Steel M50 Hot Rolled
Finish state
AISI/SAE M50 · UNS T11350 · EN 80MoCrV42-16
Mill-supplied hot worked bar before spheroidize annealing; must be annealed prior to machining.
Values for the Hot Rolled condition
Other M50 tempers and conditions
M50 is listed in 7 conditions; see the grade overview at M50.
Compare all 7 conditionsHide
| Condition · open for datasheet | Best for | Yield MPa | Tensile MPa | Elong. % | Hardness | Conductivity |
|---|---|---|---|---|---|---|
AnnealedDefault spheroidize annealed bar/forging stock | Standard supply condition for machining rings, gears and forging preforms before hardening. | 570 | 860 | 12 | 22 HRC | 26 W/m·K |
Hot RolledThis page Hot rolled / forged, un-annealed bar | Mill-supplied hot worked bar before spheroidize annealing; must be annealed prior to machining. | 880 | 1,150 | 8 | 37 HRC | 2.9 % IACS |
Hardened & double/triple tempered to 58–60 HRC | Lower-hardness heat treat used where a little extra toughness is wanted in gears or lightly loaded races. | 1,950 | 2,250 | 2 | 59 HRC | 23 W/m·K |
Vacuum arc remelted stock | Single-remelt cleanliness grade for industrial bearings and tooling where full aerospace purity is not required. | 2,100 | 2,400 | 1.5 | 61 HRC | 2.7 % IACS |
Hardened & triple tempered to 60–62 HRC | Standard aero main-shaft bearing condition — best balance of rolling contact fatigue life and toughness. | 2,150 | 2,450 | 1.5 | 61 HRC | 23 W/m·K |
Vacuum induction melted + vacuum arc remelted | Aerospace double-vacuum melt with very low oxygen and inclusion content — required for engine main-shaft bearings. | 2,200 | 2,500 | 2 | 62 HRC | 2.7 % IACS |
Hardened & tempered to 62–65 HRC | Maximum wear resistance for balls, rollers and cutting-type tooling; lowest toughness of the M50 conditions. | 2,300 | 2,600 | 1 | 64 HRC | 23 W/m·K |
What is M50 Hot Rolled?
M50 Hot Rolled is M50 supplied in the Hot Rolled condition — mill-supplied hot worked bar before spheroidize annealing; must be annealed prior to machining. M50 Hot Rolled has a yield strength of 880 MPa (128 ksi) and a tensile strength of 1,150 MPa (167 ksi) — stronger than 89% of steel grades. Elongation at break is 8% and the elastic modulus is 207 GPa (30 Msi). M50 Hot Rolled has a density of 8 g/cm³ (0.289 lb/in³), heavier than 95% of steel grades. It melts at 1,400°C (2,552 °F). Annealed is the default condition FabDigit quotes; Hot Rolled is available on request or by drawing note.
Advantages
- Polishes to a fine finish — 85/100, better than 99% of steel grades
- High strength — 880 MPa (128 ksi), better than 89% of steel grades
Limitations
- Difficult to weld — 5/100, worse than 100% of steel grades
- Limited formability — 5/100, worse than 99% of steel grades
- Difficult to machine — 18/100, worse than 97% of steel grades
- Limited ductility — 8%, worse than 95% of steel grades
- High embodied carbon — 3.6 kg CO₂/kg, worse than 94% of steel grades
M50 Hot Rolled properties
Typical room-temperature values for M50 Hot Rolled; 22 are specific to this condition. Other listed values are M50 reference data and may not represent this condition. Bars are the position among steel grades.
Physical3
M50 Hot Rolled has a density of 8 g/cm³ (0.289 lb/in³), heavier than 95% of steel grades. It melts at 1,400°C (2,552 °F).
Mechanical17
M50 Hot Rolled has a yield strength of 880 MPa (128 ksi) and a tensile strength of 1,150 MPa (167 ksi) — stronger than 89% of steel grades. Elongation at break is 8% and the elastic modulus is 207 GPa (30 Msi).
Thermal6
M50 Hot Rolled is rated for continuous service to 315°C (599 °F). It conducts heat at 26 W/m·K (15 BTU/hr·ft·°F), worse than 87% of steel grades. Thermal expansion is 11.3 µm/m·K (6.28 µin/in·°F).
Electrical3
M50 Hot Rolled conducts electricity at 2.9 % IACS, worse than 93% of steel grades.
Chemical & Environmental3
Corrosion resistance is poor (15/100), better than 75% of steel grades.
Sustainability4
Producing a kilogram of M50 Hot Rolled takes about 50 MJ of energy and emits 3.6 kg of CO₂ — more than 93% of steel grades. Typical recycled content is 15%.
Manufacturability8
M50 Hot Rolled's machinability is poor (18/100, worse than 97% of steel grades); weldability not recommended (5/100); formability not recommended (5/100).
Values are nominal handbook figures for design screening. Confirm any required mill or lot documentation when quoting.
Working with M50 Hot Rolled
Is M50 easy to machine?
Machine only in the annealed condition (~240 HB) with rigid setups and coated carbide; after hardening to 60+ HRC use CBN turning or vitrified/CBN grinding with generous coolant to avoid grinding burn.
Can M50 be welded?
Essentially not weldable for structural use — high carbon and strong air-hardening cause quench cracking; any repair needs 500–550 °C preheat, matching filler and immediate re-temper.
Can M50 be formed, bent or molded?
Hot forge 1050–1150 °C, finish above 950 °C and slow-cool to the anneal; no meaningful cold forming. Harden 1090–1120 °C (salt or vacuum), oil/gas quench, then triple temper at 540–565 °C with intermediate cooling to room temperature (deep-freeze optional).
What surface finishes work on M50?
Superfinish/lap raceways to Ra < 0.05 µm; protect with oil, black oxide, phosphate or thin dense chrome — the 4% Cr does not confer stainless behaviour, and low-temperature ion nitriding or DLC is used where extra scuffing resistance is needed.
M50 chemical composition (wt %)
Limits by weight percent from the governing specification, written the way the spec states them — a single maximum for impurities, a range for alloying elements, and the base element as balance. Nominal is the typical mid-range value.
| Element | Spec limit (wt %) | Nominal |
|---|---|---|
| C | 0.77 – 0.85 | 0.8 |
| Mn | 0.15 – 0.35 | 0.25 |
| Si | 0.1 – 0.25 | 0.2 |
| Cr | 3.75 – 4.25 | 4.1 |
| Mo | 4 – 4.5 | 4.25 |
| V | 0.9 – 1.1 | 1 |
| Wresidual | ≤ 0.25 | — |
| Niresidual | ≤ 0.15 | — |
| Coresidual | ≤ 0.25 | — |
| Curesidual | ≤ 0.1 | — |
| P | ≤ 0.02 | — |
| SAMS 6491 VIM-VAR limit | ≤ 0.01 | — |
| O10 ppm max typical for VIM-VAR | ≤ 0 | 6×10⁻⁴ |
| Fe | balance | — |
M50 Hot Rolled — frequently asked
What is M50 Hot Rolled used for?
M50 Hot Rolled is typically used for aircraft engine mainshaft bearing rings, aerospace bearing balls and rollers, gas turbine accessory bearings, high-speed machine tool spindle bearings, rolling-contact test specimens and precision cam followers. In short: high-speed M50 tool.
What is the yield strength of M50 Hot Rolled?
M50 Hot Rolled has a typical yield strength of 880 MPa (128 ksi) and a tensile strength of 1,150 MPa (167 ksi) — stronger than 89% of steel grades. Strength varies by condition: see the 7 listed tempers.
Is M50 Hot Rolled easy to machine?
Not especially — machinability is rated poor (18/100, worse than 97% of steel grades). Machine only in the annealed condition (~240 HB) with rigid setups and coated carbide; after hardening to 60+ HRC use CBN turning or vitrified/CBN grinding with generous coolant to avoid grinding burn.
Can M50 Hot Rolled be welded?
Not readily — weldability is rated not recommended (5/100). Essentially not weldable for structural use — high carbon and strong air-hardening cause quench cracking; any repair needs 500–550 °C preheat, matching filler and immediate re-temper.
What surface finishes work on M50 Hot Rolled?
Superfinish/lap raceways to Ra < 0.05 µm; protect with oil, black oxide, phosphate or thin dense chrome — the 4% Cr does not confer stainless behaviour, and low-temperature ion nitriding or DLC is used where extra scuffing resistance is needed.
Can M50 Hot Rolled be formed, bent or molded?
Hot forge 1050–1150 °C, finish above 950 °C and slow-cool to the anneal; no meaningful cold forming. Harden 1090–1120 °C (salt or vacuum), oil/gas quench, then triple temper at 540–565 °C with intermediate cooling to room temperature (deep-freeze optional).
What is the maximum service temperature of M50 Hot Rolled?
M50 Hot Rolled is rated for continuous use to about 315°C (599 °F). Strength falls off well before that limit — check the elevated-temperature data for load-bearing parts.
What is the difference between M50 Annealed and M50 VIM-VAR?
Annealed is the default condition — standard supply condition for machining rings, gears and forging preforms before hardening. VIM-VAR: aerospace double-vacuum melt with very low oxygen and inclusion content — required for engine main-shaft bearings. Yield strength is 570 MPa in Annealed versus 2,200 MPa in VIM-VAR.
Can FabDigit make parts in M50 Hot Rolled?
Yes — M50 Hot Rolled is available for CNC machining; every part is priced by an engineer rather than instantly. Upload a STEP file to get a price and a DFM check.
Sources
- AMS 6491 — Steel Bars, Forgings and Tubing, 4.1Cr-4.2Mo-1.0V, Premium Aircraft-Quality, Consumable Electrode Vacuum Melted — SAE International (2020)
- AMS 6490 — Steel Bars and Forgings, M50, Consumable Electrode Vacuum Melted — SAE International (2018)
- ASTM A600 — Standard Specification for Tool Steel High Speed — ASTM International (2016)
- ASM Handbook Vol. 1 — Properties and Selection: Irons, Steels, and High-Performance Alloys (tool steels) — ASM International (1990)
- ASM Specialty Handbook: Tool Materials — ASM International (1995)
- Bearing-quality M50 VIM-VAR bar datasheets (Böhler, Latrobe/Carpenter, Aubert & Duval) — various producers (2023)
- GB/T 3077 / 8Cr4Mo4V (2015)
Property data is compiled from published supplier and standards handbooks and normalised for comparison. Nothing on this page is a certification — request mill certs, CoC or material test reports with your order.