PA6T CF30
Reinforced grade
CF30 = 30 % carbon-fiber reinforced
Choose for highest specific stiffness, low warpage and static-dissipative surface at reduced weight vs glass.
Values for the CF30 condition
Other PA6T grades and fills
PA6T is listed in 14 conditions; see the grade overview at PA6T.
Compare all 14 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
Impact-modified / toughened | For snap fits, clips and cold-impact duty where the standard rigid PPA is too brittle. | 62 | 70 | 45 | 74 Shore D |
PA6T/M-5T copolymer | Copolymer using 2-methylpentamethylenediamine to depress Tm for easier processing while keeping high Tg and reflow resistance. | 90 | 95 | 25 | 85 Shore D |
PA6T/6I copolymer | Copolymer chemistry with isophthalic units for higher Tg, better surface gloss and lower moisture pickup; slower crystallization. | 92 | 95 | 12 | 86 Shore D |
UFDefault Unfilled / natural | Baseline unreinforced PPA for tough thin-wall parts, film/monofilament and as a base for compounding. | — | 100 | 20 | 95 HRM |
MF/GF-MF | Pick for flat, dimensionally isotropic parts and better surface appearance where peak strength is not required. | 115 | 115 | 2.5 | 88 Shore D |
15 % glass-fiber reinforced | Light reinforcement when some toughness and low warpage matter more than maximum stiffness. | — | 145 | 4 | — |
Internally lubricated (PTFE / silicone / graphite), often GF filled | Bearing/wear grade for hot dry-running bushings, gears and sliding contacts. | 155 | 155 | 2 | 87 Shore D |
ESD / conductive | For high-temperature ESD-safe fixtures, fuel-system parts and IC handling hardware. | 160 | 160 | 2 | 88 Shore D |
halogen-free flame-retardant, GF reinforced | Required for connectors/relay housings needing UL 94 V-0 at thin wall plus glow-wire performance. | — | 170 | 1.8 | — |
Heat-stabilized | Use for continuous 180–200 °C air aging (charge-air ducts, motor parts) where standard grades embrittle. | 195 | 195 | 2.4 | 90 Shore D |
30–33 % glass-fiber reinforced | The standard PPA grade for SMT connectors and under-hood parts needing lead-free reflow survival. | — | 200 | 2.5 | 105 HRM |
45 % glass-fiber reinforced | High-stiffness structural grade for metal replacement in hot, loaded brackets and housings. | — | 225 | 2 | — |
50 % glass-fiber reinforced | Maximum stiffness/creep resistance grade; most abrasive to tooling and hardest to fill in thin walls. | — | 240 | 1.8 | — |
CF30This page 30 % carbon-fiber reinforced | Choose for highest specific stiffness, low warpage and static-dissipative surface at reduced weight vs glass. | — | 245 | 1.6 | — |
What is PA6T CF30?
PA6T CF30 is PA6T in the CF30 grade — choose for highest specific stiffness, low warpage and static-dissipative surface at reduced weight vs glass. PA6T CF30 has a yield strength of 95 MPa (13.8 ksi) and a tensile strength of 245 MPa (35.5 ksi) — stronger than 93% of polymer grades. Elongation at break is 1.6% and the elastic modulus is 22 GPa (3.19 Msi). PA6T CF30 has a density of 1.34 g/cm³ (0.0484 lb/in³), heavier than 74% of polymer grades. Its glass-transition temperature is 125°C (257 °F). UF is the default condition FabDigit quotes; CF30 is available on request or by drawing note.
Advantages
- Stiff — 22 GPa (3.19 Msi), better than 100% of polymer grades
- Conducts heat well — 0.75 W/m·K (0.433 BTU/hr·ft·°F), better than 99% of polymer grades
- High strength — 95 MPa (13.8 ksi), better than 93% of polymer grades
- Low, predictable mold shrinkage — 0.25%, better than 93% of polymer grades
- High service temperature — 140°C (284 °F), better than 76% of polymer grades
Limitations
- Limited ductility — 1.6%, worse than 97% of polymer grades
- High embodied carbon — 8.5 kg CO₂/kg, worse than 85% of polymer grades
- Difficult to machine — 35/100, worse than 84% of polymer grades
PA6T CF30 properties
Typical room-temperature values for PA6T CF30; 13 are specific to this condition. Other listed values are PA6T reference data and may not represent this condition. Bars are the position among polymer grades.
Physical5
PA6T CF30 has a density of 1.34 g/cm³ (0.0484 lb/in³), heavier than 74% of polymer grades. Its glass-transition temperature is 125°C (257 °F).
Mechanical16
PA6T CF30 has a yield strength of 95 MPa (13.8 ksi) and a tensile strength of 245 MPa (35.5 ksi) — stronger than 93% of polymer grades. Elongation at break is 1.6% and the elastic modulus is 22 GPa (3.19 Msi).
Thermal11
PA6T CF30 is rated for continuous service to 140°C (284 °F). It conducts heat at 0.75 W/m·K (0.433 BTU/hr·ft·°F), better than 99% of polymer grades. Thermal expansion is 12 µm/m·K (6.67 µin/in·°F).
Electrical7
PA6T CF30 is an electrical insulator with a dielectric strength of 28 kV/mm (711.2 V/mil) and a resistivity of 1×10¹³ Ω·m.
Chemical & Environmental3
Corrosion resistance is very good (76/100), worse than 64% of polymer grades. UV resistance is poor.
Sustainability4
Producing a kilogram of PA6T CF30 takes about 150 MJ of energy and emits 8.5 kg of CO₂ — more than 84% of polymer grades. Typical recycled content is 0%.
Manufacturability7
PA6T CF30's machinability is fair (35/100, worse than 84% of polymer grades); weldability good (60/100); formability poor (25/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with PA6T CF30
Is PA6T easy to machine?
Machines like a rigid nylon with sharp carbide tools and air/mist cooling; glass- and carbon-filled grades are abrasive, so use polycrystalline-diamond or coated carbide and expect fast edge wear.
Can PA6T be welded?
Ultrasonic, vibration, hot-plate and laser welding all work on unfilled and GF grades; solvent bonding is impractical, and heat-cured epoxy or hot-melt PA adhesives are used with plasma/flame surface activation.
Can PA6T be formed, bent or molded?
Injection mold at 315–345 °C melt with 130–160 °C mold and hot-runner or well-vented tooling; resin must be dried to <0.05 % moisture (80–100 °C, 4–8 h in a desiccant dryer) and residence time kept short to avoid gas and splay.
What surface finishes work on PA6T?
Accepts laser marking, pad printing and painting after plasma/primer treatment; LDS and plateable variants exist, and glass-fiber read-through can be masked with mineral hybrids or textured tool surfaces.
PA6T chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| hexamethylenediamine (1,6-diaminohexane)diamine component, ~50 mol% of repeat units | ≈ 50 | 50 |
| terephthalic acid (6T) unitaromatic diacid giving high Tm/Tg; ≥50 mol% of the diacid fraction in commercial copolymers | 25 – 50 | 33 |
| adipic acid (66) or isophthalic acid (6Icomonomer used to lower Tm below decomposition; defines 6T/66 vs 6T/6I | 0 – 25 | 17 |
| glass fiber0 in default unfilled grade; 15–50 wt% in reinforced grades | ≈ 0 | 0 |
| heat stabilizer / lubricant / nucleant /typical additive package | 0.2 – 2 | 1 |
PA6T CF30 — frequently asked
What is PA6T CF30 used for?
PA6T CF30 is typically used for SMT electrical connectors, LED reflectors and high-heat automotive components. In short: reflow-capable high-heat nylon; most dimensionally stable polyamide; semi-aromatic connector resin.
What is the yield strength of PA6T CF30?
PA6T CF30 has a typical yield strength of 95 MPa (13.8 ksi) and a tensile strength of 245 MPa (35.5 ksi) — stronger than 93% of polymer grades. Strength varies by condition: see the 14 listed tempers.
Is PA6T CF30 easy to machine?
Not especially — machinability is rated fair (35/100, worse than 84% of polymer grades). Machines like a rigid nylon with sharp carbide tools and air/mist cooling; glass- and carbon-filled grades are abrasive, so use polycrystalline-diamond or coated carbide and expect fast edge wear.
Can PA6T CF30 be welded?
Yes — weldability is rated good (60/100). Ultrasonic, vibration, hot-plate and laser welding all work on unfilled and GF grades; solvent bonding is impractical, and heat-cured epoxy or hot-melt PA adhesives are used with plasma/flame surface activation.
What surface finishes work on PA6T CF30?
Accepts laser marking, pad printing and painting after plasma/primer treatment; LDS and plateable variants exist, and glass-fiber read-through can be masked with mineral hybrids or textured tool surfaces.
Can PA6T CF30 be formed, bent or molded?
Injection mold at 315–345 °C melt with 130–160 °C mold and hot-runner or well-vented tooling; resin must be dried to <0.05 % moisture (80–100 °C, 4–8 h in a desiccant dryer) and residence time kept short to avoid gas and splay.
What is the maximum service temperature of PA6T CF30?
PA6T CF30 is rated for continuous use to about 140°C (284 °F), and briefly to 210°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between PA6T UF and PA6T HS?
UF is the default condition — baseline unreinforced PPA for tough thin-wall parts, film/monofilament and as a base for compounding. HS: use for continuous 180–200 °C air aging (charge-air ducts, motor parts) where standard grades embrittle. Yield strength is 95 MPa in UF versus 195 MPa in HS.
Sources
- ISO 16396-1 Plastics — Polyamide (PA) moulding and extrusion materials — ISO (2022)
- JIS K 6920 Plastics — Polyamide (PA) moulding and extrusion materials — JSA (2018)
- Amodel PPA product and processing guides — Solvay/Syensqo (2023)
- Zytel HTN high-performance polyamide datasheets — DuPont/Celanese (2023)
- Grivory HT / Grilamid HT product range — EMS-Grivory (2022)
- CAMPUS plastics database — PPA (PA6T/66, PA6T/6I) datasets — CWFG (2024)
- Engineered Materials Handbook Vol. 2: Engineering Plastics — ASM International (1988)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.