 kg of CO₂ — less than 70% of polymer grades. Typical recycled content is 5%.
Manufacturability6
TPO Foam D25's machinability is good (60/100, better than 51% of polymer grades); weldability very good (70/100); formability excellent (85/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with TPO Foam D25
Is TPO Foam easy to machine?
Die cutting, kiss-cut, hot-wire, oscillating blade or waterjet all work; avoid conventional milling which smears and melts the cell walls.
Can TPO Foam be welded?
Joins by hot-air/impulse/ultrasonic welding to itself and to TPO skins; adhesives require flame, corona or plasma pretreatment because of the low-energy surface.
Can TPO Foam be formed, bent or molded?
Crosslinked sheet vacuum/press-forms at roughly 140–170 °C surface temperature; bead grades are steam-chest molded, non-crosslinked grades are extruded at about 175–215 °C melt.
What surface finishes work on TPO Foam?
Cannot be painted or plated as a foam; use flame lamination, PSA transfer tape, textile/TPO skin lamination or embossing for the visible surface.
TPO Foam chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| polypropylene (PP homo/copolymer)matrix phase | 45 – 75 | 60 |
| olefin elastomer (EPR/EPDM/POE)provides rubber-like softness and low-temperature flexibility | 20 – 50 | 33 |
| chemical blowing agent + crosslinker resomitted in physically (CO2/N2) foamed grades | 1 – 5 | 3 |
| talc / nucleant, antioxidant, UV & proce | 1 – 5 | 2 |
| flame retardant (FR grades only)ATH/phosphorus or brominated systems | 0 – 20 | 0 |
TPO Foam D25 — frequently asked
What is TPO Foam D25 used for?
TPO Foam D25 is typically used for automotive interior soft-touch padding, footwear midsole components, sporting goods cushioning, gasketing and protective sleeves. In short: softer than EPP; rubber-like closed-cell olefin; weldable to TPO skins.
What is the tensile strength of TPO Foam D25?
TPO Foam D25 has a typical tensile strength of 0.2 MPa (0.029 ksi) — weaker than 96% of polymer grades. Strength varies by condition: see the 10 listed tempers.
Is TPO Foam D25 easy to machine?
Reasonably — machinability is rated good (60/100, better than 51% of polymer grades). Die cutting, kiss-cut, hot-wire, oscillating blade or waterjet all work; avoid conventional milling which smears and melts the cell walls.
Can TPO Foam D25 be welded?
Yes — weldability is rated very good (70/100). Joins by hot-air/impulse/ultrasonic welding to itself and to TPO skins; adhesives require flame, corona or plasma pretreatment because of the low-energy surface.
What surface finishes work on TPO Foam D25?
Cannot be painted or plated as a foam; use flame lamination, PSA transfer tape, textile/TPO skin lamination or embossing for the visible surface.
Can TPO Foam D25 be formed, bent or molded?
Crosslinked sheet vacuum/press-forms at roughly 140–170 °C surface temperature; bead grades are steam-chest molded, non-crosslinked grades are extruded at about 175–215 °C melt.
What is the maximum service temperature of TPO Foam D25?
TPO Foam D25 is rated for continuous use to about 90°C (194 °F), and briefly to 120°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between TPO Foam D45 and TPO Foam D100?
D45 is the default condition — default all-round density: soft touch with usable load bearing for IP/door-trim laminates and sealing. D100: pick for load-bearing spacers, anti-squeak/rattle pads and NVH parts needing firm resilience.
Sources
- ASTM D3575 — Flexible Cellular Materials Made from Olefin Polymers — ASTM International (2020)
- UL 94 — Tests for Flammability of Plastic Materials (HBF/HF-1 foam categories) — UL (2021)
- Crosslinked polyolefin foam sheet product ranges (Alveolit/Alveolux type) — Sekisui Alveo (2023)
- Azote / Plastazote polyolefin foam technical data — Zotefoams (2023)
- Engineered Materials Handbook Vol. 2: Engineering Plastics (cellular polymers) — ASM International (1988)
- Polyolefin foam and TPO compound property records — CAMPUS / UL Prospector (2024)
- TPO/POE — 1688 / SMM (2025)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.