PA6T GF15
Reinforced grade
GF15 = 15 % glass-fiber reinforced
Light reinforcement when some toughness and low warpage matter more than maximum stiffness.
Values for the GF15 condition
Other PA6T grades and fills
PA6T is listed in 14 conditions; see the grade overview at PA6T.
Compare all 14 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
Impact-modified / toughened | For snap fits, clips and cold-impact duty where the standard rigid PPA is too brittle. | 62 | 70 | 45 | 74 Shore D |
PA6T/M-5T copolymer | Copolymer using 2-methylpentamethylenediamine to depress Tm for easier processing while keeping high Tg and reflow resistance. | 90 | 95 | 25 | 85 Shore D |
PA6T/6I copolymer | Copolymer chemistry with isophthalic units for higher Tg, better surface gloss and lower moisture pickup; slower crystallization. | 92 | 95 | 12 | 86 Shore D |
UFDefault Unfilled / natural | Baseline unreinforced PPA for tough thin-wall parts, film/monofilament and as a base for compounding. | — | 100 | 20 | 95 HRM |
MF/GF-MF | Pick for flat, dimensionally isotropic parts and better surface appearance where peak strength is not required. | 115 | 115 | 2.5 | 88 Shore D |
GF15This page 15 % glass-fiber reinforced | Light reinforcement when some toughness and low warpage matter more than maximum stiffness. | — | 145 | 4 | — |
Internally lubricated (PTFE / silicone / graphite), often GF filled | Bearing/wear grade for hot dry-running bushings, gears and sliding contacts. | 155 | 155 | 2 | 87 Shore D |
ESD / conductive | For high-temperature ESD-safe fixtures, fuel-system parts and IC handling hardware. | 160 | 160 | 2 | 88 Shore D |
halogen-free flame-retardant, GF reinforced | Required for connectors/relay housings needing UL 94 V-0 at thin wall plus glow-wire performance. | — | 170 | 1.8 | — |
Heat-stabilized | Use for continuous 180–200 °C air aging (charge-air ducts, motor parts) where standard grades embrittle. | 195 | 195 | 2.4 | 90 Shore D |
30–33 % glass-fiber reinforced | The standard PPA grade for SMT connectors and under-hood parts needing lead-free reflow survival. | — | 200 | 2.5 | 105 HRM |
45 % glass-fiber reinforced | High-stiffness structural grade for metal replacement in hot, loaded brackets and housings. | — | 225 | 2 | — |
50 % glass-fiber reinforced | Maximum stiffness/creep resistance grade; most abrasive to tooling and hardest to fill in thin walls. | — | 240 | 1.8 | — |
30 % carbon-fiber reinforced | Choose for highest specific stiffness, low warpage and static-dissipative surface at reduced weight vs glass. | — | 245 | 1.6 | — |
What is PA6T GF15?
PA6T GF15 is PA6T in the GF15 grade — light reinforcement when some toughness and low warpage matter more than maximum stiffness. PA6T GF15 has a yield strength of 95 MPa (13.8 ksi) and a tensile strength of 145 MPa (21 ksi) — stronger than 93% of polymer grades. Elongation at break is 4% and the elastic modulus is 6 GPa (0.87 Msi). PA6T GF15 has a density of 1.29 g/cm³ (0.0466 lb/in³), heavier than 68% of polymer grades. Its glass-transition temperature is 125°C (257 °F). UF is the default condition FabDigit quotes; GF15 is available on request or by drawing note.
Advantages
- High strength — 95 MPa (13.8 ksi), better than 93% of polymer grades
- Stiff — 6 GPa (0.87 Msi), better than 89% of polymer grades
- High service temperature — 155°C (311 °F), better than 81% of polymer grades
Limitations
- High embodied carbon — 8.5 kg CO₂/kg, worse than 85% of polymer grades
- Limited ductility — 4%, worse than 78% of polymer grades
PA6T GF15 properties
Typical room-temperature values for PA6T GF15; 13 are specific to this condition. Other listed values are PA6T reference data and may not represent this condition. Bars are the position among polymer grades.
Physical5
PA6T GF15 has a density of 1.29 g/cm³ (0.0466 lb/in³), heavier than 68% of polymer grades. Its glass-transition temperature is 125°C (257 °F).
Mechanical16
PA6T GF15 has a yield strength of 95 MPa (13.8 ksi) and a tensile strength of 145 MPa (21 ksi) — stronger than 93% of polymer grades. Elongation at break is 4% and the elastic modulus is 6 GPa (0.87 Msi).
Thermal11
PA6T GF15 is rated for continuous service to 155°C (311 °F). It conducts heat at 0.25 W/m·K (0.144 BTU/hr·ft·°F), better than 72% of polymer grades. Thermal expansion is 40 µm/m·K (22.2 µin/in·°F).
Electrical7
PA6T GF15 is an electrical insulator with a dielectric strength of 28 kV/mm (711.2 V/mil) and a resistivity of 1×10¹³ Ω·m.
Chemical & Environmental3
Corrosion resistance is very good (76/100), worse than 64% of polymer grades. UV resistance is poor.
Sustainability4
Producing a kilogram of PA6T GF15 takes about 150 MJ of energy and emits 8.5 kg of CO₂ — more than 84% of polymer grades. Typical recycled content is 0%.
Manufacturability7
PA6T GF15's machinability is fair (50/100, worse than 73% of polymer grades); weldability good (60/100); formability poor (25/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with PA6T GF15
Is PA6T easy to machine?
Machines like a rigid nylon with sharp carbide tools and air/mist cooling; glass- and carbon-filled grades are abrasive, so use polycrystalline-diamond or coated carbide and expect fast edge wear.
Can PA6T be welded?
Ultrasonic, vibration, hot-plate and laser welding all work on unfilled and GF grades; solvent bonding is impractical, and heat-cured epoxy or hot-melt PA adhesives are used with plasma/flame surface activation.
Can PA6T be formed, bent or molded?
Injection mold at 315–345 °C melt with 130–160 °C mold and hot-runner or well-vented tooling; resin must be dried to <0.05 % moisture (80–100 °C, 4–8 h in a desiccant dryer) and residence time kept short to avoid gas and splay.
What surface finishes work on PA6T?
Accepts laser marking, pad printing and painting after plasma/primer treatment; LDS and plateable variants exist, and glass-fiber read-through can be masked with mineral hybrids or textured tool surfaces.
PA6T chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| hexamethylenediamine (1,6-diaminohexane)diamine component, ~50 mol% of repeat units | ≈ 50 | 50 |
| terephthalic acid (6T) unitaromatic diacid giving high Tm/Tg; ≥50 mol% of the diacid fraction in commercial copolymers | 25 – 50 | 33 |
| adipic acid (66) or isophthalic acid (6Icomonomer used to lower Tm below decomposition; defines 6T/66 vs 6T/6I | 0 – 25 | 17 |
| glass fiber0 in default unfilled grade; 15–50 wt% in reinforced grades | ≈ 0 | 0 |
| heat stabilizer / lubricant / nucleant /typical additive package | 0.2 – 2 | 1 |
PA6T GF15 — frequently asked
What is PA6T GF15 used for?
PA6T GF15 is typically used for SMT electrical connectors, LED reflectors and high-heat automotive components. In short: reflow-capable high-heat nylon; most dimensionally stable polyamide; semi-aromatic connector resin.
What is the yield strength of PA6T GF15?
PA6T GF15 has a typical yield strength of 95 MPa (13.8 ksi) and a tensile strength of 145 MPa (21 ksi) — stronger than 93% of polymer grades. Strength varies by condition: see the 14 listed tempers.
Is PA6T GF15 easy to machine?
Reasonably — machinability is rated fair (50/100, worse than 73% of polymer grades). Machines like a rigid nylon with sharp carbide tools and air/mist cooling; glass- and carbon-filled grades are abrasive, so use polycrystalline-diamond or coated carbide and expect fast edge wear.
Can PA6T GF15 be welded?
Yes — weldability is rated good (60/100). Ultrasonic, vibration, hot-plate and laser welding all work on unfilled and GF grades; solvent bonding is impractical, and heat-cured epoxy or hot-melt PA adhesives are used with plasma/flame surface activation.
What surface finishes work on PA6T GF15?
Accepts laser marking, pad printing and painting after plasma/primer treatment; LDS and plateable variants exist, and glass-fiber read-through can be masked with mineral hybrids or textured tool surfaces.
Can PA6T GF15 be formed, bent or molded?
Injection mold at 315–345 °C melt with 130–160 °C mold and hot-runner or well-vented tooling; resin must be dried to <0.05 % moisture (80–100 °C, 4–8 h in a desiccant dryer) and residence time kept short to avoid gas and splay.
What is the maximum service temperature of PA6T GF15?
PA6T GF15 is rated for continuous use to about 155°C (311 °F), and briefly to 210°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between PA6T UF and PA6T HS?
UF is the default condition — baseline unreinforced PPA for tough thin-wall parts, film/monofilament and as a base for compounding. HS: use for continuous 180–200 °C air aging (charge-air ducts, motor parts) where standard grades embrittle. Yield strength is 95 MPa in UF versus 195 MPa in HS.
Sources
- ISO 16396-1 Plastics — Polyamide (PA) moulding and extrusion materials — ISO (2022)
- JIS K 6920 Plastics — Polyamide (PA) moulding and extrusion materials — JSA (2018)
- Amodel PPA product and processing guides — Solvay/Syensqo (2023)
- Zytel HTN high-performance polyamide datasheets — DuPont/Celanese (2023)
- Grivory HT / Grilamid HT product range — EMS-Grivory (2022)
- CAMPUS plastics database — PPA (PA6T/66, PA6T/6I) datasets — CWFG (2024)
- Engineered Materials Handbook Vol. 2: Engineering Plastics — ASM International (1988)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.