Steel Y15 CD-SR
Heat-treated state
GB Y15
CD-SR = cold Drawn, stress relieved
Use when long slender turned parts must stay straight after heavy metal removal.
Values for the CD-SR condition
Other Y15 tempers and conditions
Y15 is listed in 5 conditions; see the grade overview at Y15.
Compare all 5 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
Solution annealed | Softest condition for cold heading, staking or upsetting before final machining. | 240 | 420 | 30 | 120 HB | 11 % IACS |
Hot rolled | Pick for larger diameters, subsequent machining from oversize stock or when maximum ductility is wanted. | 270 | 450 | 26 | 130 HB | — |
CD-SRThis page Cold Drawn, stress relieved | Use when long slender turned parts must stay straight after heavy metal removal. | 400 | 560 | 13 | 155 HB | 10 % IACS |
CDDefault Cold drawn | Standard stock condition: tight tolerance, straight, bright bar for automatic-lathe production of screws, pins and bushings. | 450 | 600 | 10 | 167 HB | — |
Carburized and hardened | Use when the machined part needs a wear-resistant surface, e.g. small pins, bushes and cam followers. | 480 | 700 | 8 | 60 HRC | 9 % IACS |
What is Y15 CD-SR?
Y15 CD-SR is Y15 heat treated to CD-SR — use when long slender turned parts must stay straight after heavy metal removal. Y15 CD-SR has a yield strength of 400 MPa (58 ksi) and a tensile strength of 560 MPa (81.2 ksi) — weaker than 60% of steel grades. Elongation at break is 13% and the elastic modulus is 200 GPa (29 Msi). Y15 CD-SR has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,420°C (2,588 °F). CD is the default condition FabDigit quotes; CD-SR is available on request or by drawing note.
Advantages
- Easy to machine — 93/100, better than 100% of steel grades
- Conducts heat well — 51 W/m·K (29.5 BTU/hr·ft·°F), better than 92% of steel grades
- Low embodied carbon — 1.9 kg CO₂/kg, better than 92% of steel grades
- High electrical conductivity — 10 % IACS, better than 83% of steel grades
Limitations
- Difficult to weld — 20/100, worse than 84% of steel grades
- Limited ductility — 13%, worse than 78% of steel grades
Y15 CD-SR properties
Typical room-temperature values for Y15 CD-SR; 21 are specific to this condition. Other listed values are Y15 reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
Y15 CD-SR has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,420°C (2,588 °F).
Mechanical15
Y15 CD-SR has a yield strength of 400 MPa (58 ksi) and a tensile strength of 560 MPa (81.2 ksi) — weaker than 60% of steel grades. Elongation at break is 13% and the elastic modulus is 200 GPa (29 Msi).
Thermal6
Y15 CD-SR is rated for continuous service to 400°C (752 °F). It conducts heat at 51 W/m·K (29.5 BTU/hr·ft·°F), better than 92% of steel grades. Thermal expansion is 11.9 µm/m·K (6.61 µin/in·°F).
Electrical3
Y15 CD-SR conducts electricity at 10 % IACS, better than 83% of steel grades.
Chemical & Environmental3
Corrosion resistance is not recommended (8/100), worse than 99% of steel grades.
Sustainability4
Producing a kilogram of Y15 CD-SR takes about 25 MJ of energy and emits 1.9 kg of CO₂ — less than 82% of steel grades. Typical recycled content is 30%.
Manufacturability6
Y15 CD-SR's machinability is excellent (93/100, better than 100% of steel grades); weldability poor (20/100); formability fair (45/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with Y15 CD-SR
Is Y15 easy to machine?
Excellent — high speeds, small positive-rake tooling and light feeds give short broken chips and bright finish; ideal for CNC/cam automatics and threading.
Can Y15 be welded?
Avoid welding: high S and P cause hot cracking and porosity; if unavoidable use low-hydrogen filler, preheat 150 °C and expect reduced joint properties.
Can Y15 be formed, bent or molded?
Only light cold bending/knurling in the drawn state; anneal first for heading or upsetting, and orient bends across sulphide stringers with care.
What surface finishes work on Y15?
Not weather resistant — protect with oil, black oxide, zinc/nickel plating or phosphate; can be carburised and hard chrome plated for wear surfaces.
Y15 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| C | 0.1 – 0.18 | 0.14 |
| Simax only | ≤ 0.15 | 0.08 |
| Mn | 0.8 – 1.2 | 1 |
| Pdeliberately rephosphorised for chip breaking | 0.05 – 0.1 | 0.07 |
| SMnS inclusions give free-cutting behaviour | 0.23 – 0.33 | 0.28 |
| Crresidual | ≤ 0.15 | — |
| Niresidual | ≤ 0.25 | — |
| Curesidual | ≤ 0.25 | — |
| Fe | balance | — |
Y15 CD-SR — frequently asked
What is Y15 CD-SR used for?
Y15 CD-SR is typically used for screw machine parts, hose and pipe fittings, bolts, studs and threaded rod, bushings and spacers, shaft collars and keys and instrument and sensor housings. In short: free-machining carbon bar.
What is the yield strength of Y15 CD-SR?
Y15 CD-SR has a typical yield strength of 400 MPa (58 ksi) and a tensile strength of 560 MPa (81.2 ksi) — weaker than 60% of steel grades. Strength varies by condition: see the 5 listed tempers.
Is Y15 CD-SR easy to machine?
Yes — machinability is rated excellent (93/100, better than 100% of steel grades). Excellent — high speeds, small positive-rake tooling and light feeds give short broken chips and bright finish; ideal for CNC/cam automatics and threading.
Can Y15 CD-SR be welded?
Not readily — weldability is rated poor (20/100). Avoid welding: high S and P cause hot cracking and porosity; if unavoidable use low-hydrogen filler, preheat 150 °C and expect reduced joint properties.
What surface finishes work on Y15 CD-SR?
Not weather resistant — protect with oil, black oxide, zinc/nickel plating or phosphate; can be carburised and hard chrome plated for wear surfaces.
Can Y15 CD-SR be formed, bent or molded?
Only light cold bending/knurling in the drawn state; anneal first for heading or upsetting, and orient bends across sulphide stringers with care.
What is the maximum service temperature of Y15 CD-SR?
Y15 CD-SR is rated for continuous use to about 400°C (752 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between Y15-CD and Y15-A?
CD is the default condition — standard stock condition: tight tolerance, straight, bright bar for automatic-lathe production of screws, pins and bushings. A: softest condition for cold heading, staking or upsetting before final machining. Yield strength is 450 MPa in CD versus 240 MPa in A.
Can FabDigit make parts in Y15 CD-SR?
Yes — Y15 CD-SR is available for CNC machining; every part is priced by an engineer rather than instantly. Upload a STEP file to get a price and a DFM check.
Sources
- ASTM A29/A29M — Steel Bars, Carbon and Alloy, Hot-Wrought (grade 1215) — ASTM (2020)
- ASM Handbook Vol. 1 — Properties and Selection: Irons, Steels and High-Performance Alloys — ASM International (1990)
- ASM Handbook Vol. 16 — Machining (free-machining steels) — ASM International (1989)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.