Steel 100Cr6 vs M50
Steel · grade comparison
Steel 100Cr6 and M50 are both steel grades. M50 is the stronger of the two: yield strength 570 MPa (82.7 ksi) against 420 MPa (60.9 ksi) for 100Cr6, about 36% more; tensile strength follows at 860 MPa (125 ksi) vs 660 MPa (95.7 ksi). In exchange, 100Cr6 is the more ductile: elongation 22% versus 12% for M50, and M50 is harder (240 HB vs 200 HB). 100Cr6 conducts heat better (45 W/m·K vs 26 W/m·K). On the shop floor, 100Cr6 machines more easily (45 vs 35 out of 100) and 100Cr6 sits in a lower cost tier (standard, $$) than M50 (premium, $$$).
100Cr6Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
M50Choose it when strength drives the design.
100Cr6 vs M50: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Fracture Toughness (K_IC)
Hardness, Rockwell C
Same in both: Shear Modulus 80 GPa11.6 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Min Service Temperature
Same in both: Latent Heat of Fusion 250 J/g107 BTU/lb · Max Service Temperature (continuous) 200°C392 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 100Cr6 | M50 |
|---|---|---|
| Sheet metal | Yes | — |
| Default condition | Annealed | Annealed |
| Relative cost | $$ Standard | $$$ Premium |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining. Both take the same 38 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, Copper Plating, CrN, DLC, E-Coating and 26 more.
100Cr6 vs M50 — frequently asked
Is M50 stronger than 100Cr6?
Yes. M50 has a typical yield strength of 570 MPa (82.7 ksi) against 420 MPa (60.9 ksi) for 100Cr6 — about 36% more. Tensile strength is 860 MPa (125 ksi) vs 660 MPa (95.7 ksi).
Which is cheaper, 100Cr6 or M50?
100Cr6 is the lower-cost material: it sits in the standard tier ($$) while M50 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 100Cr6 or M50?
100Cr6, by a small margin. Both rate fair for machinability — 45/100 against 35/100 for M50.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 100Cr6 and M50 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.