Copper Alloy C64200-M11
Temper
UNS C64200 · ASTM B150 · EN CW301G
M11 = as forged and quenched
Hot-forged near-net parts (valve bodies, flanged nuts) machined after forging; properties between hot-rolled and annealed.
Values for the M11 condition
Other C64200 tempers and conditions
C64200 is listed in 7 conditions; see the grade overview at C64200.
Compare all 7 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Soft annealed | Pick for maximum ductility when heading, bending or deep forming before final machining. | 205 | 485 | 35 | 110 HB | 7 % IACS |
As hot rolled | Economical large-diameter bar/shape temper where drawn tolerances and peak strength are not required. | 250 | 550 | 35 | 135 HB | 7 % IACS |
As hot forged and air cooled | Hot-forged C64200 aluminium-silicon bronze cooled in still air, giving a moderately strong, tough, corrosion-resistant forging temper. | 270 | 550 | 28 | 150 HB | 7 % IACS |
As hot extruded | Hot-rolled rod/plate condition for weld-fabricated marine hardware and general machining stock. | 275 | 620 | 32 | 150 HB | 7 % IACS |
M11This page As forged and quenched | Hot-forged near-net parts (valve bodies, flanged nuts) machined after forging; properties between hot-rolled and annealed. | 275 | 585 | 30 | 145 HB | 7 % IACS |
HR50Default Extruded and drawn, then stress relieved | Standard stocked rod/bar temper: high strength with low residual stress for valve stems and machined fittings. | 370 | 690 | 32 | 180 HB | 7 % IACS |
Full hard | Highest-strength drawn rod/wire for fasteners, studs and wear-loaded pins; lower ductility and higher residual stress. | 415 | 725 | 22 | 200 HB | 7 % IACS |
What is C64200-M11?
C64200-M11 is C64200 in the M11 temper — hot-forged near-net parts (valve bodies, flanged nuts) machined after forging; properties between hot-rolled and annealed. C64200-M11 has a yield strength of 275 MPa (39.9 ksi) and a tensile strength of 585 MPa (84.8 ksi) — stronger than 57% of copper alloy grades. Elongation at break is 30% and the elastic modulus is 117 GPa (17 Msi). C64200-M11 has a density of 7.69 g/cm³ (0.278 lb/in³), lighter than 90% of copper alloy grades. It melts at 1,027°C (1,881 °F). HR50 is the default condition FabDigit quotes; M11 is available on request or by drawing note.
Advantages
- Lightweight — 7.69 g/cm³ (0.278 lb/in³), better than 90% of copper alloy grades
- High service temperature — 300°C (572 °F), better than 85% of copper alloy grades
- Readily welded — 70/100, better than 85% of copper alloy grades
- Good corrosion resistance — 72/100, better than 84% of copper alloy grades
- Ductile — tolerates forming and impact — 30%, better than 75% of copper alloy grades
Limitations
- Low electrical conductivity — 7 % IACS, worse than 86% of copper alloy grades
- Poor heat conductor — 45 W/m·K (26 BTU/hr·ft·°F), worse than 76% of copper alloy grades
C64200-M11 properties
Typical room-temperature values for C64200-M11; 20 are specific to this condition. Other listed values are C64200 reference data and may not represent this condition. Bars are the position among copper alloy grades.
Physical3
C64200-M11 has a density of 7.69 g/cm³ (0.278 lb/in³), lighter than 90% of copper alloy grades. It melts at 1,027°C (1,881 °F).
Mechanical12
C64200-M11 has a yield strength of 275 MPa (39.9 ksi) and a tensile strength of 585 MPa (84.8 ksi) — stronger than 57% of copper alloy grades. Elongation at break is 30% and the elastic modulus is 117 GPa (17 Msi).
Thermal6
C64200-M11 is rated for continuous service to 300°C (572 °F). It conducts heat at 45 W/m·K (26 BTU/hr·ft·°F), worse than 76% of copper alloy grades. Thermal expansion is 18 µm/m·K (10 µin/in·°F).
Electrical3
C64200-M11 conducts electricity at 7 % IACS, worse than 86% of copper alloy grades.
Chemical & Environmental3
Corrosion resistance is very good (72/100), better than 84% of copper alloy grades.
Sustainability4
Producing a kilogram of C64200-M11 takes about 55 MJ of energy and emits 3.6 kg of CO₂ — less than 72% of copper alloy grades. Typical recycled content is 40%.
Manufacturability8
C64200-M11's machinability is fair (52/100, better than 69% of copper alloy grades); weldability very good (70/100); formability fair (45/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with C64200-M11
Is C64200 easy to machine?
Best of the aluminium bronzes to machine (≈60 % of C36000): use sharp carbide, positive rake, high feed with light depth to break the tough chip, and flood coolant.
Can C64200 be welded?
Good with GTAW/GMAW using ECuAl-A2 or matching Cu-Al-Si filler, argon shield, preheat 100–150 °C on heavy sections; keep interpass low and avoid oxyfuel because of the refractory oxide.
Can C64200 be formed, bent or molded?
Hot works readily at 750–870 °C (forge, extrude, upset); cold formability is only fair — bend generously in O60 and interanneal between heavy draws.
What surface finishes work on C64200?
Not anodisable; take a bright polish, accepts chemical blackening/patination, nickel or chrome plating after thorough oxide removal, and needs no coating for seawater service.
C64200 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| Al | 6.3 – 7.6 | 7 |
| Si | 1.5 – 2.2 | 1.9 |
| Fe | ≤ 0.3 | 0.15 |
| Zn | ≤ 0.5 | — |
| Sn | ≤ 0.2 | — |
| Mn | ≤ 0.1 | — |
| Nimax (incl. Co) | ≤ 0.25 | — |
| Pb | ≤ 0.05 | — |
| Curemainder, Cu + named elements ≥ 99.5 %; Ag counted as Cu | ≥ 88 (balance) | — |
C64200-M11 — frequently asked
What is C64200-M11 used for?
C64200-M11 is typically used for valve stems, gears and marine hardware. In short: wear resistant silicon bronze.
What is the yield strength of C64200-M11?
C64200-M11 has a typical yield strength of 275 MPa (39.9 ksi) and a tensile strength of 585 MPa (84.8 ksi) — stronger than 57% of copper alloy grades. Strength varies by condition: see the 7 listed tempers.
Is C64200-M11 easy to machine?
Reasonably — machinability is rated fair (52/100, better than 69% of copper alloy grades). Best of the aluminium bronzes to machine (≈60 % of C36000): use sharp carbide, positive rake, high feed with light depth to break the tough chip, and flood coolant.
Can C64200-M11 be welded?
Yes — weldability is rated very good (70/100). Good with GTAW/GMAW using ECuAl-A2 or matching Cu-Al-Si filler, argon shield, preheat 100–150 °C on heavy sections; keep interpass low and avoid oxyfuel because of the refractory oxide.
What surface finishes work on C64200-M11?
Not anodisable; take a bright polish, accepts chemical blackening/patination, nickel or chrome plating after thorough oxide removal, and needs no coating for seawater service.
Can C64200-M11 be formed, bent or molded?
Hot works readily at 750–870 °C (forge, extrude, upset); cold formability is only fair — bend generously in O60 and interanneal between heavy draws.
What is the maximum service temperature of C64200-M11?
C64200-M11 is rated for continuous use to about 300°C (572 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between C64200-HR50 and C64200-O60?
HR50 is the default condition — standard stocked rod/bar temper: high strength with low residual stress for valve stems and machined fittings. O60: pick for maximum ductility when heading, bending or deep forming before final machining. Yield strength is 370 MPa in HR50 versus 205 MPa in O60.
Can FabDigit make parts in C64200-M11?
Yes — C64200-M11 is available for CNC machining and sheet metal; every part is priced by an engineer rather than instantly. Upload a STEP file to get a price and a DFM check.
Sources
- Copper Alloy C64200 alloy data sheet — Copper Development Association (copper.org) (2023)
- ASTM B150/B150M — Aluminum Bronze Rod, Bar and Shapes — ASTM International (2019)
- ASTM B601 — Temper Designations for Copper and Copper Alloys — ASTM International (2019)
- ASM Handbook Vol. 2 — Properties and Selection: Nonferrous Alloys — ASM International (1990)
- Aluminum Bronze C642 bar datasheet — Farmers Copper / Concast Metal Products (2022)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.