mPPE GF30-FR
Reinforced grade
also Noryl
GF30-FR = 30% glass-fiber reinforced, flame-retardant V-0
Structural + V-0 combination for EV battery frames, chargers and electrical switchgear.
Values for the GF30-FR condition
Other mPPE grades and fills
mPPE is listed in 12 conditions; see the grade overview at mPPE.
Compare all 12 grades and fillsHide
| Grade · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness |
|---|---|---|---|---|---|
Structural foam grade | Chemically blown thick-wall grade for large, stiff, low-density enclosures and pallets. | 32 | 32 | 5 | 110 HRR |
PPE+PP alloy | Low-density, hydrolysis- and chemical-resistant alloy used for EV battery packs and photovoltaic hardware where light weight plus non-halogen FR matters. | 40 | 42 | 25 | 60 HRM |
Impact-modified | Rubber-boosted grade for thin-wall enclosures and parts needing cold-temperature drop resistance. | 46 | 46 | 70 | 65 HRM |
Mineral / talc filled | Low-warpage stiffening with isotropic shrinkage and good surface for painted or plated cosmetic parts. | 52 | 52 | 12 | 82 HRM |
Non-halogen flame-retardant, UL 94 V-0 | Phosphate-ester FR grade for enclosures, breakers, PV junction boxes and battery components requiring V-0 at 1.5 mm. | — | 55 | 40 | — |
PPE+PA alloy | Semi-crystalline nylon-continuous alloy chosen when solvent resistance and online-paint-bake temperature are needed (automotive fenders, EV connectors). | 55 | 58 | 45 | 70 HRM |
UNFDefault Unfilled / natural | Default choice for housings, water-contact parts and dielectric components needing toughness and dimensional stability. | 58 | 58 | 50 | 78 HRM |
ESD / static-dissipative | Carbon-black or carbon-fiber loaded mPPE for electronics trays, fuel-system and clean-handling parts. | 60 | 60 | 8 | 80 HRM |
10% glass-fiber reinforced | Light reinforcement when stiffness and creep resistance must improve but low warpage is still required. | — | 76 | 6 | — |
20% glass-fiber reinforced | Mid-range stiffness/temperature upgrade for pump housings and structural brackets. | — | 95 | 4 | — |
GF30-FRThis page 30% glass-fiber reinforced, flame-retardant V-0 | Structural + V-0 combination for EV battery frames, chargers and electrical switchgear. | — | 100 | 2.8 | 95 HRM |
30% glass-fiber reinforced | Highest stiffness and HDT of the standard mPPE range; pick for load-bearing housings and metal-replacement parts. | — | 112 | 3.5 | — |
What is mPPE GF30-FR?
mPPE GF30-FR is mPPE in the GF30-FR grade — structural + V-0 combination for EV battery frames, chargers and electrical switchgear. mPPE GF30-FR has a yield strength of 58 MPa (8.41 ksi) and a tensile strength of 100 MPa (14.5 ksi) — stronger than 66% of polymer grades. Elongation at break is 2.8% and the elastic modulus is 7.8 GPa (1.13 Msi). mPPE GF30-FR has a density of 1.32 g/cm³ (0.0477 lb/in³), heavier than 72% of polymer grades. Its glass-transition temperature is 145°C (293 °F). UNF is the default condition FabDigit quotes; GF30-FR is available on request or by drawing note.
Advantages
- Tough — resists crack growth — 5 MPa·√m (4.55 ksi·√in), better than 98% of polymer grades
- Low, predictable mold shrinkage — 0.2%, better than 94% of polymer grades
- Stiff — 7.8 GPa (1.13 Msi), better than 91% of polymer grades
- Conducts heat well — 0.3 W/m·K (0.173 BTU/hr·ft·°F), better than 83% of polymer grades
- Low moisture uptake — 0.07%, better than 81% of polymer grades
Limitations
- Limited formability — 8/100, worse than 91% of polymer grades
- Limited ductility — 2.8%, worse than 86% of polymer grades
- Difficult to machine — 40/100, worse than 82% of polymer grades
mPPE GF30-FR properties
Typical room-temperature values for mPPE GF30-FR; 26 are specific to this condition. Other listed values are mPPE reference data and may not represent this condition. Bars are the position among polymer grades.
Physical4
mPPE GF30-FR has a density of 1.32 g/cm³ (0.0477 lb/in³), heavier than 72% of polymer grades. Its glass-transition temperature is 145°C (293 °F).
Mechanical16
mPPE GF30-FR has a yield strength of 58 MPa (8.41 ksi) and a tensile strength of 100 MPa (14.5 ksi) — stronger than 66% of polymer grades. Elongation at break is 2.8% and the elastic modulus is 7.8 GPa (1.13 Msi).
Thermal11
mPPE GF30-FR is rated for continuous service to 120°C (248 °F). It conducts heat at 0.3 W/m·K (0.173 BTU/hr·ft·°F), better than 83% of polymer grades. Thermal expansion is 65 µm/m·K (36.1 µin/in·°F).
Electrical7
mPPE GF30-FR is an electrical insulator with a dielectric strength of 21 kV/mm (533.4 V/mil) and a resistivity of 1×10¹⁴ Ω·m.
Chemical & Environmental3
Corrosion resistance is very good (80/100), worse than 52% of polymer grades. UV resistance is fair.
Sustainability4
Producing a kilogram of mPPE GF30-FR takes about 110 MJ of energy and emits 4.6 kg of CO₂ — more than 64% of polymer grades. Typical recycled content is 5%.
Manufacturability8
mPPE GF30-FR's machinability is fair (40/100, worse than 82% of polymer grades); weldability fair (40/100); formability not recommended (8/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with mPPE GF30-FR
Is mPPE easy to machine?
Machines cleanly with sharp positive-rake tools and air cooling; avoid aromatic/chlorinated coolants which cause stress cracking, and anneal 2 h at ~110 °C before tight-tolerance finishing.
Can mPPE be welded?
Excellent for ultrasonic, vibration and hot-plate welding; solvent bonding with chlorinated solvents or adhesives also works, but hot-gas welding needs careful temperature control to avoid PS-phase degradation.
Can mPPE be formed, bent or molded?
Dry 2–4 h at 100–110 °C, mold at 260–300 °C melt with 60–110 °C tool; amorphous shrinkage of ~0.5–0.7 % is low and isotropic, giving very stable tolerances.
What surface finishes work on mPPE?
Takes paint, hot stamping and electroless plating well after standard etch/primer steps; UV-absorbing paint or pigment is recommended for outdoor use since unstabilized mPPE yellows.
mPPE chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| poly(2,6-dimethyl-1,4-phenylene ether) (resin fraction sets Tg/HDT | 25 – 70 | 45 |
| impact modifier (SBS/SEBS rubber) | 0 – 10 | 3 |
| phosphate ester flame retardantFR grades only, non-halogen | 0 – 15 | 0 |
| glass fiberGF variants | 0 – 30 | 0 |
| stabilizers, pigments, mold release | 0.3 – 3 | 1 |
| high-impact polystyrene (HIPS/PS)flow and impact carrier phase | ≥ 25 (balance) | — |
mPPE GF30-FR — frequently asked
What is mPPE GF30-FR used for?
mPPE GF30-FR is typically used for electrical enclosures and connectors, automotive instrument panels, plumbing fittings, business machine housings and HVAC components. In short: most dimensionally stable amorphous resin; lowest-density engineering thermoplastic; inherently flame-retardant blend.
What is the yield strength of mPPE GF30-FR?
mPPE GF30-FR has a typical yield strength of 58 MPa (8.41 ksi) and a tensile strength of 100 MPa (14.5 ksi) — stronger than 66% of polymer grades. Strength varies by condition: see the 12 listed tempers.
Is mPPE GF30-FR easy to machine?
Not especially — machinability is rated fair (40/100, worse than 82% of polymer grades). Machines cleanly with sharp positive-rake tools and air cooling; avoid aromatic/chlorinated coolants which cause stress cracking, and anneal 2 h at ~110 °C before tight-tolerance finishing.
Can mPPE GF30-FR be welded?
With care — weldability is rated fair (40/100). Excellent for ultrasonic, vibration and hot-plate welding; solvent bonding with chlorinated solvents or adhesives also works, but hot-gas welding needs careful temperature control to avoid PS-phase degradation.
What surface finishes work on mPPE GF30-FR?
Takes paint, hot stamping and electroless plating well after standard etch/primer steps; UV-absorbing paint or pigment is recommended for outdoor use since unstabilized mPPE yellows.
Can mPPE GF30-FR be formed, bent or molded?
Dry 2–4 h at 100–110 °C, mold at 260–300 °C melt with 60–110 °C tool; amorphous shrinkage of ~0.5–0.7 % is low and isotropic, giving very stable tolerances.
What is the maximum service temperature of mPPE GF30-FR?
mPPE GF30-FR is rated for continuous use to about 120°C (248 °F), and briefly to 130°C. Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between mPPE UNF and mPPE SF?
UNF is the default condition — default choice for housings, water-contact parts and dielectric components needing toughness and dimensional stability. SF: chemically blown thick-wall grade for large, stiff, low-density enclosures and pallets. Yield strength is 58 MPa in UNF versus 32 MPa in SF.
Sources
- Noryl resin family datasheets (731, N190, GFN2/GFN3, PPX, GTX) — SABIC Specialties / SHPP (2023)
- CAMPUS plastics database — PPE+PS entries — CWFG / CAMPUS consortium (2024)
- Engineered Materials Handbook Vol. 2: Engineering Plastics — ASM International (1988)
- ISO 1043-1 / ISO 527 / ISO 75 / ISO 306 test methods for thermoplastics — ISO (2019)
- GB/T 15065 GB/T 1040 — SAC (2018)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.