RTPU GF30
Reinforced grade
also Isoplast
GF30 = 30 % glass-fibre reinforced
Highest stiffness and strength grade; pick for metal-replacement structural parts where impact demand is moderate.
Values for the GF30 condition
Other RTPU grades and fills
RTPU is listed in 6 conditions; see the grade overview at RTPU.
Compare all 6 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
Flame-retardant (UL 94 V-0) grade | Use for electrical enclosures, connectors and rail/transport parts needing V-0 at 1.5–3 mm; slight loss of impact and elongation. | 46 | 50 | 80 | 79 Shore D |
ESD / antistatic compounded grade | Carbon-black or permanent-antistat filled compound for tool housings and handling parts needing static dissipation. | 47 | 50 | 50 | 80 Shore D |
Hydrolysis / chemical-resistance stabilised grade | Polyether or carbodiimide-stabilised chemistry for hot-water, humid or fuel/oil-contact service (e.g. oilfield and plumbing parts). | 50 | 55 | 160 | 76 Shore D |
10 % glass-fibre reinforced | Mild stiffening step that keeps useful ductility and impact strength; good for housings needing better creep resistance. | — | 72 | 25 | — |
20 % glass-fibre reinforced | Balanced stiffness/toughness reinforcement for load-bearing brackets and pressurised fittings. | — | 95 | 8 | — |
GF30This page 30 % glass-fibre reinforced | Highest stiffness and strength grade; pick for metal-replacement structural parts where impact demand is moderate. | — | 115 | 5 | — |
What is RTPU GF30?
RTPU GF30 is RTPU in the GF30 grade — highest stiffness and strength grade; pick for metal-replacement structural parts where impact demand is moderate. RTPU GF30 has a yield strength of 52 MPa (7.54 ksi) and a tensile strength of 115 MPa (16.7 ksi) — stronger than 56% of polymer grades. Elongation at break is 5% and the elastic modulus is 8 GPa (1.16 Msi). RTPU GF30 has a density of 1.43 g/cm³ (0.0517 lb/in³), heavier than 84% of polymer grades. Its glass-transition temperature is 100°C (212 °F).
Advantages
- Low, predictable mold shrinkage — 0.2%, better than 94% of polymer grades
- Stiff — 8 GPa (1.16 Msi), better than 91% of polymer grades
Limitations
- Heavy — 1.43 g/cm³ (0.0517 lb/in³), worse than 84% of polymer grades
- Difficult to machine — 45/100, worse than 78% of polymer grades
RTPU GF30 properties
Typical room-temperature values for RTPU GF30; 12 are specific to this condition. Other listed values are RTPU reference data and may not represent this condition. Bars are the position among polymer grades.
Physical6
RTPU GF30 has a density of 1.43 g/cm³ (0.0517 lb/in³), heavier than 84% of polymer grades. Its glass-transition temperature is 100°C (212 °F).
Mechanical13
RTPU GF30 has a yield strength of 52 MPa (7.54 ksi) and a tensile strength of 115 MPa (16.7 ksi) — stronger than 56% of polymer grades. Elongation at break is 5% and the elastic modulus is 8 GPa (1.16 Msi).
Thermal11
RTPU GF30 is rated for continuous service to 95°C (203 °F). It conducts heat at 0.2 W/m·K (0.116 BTU/hr·ft·°F), worse than 56% of polymer grades. Thermal expansion is 30 µm/m·K (16.7 µin/in·°F).
Electrical7
RTPU GF30 is an electrical insulator with a dielectric strength of 24 kV/mm (609.6 V/mil) and a resistivity of 1×10¹² Ω·m.
Chemical & Environmental3
Corrosion resistance is very good (80/100), worse than 52% of polymer grades. UV resistance is fair.
Sustainability4
Producing a kilogram of RTPU GF30 takes about 118 MJ of energy and emits 5.5 kg of CO₂ — more than 72% of polymer grades. Typical recycled content is 0%.
Manufacturability8
RTPU GF30's machinability is fair (45/100, worse than 78% of polymer grades); weldability very good (70/100); formability good (60/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with RTPU GF30
Is RTPU easy to machine?
Machines like tough PC: sharp positive-rake carbide tools, high speed with low feed and air/mist cooling to avoid gumming and stress whitening; anneal stock before tight-tolerance cuts.
Can RTPU be welded?
Joins well by ultrasonic, hot-plate, spin and RF welding, and bonds with polyurethane/cyanoacrylate or solvent-type adhesives after light abrasion.
Can RTPU be formed, bent or molded?
Dry pellets 2–4 h at 90–100 °C to <0.02 % moisture, mould at 200–235 °C melt / 20–60 °C tool with generous gates; sheet thermoforms near 150–170 °C.
What surface finishes work on RTPU?
Takes paint and PU topcoats readily after adhesion promoter; can be pad-printed, laser-marked, vacuum-metallised or textured — avoid strong ketone/chlorinated solvent cleaners.
RTPU chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| 4,4'-MDI (diphenylmethane diisocyanate hhigh hard-segment content gives rigidity | 45 – 65 | 55 |
| short-chain diol chain extender (1,4-but | 15 – 30 | 25 |
| additives (antioxidant, UV stabiliser, l | 0.2 – 2 | 0.8 |
| glass fiber0 in default unfilled grade; 10/20/30 % in GF variants | 0 – 30 | 0 |
| polyol soft segment (polyether PTMEG or polyether for hydrolysis resistance, polyester for oil/abrasion | ≥ 10 (balance) | — |
RTPU GF30 — frequently asked
What is RTPU GF30 used for?
RTPU GF30 is typically used for power tool housings, ski boots and sporting goods, automotive interior trim, medical device housings and industrial rollers. In short: stiffest thermoplastic polyurethane; tough chemical-resistant housings; PC-like rigidity, higher toughness.
What is the yield strength of RTPU GF30?
RTPU GF30 has a typical yield strength of 52 MPa (7.54 ksi) and a tensile strength of 115 MPa (16.7 ksi) — stronger than 56% of polymer grades. Strength varies by condition: see the 6 listed tempers.
Is RTPU GF30 easy to machine?
Reasonably — machinability is rated fair (45/100, worse than 78% of polymer grades). Machines like tough PC: sharp positive-rake carbide tools, high speed with low feed and air/mist cooling to avoid gumming and stress whitening; anneal stock before tight-tolerance cuts.
Can RTPU GF30 be welded?
Yes — weldability is rated very good (70/100). Joins well by ultrasonic, hot-plate, spin and RF welding, and bonds with polyurethane/cyanoacrylate or solvent-type adhesives after light abrasion.
What surface finishes work on RTPU GF30?
Takes paint and PU topcoats readily after adhesion promoter; can be pad-printed, laser-marked, vacuum-metallised or textured — avoid strong ketone/chlorinated solvent cleaners.
Can RTPU GF30 be formed, bent or molded?
Dry pellets 2–4 h at 90–100 °C to <0.02 % moisture, mould at 200–235 °C melt / 20–60 °C tool with generous gates; sheet thermoforms near 150–170 °C.
What is the maximum service temperature of RTPU GF30?
RTPU GF30 is rated for continuous use to about 95°C (203 °F), and briefly to 110°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Sources
- Isoplast Engineering Thermoplastic Polyurethane Resins — product and processing data — Lubrizol Engineered Polymers (2022)
- CAMPUS / UL Prospector rigid TPU (TPU-ARES/TPU-ARET) datasheets — CWFG / UL Solutions (2024)
- ASM Engineered Materials Handbook Vol. 2 — Engineering Plastics (polyurethanes) — ASM International (1988)
- ISO 527 / ISO 178 / ISO 75 / ASTM D256 test methods — ISO / ASTM (2019)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.