PA6T CF30 vs PA6T GF50
Polymer · PA6T grade comparison
PA6T CF30 and PA6T GF50 are two grades of the same polymer grade, PA6T: CF30 (30 % carbon-fiber reinforced) versus GF50 (50 % glass-fiber reinforced). The chemistry is identical, so every difference below comes from the condition. Both yield at about 95 MPa — the mechanical properties are the same, and the difference is in how the stock is processed and what it is certified to (30 % carbon-fiber reinforced versus 50 % glass-fiber reinforced). PA6T GF50 is the more ductile: elongation 1.8% versus 1.6% for PA6T CF30. PA6T CF30 is lighter (1.34 g/cm³ vs 1.62 g/cm³ for PA6T GF50) and PA6T CF30 is stiffer (22 GPa vs 18 GPa).
PA6T CF30Choose it when weight is the constraint.
PA6T GF50Choose it when the part is bent, formed or impact-loaded.
PA6T CF30 vs PA6T GF50: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all polymer grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Elongation at Break
Flexural Strength
Flexural Modulus
Izod Impact, Notched
Same in both: Shear Modulus 1.2 GPa0.17 Msi · Bulk Modulus 5 GPa0.77 Msi · Poisson's Ratio 0.4 · Yield Strength (0.2% offset) 95 MPa13.8 ksi · Compressive Strength 105 MPa15.2 ksi · Compressive Modulus 3 GPa0.44 Msi · Shear Strength 62 MPa9 ksi · Hardness, Shore D 86 Shore D · Hardness, Rockwell M 95 HRM · Hardness, Rockwell R 122 HRR
Physical
Density and transition temperatures.
Density
Same in both: Melting Temperature (Tm) 315°C599 °F · Glass Transition (Tg) 125°C257 °F · Water Absorption (24 h) 0.3% · Water Absorption (Saturation) 4%
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Heat Deflection Temp. @ 1.8 MPa
Same in both: Specific Heat Capacity 1,500 J/kg·K0.36 BTU/lb·°F · Max Service Temperature (continuous) 140°C284 °F · Min Service Temperature -40°C-40 °F · Heat Deflection Temp. @ 0.45 MPa 250°C482 °F · Vicat Softening Point (B50) 265°C509 °F · Limiting Oxygen Index 26% · Max Service Temperature (short-term) 210°C410 °F
Electrical
Conductivity and insulation.
Surface Resistivity
Same in both: Electrical Resistivity 1×10¹³ Ω·m3.94×10²⁰ µΩ·in · Dielectric Strength 28 kV/mm711 V/mil · Dielectric Constant (1 MHz) 3.6 · Dissipation Factor (1 MHz) 0.018 · Volume Resistivity 1×10¹⁵ Ω·cm · Comparative Tracking Index (CTI) 600 V
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 76 / 100 · UV / Weathering Resistance 30 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Same in both: Weldability 60 / 100 · Formability (cold) 25 / 100 · Polishability 55 / 100 · Mold Shrinkage 0.25% · Processing Melt Temperature (typ.) 330°C626 °F · Mold Temperature (typ.) 140°C284 °F
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 150 MJ/kg64,488 BTU/lb · Embodied Carbon (primary production) 8.5 kg CO₂/kg · Embodied Water 500 L/kg59.9 gal/lb · Typical Recycled Content 0%
Strength versus weight
Yield strength against density for every polymer grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
PA6T CF30 vs PA6T GF50 — frequently asked
What is the difference between PA6T CF30 and PA6T GF50?
PA6T CF30 and PA6T GF50 are two grades of the same polymer grade, PA6T: CF30 (30 % carbon-fiber reinforced) versus GF50 (50 % glass-fiber reinforced). The chemistry is identical, so every difference below comes from the condition. Both yield at about 95 MPa — the mechanical properties are the same, and the difference is in how the stock is processed and what it is certified to (30 % carbon-fiber reinforced versus 50 % glass-fiber reinforced).
Which grade does FabDigit quote by default, CF30 or GF50?
UF is the default PA6T condition in the FabDigit quote flow (neither CF30 nor GF50). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, PA6T CF30 or PA6T GF50?
PA6T CF30. Its machinability rates fair (35/100) against poor (30/100) for PA6T GF50.
Ready to make it?
Upload a CAD file and FabDigit prices the part in PA6T CF30 and PA6T GF50 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.