Steel S1 Hot Rolled
Finish state
AISI/SAE S1 · UNS T41901 · GB 4CrW2Si, 6CrW2Si
Mill condition on larger forged sections; normally spheroidize-annealed before machining.
Values for the Hot Rolled condition
Other S1 tempers and conditions
S1 is listed in 5 conditions; see the grade overview at S1.
- Annealed
- Hot Rolled
- H&T 50-52 HRC
- Q&T
- H&T 54-56 HRC
Compare all 5 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
AnnealedDefault soft, as-supplied bar/flat condition | Standard stocking condition for machining, drilling and forging before hardening. | 415 | 690 | 25 | 200 HB | — |
Hot RolledThis page Hot Rolled / as-forged (unannealed bar) | Mill condition on larger forged sections; normally spheroidize-annealed before machining. | 720 | 1,050 | 10 | 34 HRC | 7.5 % IACS |
Tempered ~425 °C for maximum shock resistance | Choose for pneumatic chisels, hot punches and other severe-impact tools where toughness rules. | 1,400 | 1,700 | 9 | 51 HRC | — |
Quenched and tempered | General working condition; pick the tempering temperature to trade hardness against shock toughness. | 1,550 | 1,900 | 6 | 55 HRC | — |
Tempered ~315 °C | Balanced hardness/toughness for cold-heading dies, rivet sets and heavy punches. | 1,600 | 1,950 | 6 | 55 HRC | — |
What is S1 Hot Rolled?
S1 Hot Rolled is S1 supplied in the Hot Rolled condition — mill condition on larger forged sections; normally spheroidize-annealed before machining. S1 Hot Rolled has a yield strength of 720 MPa (104 ksi) and a tensile strength of 1,050 MPa (152 ksi) — stronger than 82% of steel grades. Elongation at break is 10% and the elastic modulus is 207 GPa (30 Msi). S1 Hot Rolled has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,420°C (2,588 °F). Annealed is the default condition FabDigit quotes; Hot Rolled is available on request or by drawing note.
Advantages
- High strength — 720 MPa (104 ksi), better than 82% of steel grades
Limitations
- Limited formability — 10/100, worse than 95% of steel grades
- Difficult to machine — 25/100, worse than 93% of steel grades
- Limited ductility — 10%, worse than 91% of steel grades
- Difficult to weld — 15/100, worse than 91% of steel grades
- Poor heat conductor — 25 W/m·K (14.4 BTU/hr·ft·°F), worse than 88% of steel grades
S1 Hot Rolled properties
Typical room-temperature values for S1 Hot Rolled; 22 are specific to this condition. Other listed values are S1 reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
S1 Hot Rolled has a density of 7.85 g/cm³ (0.284 lb/in³), heavier than 56% of steel grades. It melts at 1,420°C (2,588 °F).
Mechanical15
S1 Hot Rolled has a yield strength of 720 MPa (104 ksi) and a tensile strength of 1,050 MPa (152 ksi) — stronger than 82% of steel grades. Elongation at break is 10% and the elastic modulus is 207 GPa (30 Msi).
Thermal6
S1 Hot Rolled is rated for continuous service to 250°C (482 °F). It conducts heat at 25 W/m·K (14.4 BTU/hr·ft·°F), worse than 88% of steel grades. Thermal expansion is 12.4 µm/m·K (6.89 µin/in·°F).
Electrical3
S1 Hot Rolled conducts electricity at 7.5 % IACS, worse than 67% of steel grades.
Chemical & Environmental3
Corrosion resistance is not recommended (12/100), worse than 53% of steel grades.
Sustainability4
Producing a kilogram of S1 Hot Rolled takes about 34 MJ of energy and emits 2.5 kg of CO₂ — more than 82% of steel grades. Typical recycled content is 30%.
Manufacturability7
S1 Hot Rolled's machinability is poor (25/100, worse than 93% of steel grades); weldability poor (15/100); formability not recommended (10/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with S1 Hot Rolled
Is S1 easy to machine?
Machine in the annealed condition (≈55 % of AISI 1212) with rigid setups and sharp carbide or cobalt HSS; hardened parts need grinding or EDM.
Can S1 be welded?
Poor weldability — preheat to 300–400 °C, use matched or low-hydrogen filler, then immediately re-temper; keep welds off high-stress impact faces.
Can S1 be formed, bent or molded?
Forge 1040–1150 °C, stop above ~900 °C and cool slowly, then spheroidize anneal at 760–790 °C; almost no cold forming capability.
What surface finishes work on S1?
Harden from 900–955 °C in oil (protect against decarburisation), temper 205–425 °C to the chosen hardness; finish with black oxide, phosphate or nitriding for wear and light rust protection.
S1 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| C | 0.4 – 0.55 | 0.5 |
| Mn | 0.1 – 0.4 | 0.3 |
| Siwide range; Si-rich variants behave like 5CrW2Si | 0.15 – 1.2 | 0.3 |
| Cr | 1 – 1.8 | 1.5 |
| W | 1.5 – 3 | 2.5 |
| VV optional in some heats (max 0.30) | 0.15 – 0.3 | 0.2 |
| Momax per ASTM A681 | ≤ 0.5 | — |
| Niresidual max | ≤ 0.3 | — |
| P | ≤ 0.03 | — |
| S | ≤ 0.03 | — |
| Fe | balance | — |
S1 Hot Rolled — frequently asked
What is S1 Hot Rolled used for?
S1 Hot Rolled is typically used for chisels, rivet sets and punches. In short: shock-resistant tool steel.
What is the yield strength of S1 Hot Rolled?
S1 Hot Rolled has a typical yield strength of 720 MPa (104 ksi) and a tensile strength of 1,050 MPa (152 ksi) — stronger than 82% of steel grades. Strength varies by condition: see the 5 listed tempers.
Is S1 Hot Rolled easy to machine?
Not especially — machinability is rated poor (25/100, worse than 93% of steel grades). Machine in the annealed condition (≈55 % of AISI 1212) with rigid setups and sharp carbide or cobalt HSS; hardened parts need grinding or EDM.
Can S1 Hot Rolled be welded?
Not readily — weldability is rated poor (15/100). Poor weldability — preheat to 300–400 °C, use matched or low-hydrogen filler, then immediately re-temper; keep welds off high-stress impact faces.
What surface finishes work on S1 Hot Rolled?
Harden from 900–955 °C in oil (protect against decarburisation), temper 205–425 °C to the chosen hardness; finish with black oxide, phosphate or nitriding for wear and light rust protection.
Can S1 Hot Rolled be formed, bent or molded?
Forge 1040–1150 °C, stop above ~900 °C and cool slowly, then spheroidize anneal at 760–790 °C; almost no cold forming capability.
What is the maximum service temperature of S1 Hot Rolled?
S1 Hot Rolled is rated for continuous use to about 250°C (482 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
Can FabDigit make parts in S1 Hot Rolled?
Yes — S1 Hot Rolled is available for CNC machining; every part is priced by an engineer rather than instantly. Upload a STEP file to get a price and a DFM check.
Sources
- ASTM A681 — Alloy Tool Steels — ASTM International (2015)
- ASM Handbook Vol. 1 — Properties and Selection: Irons, Steels, and High-Performance Alloys (Tool Steels) — ASM International (1990)
- Tool Steels, 5th ed. (Roberts, Krauss, Kennedy) — ASM International (1998)
- GB/T 1299 (5CrW2Si / 6CrW2Si) — SAC (2014)
- Shock-resisting S1 tool steel bar datasheet — tool steel producers/distributors (2023)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.